Reinforcement of articles of cast metal or metal alloy
Assignee: AE PLC
•
Filing: 1986-04-14
•
Granted: 1987-12-29
•
Expires: 2006-04-14
Abstract
Abstract Milled silica or alumina fibres or whiskers are formed into a reinforcement for a squeeze cast article such as a piston for an internal combustion engine. The problem of handling the milled fibres or whiskers while they are formed into the reinforcement is mitigated or overcome by the use of coagulated latex to bind the milled fibres or whiskers in a colloidal silica solution until they are fired to form the reinforcement. In addition, a starch is used to prevent the milled fibres or whiskers settling when in the colloidal silica solution.
Inventors
- 👤 Norman Tommis
- 👤 James A. Cooper
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 17:20
CPC Classifications
C; C22; C22C; C22C47/00; C22C47/02; C22C47/025; B; B22; B22D; B22D19/00; B22D19/14; C04; C04B; C04B26/00; C04B38/00; C04B38/06; C04B38/063; C04B38/0635; C04B38/0645; C22C47/06; C22C47/08; B22F; B22F2998/00; C04B2111/00; C04B2111/00474; C04B2111/00905; C04B2111/00913; C04B2111/00931; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49229; Y10T29/49249; Y10T29/49256; Y10T29/49259
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
117 words
A method of manufacturing a reinforcement for incorporation in a cast article of metal or metal alloy, and comprising: milling fibres or whiskers, dispersing a mass of milled fibres or whiskers in a solution of colloidal silica, adding starch to the dispersed milled fibres or whiskers in said colloidal silica solution to prevent settling, adding latex to the dispersed milled fibres or whiskers in said colloidal silica solution, precipitating said latex to bend the milled fibres or whiskers together, forming a compact of said latex bound milled fibres or whiskers, drying the compact, and firing the compact to disperse the latex and to leave the milled fibres or whiskers of the compact bound together, by said silica.
Claim 2
Independent Claim
117 words
A method of manufacturing a reinforcement for incorporation in a cast article of metal or metal alloy, and comprising: milling fibres or whiskers, dispersing a mass of milled fibres or whiskers in a solution of colloidal silica, adding starch to the dispersed milled fibres or whiskers in said colloidal silica solution to prevent settling, adding latex to the dispersed milled fibres or whiskers in said colloidal silica solution, precipitating said latex to bend the milled fibres or whiskers together, forming a compact of said latex bound milled fibres or whiskers, drying the compact, and firing the compact to disperse the latex and to leave the milled fibres or whiskers of the compact bound together, by said silica.
Claim 3
Dependent Claim
15 words
A method according to claim 1, wherein the latex is added in a 50% solution.
Claim 4
Dependent Claim
16 words
A method according to claim 1, wherein the latex is precipitated at a pH of 3.
Claim 5
Dependent Claim
23 words
A method according to claim 1 and further including the step of adding a retention aid prior to the addition of the latex.
Claim 6
Dependent Claim
19 words
A method according to claim 1, wherein the drying of the compact is at a temperature of 110° C.
Claim 7
Dependent Claim
27 words
A method according to claim 1, wherein the firing of the compact is at a temperature of 1200° C. and is for a time of 20 minutes.
Claim 8
Dependent Claim
21 words
A method according to claim 1, wherein the density of the milled fibres or whiskers in the reinforcement is 0.6 grammes/cc.
Claim 9
Dependent Claim
67 words
A method of manufacturing a piston for an internal combustion engine comprising: placing in a casting mould a reinforcement according to claim 1, introducing into said mould under gravity a molten material selected from aluminium or an aluminium alloy, closing said mould, applying pressure to said molten material to force said molten material into said reinforcement, solidifying said molten metal under said pressure to form said piston.
References Cited (Backward Citations)
JPS5125211A
Cited
JPS5470333A
Cited
GB2033805A
Cited
US4312398A
Cited
EP0064411A1
Cited
GB2106433A
Cited
JPH111565A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-12-28 | 1991-06-29 | 1991-12-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-12-28 | 1995-06-29 | 1995-12-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-12-28 | 1999-06-29 | 1999-12-29 | $7700.00 | Window Closed / Lapsed |