Process for making puncture resistant, heat-shrinkable films containing very low density polyethylene
Assignee: Curwood Inc
•
Filing: 1989-07-25
•
Granted: 1990-12-11
•
Expires: 2009-07-25
Abstract
Abstract Method of manufacturing a heat shrinkable biaxially oriented thermoplastic film by extruding a primary tube including very low density polyethylene (VLDPE), heating the primary tube and biaxially stretching the heated primary tube using a double bubble method to form a tube which is heat shrinkable from about 30% to about 50% in at least one of the transverse and machine directions.
Inventors
- 👤 Stanley Lustig
- 👤 Nancy M. Mack
- 👤 Jeffrey M. Schuetz
- 👤 Stephen J. Vicik
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 08:33
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/08
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
113 words
A method of manufacturing a heat-shrinkable, puncture resistant, biaxially stretched, thermoplastic film comprising the steps of extruding a primary tube comprising a very low density polyethylene which is a linear copolymer of ethylene and higher alpha olefin containing from 3 to 8 carbon atoms, having a density below about 0.91 g/cm 3 and a 1% secant modulus below about 140,000 kPa; heating the very low density polyethylene primary tube; biaxially stretching the heated primary tube using a double bubble method under conditions wherein the biaxially stretched tube is heat shrinkable from about 30% to about 50% at a temperature of about 90° C. in at least one of the transverse and machine directions.
Claim 2
Independent Claim
113 words
A method of manufacturing a heat-shrinkable, puncture resistant, biaxially stretched, thermoplastic film comprising the steps of extruding a primary tube comprising a very low density polyethylene which is a linear copolymer of ethylene and higher alpha olefin containing from 3 to 8 carbon atoms, having a density below about 0.91 g/cm 3 and a 1% secant modulus below about 140,000 kPa; heating the very low density polyethylene primary tube; biaxially stretching the heated primary tube using a double bubble method under conditions wherein the biaxially stretched tube is heat shrinkable from about 30% to about 50% at a temperature of about 90° C. in at least one of the transverse and machine directions.
Claim 3
Dependent Claim
31 words
A method according to claim 1 wherein said biaxially stretched tube is heat shrinkable from about 30% to about 50% at a temperature of about 90° C. in the transverse direction.
Claim 4
Dependent Claim
31 words
A method according to claim 1 wherein said biaxially stretched tube is heat shrinkable from about 30% to about 50% at a temperature of about 90° C. in the machine direction.
Claim 5
Dependent Claim
34 words
A method according to claim 1 wherein said biaxially stretched tube is heat shrinkable from about 30% to about 50% at a temperature of about 90° C. in both the transverse and machine directions.
Claim 6
Dependent Claim
13 words
A method according to claim 1 wherein the film comprises a monolayer film.
Claim 7
Dependent Claim
13 words
A method according to claim 1 wherein the film comprises a multilayer film.
Claim 8
Dependent Claim
15 words
A method according to claim 6 wherein the primary multilayer film is prepared by coextrusion.
Claim 9
Dependent Claim
29 words
A method according to claim 6 wherein at least one layer of said multilayer film comprises a blend of said very low density polyethylene and an ethylene-vinyl acetate copolymer.
Claim 10
Dependent Claim
46 words
A method according to claim 6 wherein the multilayer film comprises a first outer layer of an ethylene-vinyl acetate copolymer, a core layer comprising a barrier film, and a second outer layer comprising a blend of said very low density polyethylene and an ethylene-vinyl acetate copolymer.
Claim 11
Dependent Claim
24 words
A method according to claim 6 wherein said film is irradiated to a dosage level of between about 1 megarad and about 5 megarads.
Claim 12
Dependent Claim
23 words
A method according to claim 1 wherein the polyethylene copolymer has a standard load melt index of up to about 25.0 g/10 minutes.
Claim 13
Dependent Claim
23 words
A method according to claim 1 wherein the polyethylene copolymer has a high load melt index of up to about 1000 g/10 minutes.
Claim 14
Dependent Claim
22 words
A method according to claim 6 wherein the multilayer film has a thickness of from about 1.75 mils to about 3.0 mils.
Claim 15
Dependent Claim
20 words
A method according to claim 6 wherein at least one layer of said multilayer film comprises an oxygen barrier layer.
Claim 16
Dependent Claim
15 words
A method according to claim 14 wherein said oxygen barrier layer is a core layer.
Claim 17
Dependent Claim
35 words
A method according to claim 14 wherein said oxygen barrier layer comprises a copolymer of vinylidene chloride and at least one comonomer selected from the group of comprising vinyl chloride, acrylonitrile and an acrylate ester.
Claim 18
Dependent Claim
33 words
A method according to claim 14 wherein said oxygen barrier layer comprises a copolymer of vinylidene chloride and an acrylate ester wherein vinylidene chloride constitute at least 65 weight percent of the copolymer.
Claim 19
Dependent Claim
33 words
A method according to claim 14 wherein said oxygen barrier layer comprises a copolymer of vinylidene chloride and a vinyl chloride wherein at least 65 weight percent of the copolymer comprises vinylidene chloride.
Claim 20
Dependent Claim
20 words
A method according to claim 14 wherein said oxygen barrier layer comprises a copolymer of vinylidene chloride and methyl methacrylate.
Claim 21
Dependent Claim
23 words
A method according to claim 16 wherein said oxygen barrier layer copolymer comprises between about 70 and 95 weight percent of vinylidene chloride.
Claim 22
Dependent Claim
15 words
A method according to claim 14 wherein said oxygen barrier layer comprises ethylene-vinyl alcohol copolymer.
Claim 23
Dependent Claim
19 words
A method according to claim 14 wherein said oxygen barrier layer comprises a copolymer of vinylidene chloride and acrylonitrile.
Claim 24
Dependent Claim
26 words
A method according to claim 14 wherein said oxygen barrier is a copolymer having at least 65 weight percent of said copolymer derived from vinylidene chloride.
Claim 25
Dependent Claim
22 words
A method according to claim 23 wherein from 70 to about 95 weight percent of said copolymer is derived from vinylidene chloride.
References Cited (Backward Citations)
US4076698B1
Cited
US4076698A
Cited
US3456044A
Cited
US3555604A
Cited
US3424649A
Cited
US3645992A
Cited
CA975280A
Cited
CA982923A
Cited
US4011382A
Cited
US4277578A
Cited
US4212961A
Cited
US4835218A
Cited
US4701496A
Cited
US4542886A
Cited
GB2034336A
Cited
GB2034337A
Cited
GB2034723A
Cited
US4399181A
Cited
US4469752A
Cited
US4354997A
Cited
US4424243A
Cited
US4330639A
Cited
GB2066274A
Cited
US4335224A
Cited
US4429079A
Cited
US4456646A
Cited
US4405774A
Cited
US4438238A
Cited
GB2097324A
Cited
US4597920A
Cited
US4495249A
Cited
GB2131033A
Cited
GB2133020A
Cited
US4447480A
Cited
EP0120503A1
Cited
US4668752A
Cited
US4600616A
Cited
US4617241A
Cited
GB2154178A
Cited
US4832897A
Cited
US4640856A
Cited
EP0199871A2
Cited
US4894107A
Cited
US4668575A
Cited
JPS6345306A
Cited
JPS64339A
Cited
JPS643228A
Cited
JPH026621A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-12-10 | 1994-06-11 | 1994-12-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-12-10 | 1998-06-11 | 1998-12-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-12-10 | 2002-06-11 | 2002-12-11 | $7700.00 | Window Closed / Lapsed |