Patent US4978352A successfully refreshed from Google Patents.
US4978352A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing collagen-based cross-linked biopolymer, an implant from said biopolymer, method for producing said implant, and method for hermetization of corneal or scleral wounds involved in eye injuries, using said implant
Assignee: MEZHOTRASLEVOI NAUCHNO-TEKHNICHESKY KOMPLEX "MIKROKHIRURGIY A GLAZA "
•
Filing: 1989-05-23
•
Granted: 1990-12-18
•
Expires: 2009-05-23
Abstract
Abstract A process for producing a collagen-based cross-linked biopolymer is provided in which a collagen solution free of low-molecular impurities is saturated with nitrogen protoxide, its concentration is brought to maximum 80 mass percent and the solution is exposed to an ionizing radiation in a dose of 0.5 to 15 kGy. An implant for hermetization of corneal and scleral wounds involved in eye injuries prepared from said bipolymer has the shape and size that provide for complete hermetization of said wounds. The method for its preparation comprises saturation of a collagen solution free of impurities and having a concentration of 0.2 to 1.3 mass percent, with nitrous oxide, filling of a mould with said solution and its exposure to an ionizing radiation in a dose of 0.5 to 15 kGy. The resultant blank is dried to a moisture content in its biopolymer of 30 to 50 mass percent, whereupon the blank is given the shape and size of a required implant. The method of hermetization of said wounds is carried into effect by introducing the implant shaped as a cylinder with a tapered end, with said end into an operative wound incision, fixing the implant in the wound for 1 or 2 minutes and removal of the implant portion that stands over the corneal or scleral surface.
Inventors
- 👤 Svyatoslav N. Fedorov
- 👤 Sergei N. Bagrov
- 👤 Vladislav T. Trofimov
- 👤 Tatyana S. Amstislavskaya
- 👤 Alexei V. Osipov
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 08:13
CPC Classifications
A; A61; A61L; A61L27/00; A61L27/36; A61L27/3604; A61F; A61F2/00; A61F2/02; A61F2/14; A61F2/16; A61K; A61K35/00; A61K35/12; A61K35/44; A61L27/14; A61L27/22; A61L27/24; A61L27/3641; A61L27/3683; A61L27/3691; C; C08; C08H; C08H1/00; C08H1/06; A61F2310/00; A61F2310/00005; A61F2310/00365; A61L2430/00; A61L2430/16; A61L2430/40; Y; Y10; Y10S; Y10S128/00; Y10S128/08
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
87 words
A process for producing a collagen-based cross-linked biopolymer for ophthalmological uses, comprising: alkali-salt treatment of animals' sclera; homogenization of the thus-obtained tissue with an aqueous solution of an organic acid until a collagen solution is formed; extraction of low molecular impurities from the collagen solution; saturation of said solution with nitrous oxide; brining the concentration of said collagen solution to 80 mass percent maximum; exposure of said collagen solution to an ionizing radiation in a dose of 0.5 to 15 kGy until a cross-linked biopolymer is formed.
Claim 2
Dependent Claim
87 words
A process for producing a collagen-based cross-linked biopolymer for ophthalmological uses, comprising: alkali-salt treatment of animals' sclera; homogenization of the thus-obtained tissue with an aqueous solution of an organic acid until a collagen solution is formed; extraction of low molecular impurities from the collagen solution; saturation of said solution with nitrous oxide; brining the concentration of said collagen solution to 80 mass percent maximum; exposure of said collagen solution to an ionizing radiation in a dose of 0.5 to 15 kGy until a cross-linked biopolymer is formed.
Claim 3
Dependent Claim
33 words
A process as claimed in claim 1, wherein the collagen solution is subject, prior to irradiation, to partial degassing by its centrifugation at 3 to 4·10 3 rpm for 10 to 30 minutes.
Claim 4
Dependent Claim
30 words
An implant for hermetization of corneal and scleral wounds involved in eye injuries, said implant being made from the collagen-based cross-linked biopolymer produced according to the process of claim 1.
Claim 5
Dependent Claim
173 words
A method for producing an implant for hermetization of corneal and scleral wounds involved in eye injuries as claimed in claim 3, comprising: alkali-salt treatment of animals' sclera; homogenization of the thus-obtained tissue with an aqueous solution of an organic acid until a collagen solution is formed; extraction of low-molecular impurities from the collagen solution; bringing the concentration of said solution to 0.2 or 1.3 mass percent; saturation of said collagen solution with nitrous oxide; filling a mold with said collagen solution and exposure of said solution to an ionizing radiation in a dose of 0.5 to 15 kGy until a blank is formed for an implant made from the collagen-based cross-linked biopolymer; subjecting said blank made from the cross-linked biopolymer to dialysis with water for 24 to 48 hours; drying said blank until the moisture content of its cross-linked biopolymer equals 30 to 50 mass percent; imparting to said blank the shape and size of an implant so as to ensure complete hermetization of corneal and scleral wounds involved in eye injuries.
Claim 6
Dependent Claim
47 words
A method as claimed in claim 4, wherein the collagen solution before being placed in a mold is subjected to partial degassing by way of consecutively performed freezing, thawing at 20° to 25° C. and centrifugation at 1 to 2·10 3 rpm for 10 to 60 minutes.
Claim 7
Dependent Claim
89 words
A method for hermeitization of corneal or scleral wounds involved in eye injuries, comprising: introducing an implant as claimed in claim 3, made from the collagen-based cross-linked biopolymer and shaped as a cylinder with a tapered end, with said tapered end, into an operative wound incision; fixing said implant in the wound for 1 to 2 minutes in order to ensure a contact of the wound lips with the implant cylindrical surface and ; removing the implant portion that stands over the corneal or scleral surface of the eye.
Claim 8
Dependent Claim
37 words
A method as claimed in claim 6, wherein the implant is shaped as a cylinder with a tapered end, said cylindrical being 3 to 5 mm long and having its base diameter of 0.5 to 4 mm.
Claim 9
Dependent Claim
8 words
A product of the process of claim 1.
Claim 10
Dependent Claim
8 words
A product of the process of claim 2.
References Cited (Backward Citations)
US3553299A
Cited
SU628913A1
Cited
US4164559A
Cited
US4223984A
Cited
US4268131A
Cited
US4374121A
Cited
US4349470A
Cited
SU990221A1
Cited
US4357274A
Cited
US4505855A
Cited
US4581030A
Cited
US4540532A
Cited
SU1321420A1
Cited
US4913904A
Cited
US4772283A
Cited
US4931546A
Cited
US4781187A
Cited
US4879072A
Cited
US4865779A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-12-17 | 1994-06-18 | 1994-12-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-12-17 | 1998-06-18 | 1998-12-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-12-17 | 2002-06-18 | 2002-12-18 | $7700.00 | Window Closed / Lapsed |