Method of squeeze forming metal articles
Assignee: GKN Technology Ltd
•
Filing: 1985-04-02
•
Granted: 1987-05-26
•
Expires: 2005-04-02
Abstract
Abstract A squeeze formed aluminium alloy article, such as a piston, is formed with a re-entrant cavity (14) with reinforced edges by locating an isostatically compacted salt core (10) and annular alumina-silicate fibre pad (11) in the mould cavity of the squeeze forming press prior to introduction of the molten metal therein. The core (10) is subsequently dissolved from the squeeze formed article to provide a reinforced corresponding shape to the article which does not require subsequent machining.
Inventors
- 👤 John Barlow
- 👤 David B. Rogers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 17:51
CPC Classifications
B; B22; B22D; B22D19/00; B22D19/0009; B22D19/0027; B22C; B22C9/00; B22C9/10; B22C9/105; B22D15/00; B22D15/02; F; F02; F02B; F02B23/00; F02B23/02; F02B23/06; F02B23/0603; F02B23/0636; F02F; F02F3/00; F02F3/02; F02F3/04; F02F3/045; F02F2200/00; F02F2200/06; F05; F05C; F05C2201/00; F05C2201/02; F05C2201/021; F05C2253/00; F05C2253/16; Y; Y02; Y02T; Y02T10/00; Y02T10/10; Y02T10/12
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
180 words
A method of manufacturing a light metal article having a formed shape therein comprising: placing a core and a preformed reinforcement insert adjacent and in contact with the core in a cavity of a mould prior to introduction of molten light metal into the mould; the core comprising a soluble salt core of a fine grained salt mixture; introducing molten light metal into the mould cavity, closing the mould under pressure to displace molten metal into the cavity and maintaining the metal under pressure whilst solidification thereof takes place to produce a squeeze formed light metal article having a formed shape; opening the mould and removing the squeeze formed light metal article having a formed shape therein; the formed shape being partially defined by a volume of reinforced light metal adjacent a volume of unreinforced light metal; both the volume of reinforced light metal and the volume of unreinforced light metal defining a common boundary which ends at an external surface of the formed shape predetermined to require reinforcement to meet operational conditions; and dissolving the core from the article.
Claim 2
Independent Claim
180 words
A method of manufacturing a light metal article having a formed shape therein comprising: placing a core and a preformed reinforcement insert adjacent and in contact with the core in a cavity of a mould prior to introduction of molten light metal into the mould; the core comprising a soluble salt core of a fine grained salt mixture; introducing molten light metal into the mould cavity, closing the mould under pressure to displace molten metal into the cavity and maintaining the metal under pressure whilst solidification thereof takes place to produce a squeeze formed light metal article having a formed shape; opening the mould and removing the squeeze formed light metal article having a formed shape therein; the formed shape being partially defined by a volume of reinforced light metal adjacent a volume of unreinforced light metal; both the volume of reinforced light metal and the volume of unreinforced light metal defining a common boundary which ends at an external surface of the formed shape predetermined to require reinforcement to meet operational conditions; and dissolving the core from the article.
Claim 3
Dependent Claim
18 words
A method according to claim 1 wherein the reinforcement insert is annular and surrounds the shaped salt core.
Claim 4
Dependent Claim
53 words
A method according to claim 1 wherein the reinforcement insert comprises an inorganic whisker or fibre pad whereby the molten metal will penetrate the interstices between the whiskers or fibres and said whiskers or fibres will become embedded within the article adjacent the shaped part of the article formed by the salt core.
Claim 5
Dependent Claim
16 words
A method according to claim 3 wherein the whisker or fibre mat comprises an alumina-silicate material.
Claim 6
Dependent Claim
83 words
A method according to claim 1 in which the article is a piston for an internal combustion engine, in which: the mould has a bottom mould part; the shaped core and the reinforcement insert are located in the bottom mould part and are shaped to form a bowl having a reinforced edge in a piston crown; a top punch; and the top punch and mould are vertically movable relative to one another whereby a piston is squeeze formed in the mould crown down.
Claim 7
Dependent Claim
22 words
A method according to claim 5 wherein the salt core is shaped to provide a re-entrant bowl configuration in the piston crown.
Claim 8
Dependent Claim
29 words
A method according to claim 5 wherein the top punch is provided with magnetic holding means for supporting ferrous expansion inserts thereon for incorporation into the squeeze formed piston.
Claim 9
Dependent Claim
22 words
A method according to claim 1 in which the formed shape is a bowl and the common boundary ends in the bowl.
Claim 10
Dependent Claim
39 words
A method according to claim 8 in which the bowl has a surface partially defined by the reinforced light metal and partially defined by the unreinforced light metal and the bowl surface is an external surface of the article.
Claim 11
Dependent Claim
18 words
A method according to claim 9 in which the reinforced light metal contains inorganic fibers as a reinforcement.
Claim 12
Dependent Claim
24 words
A method according to claim 10 in which the surface of the bowl has an intergral covering of light metal over the fiber reinforcement.
Claim 13
Dependent Claim
21 words
A method according to claim 11 in which the light metal is integral to the reinforced and unreinforced light metal volumes.
References Cited (Backward Citations)
US3459253A
Cited
US3439732A
Cited
FR2011343A1
Cited
US3963818A
Cited
US3801334A
Cited
US4334507A
Cited
US4279289A
Cited
US4446906A
Cited
US4491168A
Cited
GB2106433A
Cited
GB2123727A
Cited
US4480681A
Cited
US4570693A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-05-25 | 1990-11-24 | 1991-05-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-05-25 | 1994-11-24 | 1995-05-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-05-25 | 1998-11-24 | 1999-05-26 | $7700.00 | Window Closed / Lapsed |