Method for producing metal or alloy casting composites reinforced with fibrous or particulate materials
Assignee: Battelle Memorial Institute Inc
•
Filing: 1990-06-08
•
Granted: 1991-02-26
•
Expires: 2010-06-08
Abstract
Abstract A framework template of non-reinforcing material is provided containing, distributed therein and bonded to the building constituents thereof, a reinforcing material such as particles, fibers or whiskers of high tenacity nitrides, carbides, borides, oxides and the like, this distribution being arranged according to some given pattern of orientation and packing density. The template is placed in a mould which is then filled with molten metal which solidifies by cooling. During casting, the constituents of the template may be destroyed by the heat, or they may dissolve in the metal, or they can remain embedded therein.
Inventors
- 👤 Mark Jolly
- 👤 Guy Negaty-Hindi
- 👤 Georges Haour
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 02:49
CPC Classifications
C; C22; C22C; C22C47/00; C22C47/02; C22C47/025; B; B22; B22D; B22D19/00; B22D19/14; C04; C04B; C04B38/00; C04B38/06; C04B41/00; C04B41/009; C04B41/45; C04B41/52; C22C1/00; C22C1/10; C22C1/1005; C22C1/1015; C22C1/1021; C22C1/1036; C22C47/06; C22C47/08; C22C49/00; C22C49/02; C22C49/04; C22C49/06; C22C49/14; B22F; B22F2998/00; C04B2111/00; C04B2111/00474; C04B2111/00905; C04B2111/00913; C04B2111/00931
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
182 words
A method for producing metal or alloy casting composites, consisting essentially of a metal matrix reinforced with fibers or particles of reinforcing material distributed in this matrix according to a desired pattern, which comprises the steps of: (a) providing a self-supporting template preform structure having no to little reinforcing properties, made of a porous body or of a network of cross-linked building constituents containing particles or fibers of reinforcing material distributed in pores or in voids between said constituents of the structure and binding said particles or fibers of reinforcing material according to a desired pattern, to said constituents of said preform structure by adding a binder substance; (b) introducing said preform structure into a casting mould or die, filling said mould or die with a molten metal or alloy and causing said molten metal or alloy to infiltrate interstices in the preform structure and thus embed said particles or fibers within the metal to form a matrix of a casting composite; and (c) allowing the molten metal or alloy to solidify, and separating the resulting solidified casting composite from the mould.
Claim 2
Independent Claim
182 words
A method for producing metal or alloy casting composites, consisting essentially of a metal matrix reinforced with fibers or particles of reinforcing material distributed in this matrix according to a desired pattern, which comprises the steps of: (a) providing a self-supporting template preform structure having no to little reinforcing properties, made of a porous body or of a network of cross-linked building constituents containing particles or fibers of reinforcing material distributed in pores or in voids between said constituents of the structure and binding said particles or fibers of reinforcing material according to a desired pattern, to said constituents of said preform structure by adding a binder substance; (b) introducing said preform structure into a casting mould or die, filling said mould or die with a molten metal or alloy and causing said molten metal or alloy to infiltrate interstices in the preform structure and thus embed said particles or fibers within the metal to form a matrix of a casting composite; and (c) allowing the molten metal or alloy to solidify, and separating the resulting solidified casting composite from the mould.
Claim 3
Dependent Claim
18 words
The method of claim 1, in which the reinforcing material has a packing density pattern which is uniform.
Claim 4
Dependent Claim
25 words
The method of claim 1, in which the metal or alloy is selected from light alloys, aluminum, magnesium, copper, zinc, lead, tin and alloys thereof.
Claim 5
Dependent Claim
19 words
The method of claim 1, in which the reinforcing material is selected from metal oxides, carbides, nitrides and borides.
Claim 6
Dependent Claim
31 words
The method of claim 1, in which the reinforcing material is selected from SiC, graphitic carbon, Si 3 N 4 , WC, TiN, TiC, ZrN, ZrC, AlN and B 4 C.
Claim 7
Dependent Claim
18 words
The method of claim 1, in which the reinforcing material has a packing density pattern which varies directionally.
Claim 8
Dependent Claim
14 words
The method of claim 6 in which said packing density pattern varies by steps.
Claim 9
Dependent Claim
13 words
The method of claim 6 in which said packing density pattern varies continuously.
Claim 10
Dependent Claim
24 words
The method of claim 1, in which the preform structure is temporary, the constituents therof being fused within the metal matrix during step (b).
Claim 11
Dependent Claim
26 words
The method of claim 9 in which said constituents are made of an alloy or metal which dissolves in the molten metal or alloy upon casting.
Claim 12
Dependent Claim
20 words
The method of claim 1, in which the preform structure is temporary, the constituents thereof being eliminated during step (b).
Claim 13
Dependent Claim
26 words
The method of claim 11 in which said constituents are made of an organic polymer which volatilizes at the temperature of the molten metal or alloy.
Claim 14
Dependent Claim
26 words
The method of claim 11 in which said constituents are made of an organic polymer which decomposes at the temperature of the molten metal or alloy.
Claim 15
Dependent Claim
22 words
The method of claim 1, in which the preform structure is permanent, the constituents thereof being made of a refractory mineral material.
Claim 16
Dependent Claim
34 words
The method of claim 1, in which said preform constituents are fibers selected from Al 2 O 3 , SiO 2 , Al 2 O 3 -SiO 2 , magnesium silicate, rock-wool and asbestos.
Claim 17
Dependent Claim
26 words
The method of claim 1, in which said binder is selected from alkali metal silicates, colloidal silica, alkyl silicates, starch, sugars, hydroxylic polymers, glues, and gums.
Claim 18
Dependent Claim
22 words
The method of claim 1, in which pressure is applied over the molten metal in the mould, thereby squeeze casting the casting.
Claim 19
Independent Claim
223 words
A method for producing metal or alloy casting composites, consisting essentially of a metal matrix reinforced with fibers or particles of reinforcing material distributed in this matrix according to a desired pattern, which comprises the steps of: (a) providing a self-supporting template preform structure made of a porous body or of a network of cross-linked building constituents containing particles or fibers of reinforcing material distributed in pores or in voids between said constituents of the structure and binding said particles or fibers of reinforcing material according to a desired pattern, to said constituents of said preform structure by adding a binder substance, said step (a) being achieved by, (i) forming a homogeneous slurry of preform building constituents and said binder in a liquid medium, and (ii) forming this slurry into a cake in a desired preform shape and removing liquid from the cake to obtain a dry preform structure; (b) introducing said preform structure into a casting mould or die, filling said mould or die with a molten metal or alloy and causing said molten metal or alloy to infiltrate interstices in the preform structure and thus embed said particles or fibers within the metal to form a matrix of a casting composite; and (c) allowing the molten metal or alloy to solidify, and separating the resulting solidified casting composite from the mould.
Claim 20
Independent Claim
223 words
A method for producing metal or alloy casting composites, consisting essentially of a metal matrix reinforced with fibers or particles of reinforcing material distributed in this matrix according to a desired pattern, which comprises the steps of: (a) providing a self-supporting template preform structure made of a porous body or of a network of cross-linked building constituents containing particles or fibers of reinforcing material distributed in pores or in voids between said constituents of the structure and binding said particles or fibers of reinforcing material according to a desired pattern, to said constituents of said preform structure by adding a binder substance, said step (a) being achieved by, (i) forming a homogeneous slurry of preform building constituents and said binder in a liquid medium, and (ii) forming this slurry into a cake in a desired preform shape and removing liquid from the cake to obtain a dry preform structure; (b) introducing said preform structure into a casting mould or die, filling said mould or die with a molten metal or alloy and causing said molten metal or alloy to infiltrate interstices in the preform structure and thus embed said particles or fibers within the metal to form a matrix of a casting composite; and (c) allowing the molten metal or alloy to solidify, and separating the resulting solidified casting composite from the mould.
Claim 21
Independent Claim
187 words
A method for producing metal or alloy casting composites, consisting essentially of a metal matrix reinforced with fibers or particles of reinforcing material distributed in this matrix according to a desired pattern, which comprises the steps of: (a) providing a self-supporting template preform structure having no to little reinforcing properties, made of a porous body or of a network of cross-linking building constituents containing, particles or fibers of reinforcing material distributed in pores or in voids between said constituents of the structure and binding said particles or fibers of reinforcing material according to a desired pattern, to said constituents of said preform structure by coating said constituents with said particles of reinforcing material; (b) introducing said preform structure into a casting mould or die, filling said mould or die with a molten metal or alloy and causing said molten metal or alloy to infiltrate interstices in the preform structure and thus embed said particles or fibers within the metal to form a matrix of a casting composite; and (c) allowing the molten metal or alloy to solidify, and separating the resulting solidified casting composite from the mould.
Claim 22
Independent Claim
187 words
A method for producing metal or alloy casting composites, consisting essentially of a metal matrix reinforced with fibers or particles of reinforcing material distributed in this matrix according to a desired pattern, which comprises the steps of: (a) providing a self-supporting template preform structure having no to little reinforcing properties, made of a porous body or of a network of cross-linking building constituents containing, particles or fibers of reinforcing material distributed in pores or in voids between said constituents of the structure and binding said particles or fibers of reinforcing material according to a desired pattern, to said constituents of said preform structure by coating said constituents with said particles of reinforcing material; (b) introducing said preform structure into a casting mould or die, filling said mould or die with a molten metal or alloy and causing said molten metal or alloy to infiltrate interstices in the preform structure and thus embed said particles or fibers within the metal to form a matrix of a casting composite; and (c) allowing the molten metal or alloy to solidify, and separating the resulting solidified casting composite from the mould.
References Cited (Backward Citations)
BE627229A
Cited
US4033400A
Cited
GB1489346A
Cited
GB1595280A
Cited
GB2106433A
Cited
JPS59111970A
Cited
WO1984002927A1
Cited
US4715422A
Cited
US4538253A
Cited
EP0143330A2
Cited
US4586554A
Cited
US4667727A
Cited
WO1986003997A1
Cited
US4696866A
Cited
US4669523A
Cited
US4712600A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-02-25 | 1994-08-27 | 1995-02-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-02-25 | 1998-08-27 | 1999-02-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-02-25 | 2002-08-27 | 2003-02-26 | $7700.00 | Window Closed / Lapsed |