Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for manufacturing fiber reinforced light metal castings
Assignee: Daimler Benz AG
•
Filing: 1985-02-06
•
Granted: 1986-05-06
•
Expires: 2005-02-06
Abstract
Abstract A process is provided for the production of fibre-reinforced light-metal castings by die casting. A fibre moulding is introduced into an auxiliary mould and the auxiliary mould is heated to an optimum temperature above the melting point of the light metal. The auxiliary mould is then inserted with positive fit into a die casting mould corresponding to the outer contour of the auxiliary mould and filled with light metal under pressure. The fibre moulding can optionally be stabilized by means of a temporary organic binder which decomposes when the auxiliary mould is heated.
Inventors
- 👤 Eggert Tank
- 👤 Peter Straub
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 00:33
CPC Classifications
B; B22; B22D; B22D17/00; B22D19/00; B22D19/14; C; C22; C22C; C22C49/00; C22C49/02; C22C49/04
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
111 words
A die casting process for the production of fibre reinforced metal castings containing fibrous material and metal comprising: placing said fibrous material into an opened reusable auxiliary mould means, said mould means having at least two parts, closing said auxiliary mould means, heating said auxiliary mould means containing said fibrous material to a temperature at which said metal exists in a molten state, placing said auxiliary mould means into a die casting mould means with positive fit, said die casting mould means having an inner contour corresponding to an outer contour of said auxiliary mould means, and filling said auxiliary mould means with said metal in a molten state under pressure.
Claim 2
Dependent Claim
111 words
A die casting process for the production of fibre reinforced metal castings containing fibrous material and metal comprising: placing said fibrous material into an opened reusable auxiliary mould means, said mould means having at least two parts, closing said auxiliary mould means, heating said auxiliary mould means containing said fibrous material to a temperature at which said metal exists in a molten state, placing said auxiliary mould means into a die casting mould means with positive fit, said die casting mould means having an inner contour corresponding to an outer contour of said auxiliary mould means, and filling said auxiliary mould means with said metal in a molten state under pressure.
Claim 3
Dependent Claim
20 words
A process according to claim 1, wherein said pressure is maintained until said metal in a molten state has solidified.
Claim 4
Dependent Claim
22 words
A process according to claim 2, wherein said fibrous material is in a compressed state when said auxiliary mould means is closed.
Claim 5
Dependent Claim
14 words
A process according to claim 1, wherein said fibrous material contains a binder means.
Claim 6
Dependent Claim
14 words
A process according to claim 4, wherein said binder means comprises an organic binder.
Claim 7
Dependent Claim
21 words
A process accordihg to claim 5, wherein said organic binder is selected from a group consisting of alginates and methacrylate polymers.
Claim 8
Dependent Claim
27 words
A process according to claim 1, wherein said fibrous material is composed of a material selected from the group consisting of glass, carbon, metals and metal oxides.
Claim 9
Dependent Claim
27 words
A process according to claim 1, wherein said auxiliary mould means is heated to a temperature between the melting point of said metal and about 850° C.
Claim 10
Dependent Claim
22 words
A process according to claim 1, wherein said auxiliary mould is heated to a temperature between about 650° C. and 750° C.
Claim 11
Dependent Claim
18 words
A process according to claim 5, wherein said binder is degraded when said auxiliary mould means is heated.
Claim 12
Dependent Claim
18 words
A process according to claim 1, wherein said fibre-reinforced metal casting is a component for a motor vehicle.
References Cited (Backward Citations)
US3853635A
Cited
US4492265A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-05-05 | 1989-11-04 | 1990-05-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-05-05 | 1993-11-04 | 1994-05-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-05-05 | 1997-11-04 | 1998-05-06 | $7700.00 | Window Closed / Lapsed |