Catalyst for purifying exhaust gases and preparation thereof
Assignee: WC Heraus GmbH and Co KG
•
Filing: 1989-03-02
•
Granted: 1990-12-04
•
Expires: 2009-03-02
Abstract
Abstract The invention concerns a catalyst for oxidation of hydrocarbons and carbon monoxide and/or reduction of nitrogen oxides. The catalyst consists of a carrier body and on this a catalytical coating, which consists of a washcoat layer containing a support material with a high specific surface area, one or more metal oxides with a promoting effect and at least two catalytically active noble metals within the washcoat or on the washcoat. The catalytical coating consists of at least two washcoat layers containing different amounts of at least one noble metal, in such a way that at least one noble metal is concentrated to more than 50% by weight of its total amount to at least one of the layers and that at least two noble metals are contained together in at least one of the layers. The invention also concerns a process for the preparation of said catalyst in order to obtain said layers with different composition of noble metals. The invention also concerns the use of said catalyst for purification of exhaust gases from internal combustion engines.
Inventors
- 👤 Arne Frestad
- 👤 Soren Andersson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 11:54
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/34; B01D53/92; B01D53/94; B01D53/9445; B01D53/945; B01J; B01J23/00; B01J23/70; B01J23/89; B01J37/00; B01J37/02; B01J37/024; B01J37/0244; B01D2255/00; B01D2255/90; B01D2255/902; Y; Y02; Y02T; Y02T10/00; Y02T10/10; Y02T10/12
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
130 words
A catalyst for treating a gas flow for the oxidation of hydrocarbons and carbon monoxide and/or the reduction of nitrogen oxides comprising a carrier body and a catalytic coating, said coating comprising at least two washcoat layers applied parallel to the gas flow, each washcoat layer comprising a support material having a high surface area and one or more metal oxide promoters and one layer containing at least one catalytically active noble metal, the amount of said at least one catalytically active noble metal being different in each washcoat layer with more than 50% by weight of the total amount of said at least one catalytically active noble metal being contained in one said layer and further wherein at least one layer contains at least two catalytically active noble metals.
Claim 2
Dependent Claim
130 words
A catalyst for treating a gas flow for the oxidation of hydrocarbons and carbon monoxide and/or the reduction of nitrogen oxides comprising a carrier body and a catalytic coating, said coating comprising at least two washcoat layers applied parallel to the gas flow, each washcoat layer comprising a support material having a high surface area and one or more metal oxide promoters and one layer containing at least one catalytically active noble metal, the amount of said at least one catalytically active noble metal being different in each washcoat layer with more than 50% by weight of the total amount of said at least one catalytically active noble metal being contained in one said layer and further wherein at least one layer contains at least two catalytically active noble metals.
Claim 3
Dependent Claim
124 words
A catalyst according to claim 1 wherein each said layer contains (a) at least 50% by weight of a support material a specific surface area of 50-200 m 2 /g, (b) one or more metal oxide promoters with a reaction promoting and temperature stabilizing effect selected from the group consisting of 1-10% by weight of alkaline earth metal oxides, 1-50% by weight of rare earth metal oxides, 1-20% by weight of group IV B metal oxides, or 1-20% by weight of oxides of metals selected from the group consisting of W, Co, Mo, Fe, Ni, Zn, Sn, and Cr, and (c) at least one catalytically active noble metal in an amount not exceeding 3% by weight, calculated on weight of the entire catalytic coating.
Claim 4
Dependent Claim
73 words
A catalyst according to claim 1 wherein the metal oxide promoter is constituted of: 1-50% by weight of rare earth metal oxides, and none, one of or both of the following: 1-10% by weight of group IV B metal oxides, 1-5% by weight of an oxide of a metal selected from the group consisting of W, Co, Mo, Fe, Ni, Zn, Sn and Cr, calculated on the weight of the entire catalytic coating.
Claim 5
Dependent Claim
49 words
A catalyst according to claim 1 wherein the noble metals are Pt and Rh and one layer contains more than 50% by weight of the total amount of Pt and also contains Rh, while another layer contains the remaining part of the total amount of the Rh and Pt.
Claim 6
Dependent Claim
39 words
A catalyst according to claim 1 wherein one layer contains 75-100% by weight of the total amount of Pt and also contains Rh, while another layer contains the remaining part of the total amount of the Rh and Pt.
Claim 7
Dependent Claim
49 words
A catalyst according to claim 1 wherein the noble metals are Pt and Rh and one layer contains more than 50% by weight of the total amount of Rh and also contains Pt, while another layer contains the remaining part of the total amount of the Pt and Rh.
Claim 8
Dependent Claim
39 words
A catalyst according to claim 1 wherein one layer contains 75-100% by weight of the total amount of Rh and also contains Pt, while another layer contains the remaining part of the total amount of the Pt and Rh.
Claim 9
Dependent Claim
19 words
A catalyst according to claim 1 wherein the different layers also contain different amounts of the metal oxide promoters.
Claim 10
Dependent Claim
25 words
A catalyst according to claim 1 wherein the support material is Al 2 O 3 with a specific surface area of 50-200 m 2 /g.
Claim 11
Dependent Claim
37 words
A catalyst according to claim 1 wherein said catalytic coating comprises a layer of from 0 to 50% by weight of a support material with a high specific surface area, the remainder being a metal oxide promoter.
Claim 12
Dependent Claim
41 words
A catalyst according to claim 10 wherein said metal oxide promoter is constituted of 50-100% by weight of rare earth metal oxides and 0-25% by weight of group IV B metal oxides and also 0-50% by weight of a support material.
Claim 13
Dependent Claim
41 words
A catalyst according to claim 10 wherein said metal oxide promoter is constituted of 50-100% by weight of group IV B metal oxides and 0-25% by weight of rare earth metal oxides and also 0-50% by weight of a support material.
Claim 14
Dependent Claim
25 words
A catalyst according to claim 10 wherein the support material is Al 2 O 3 with a specific surface area of 50-200 m 2 /g.
Claim 15
Dependent Claim
79 words
A catalyst according to claim 10 wherein the metal oxide promoter is one or more metal oxide with a reaction promoting and temperature stabilizing effect selected from the group consisting of 1-10% by weight of alkaline earth metal oxides, 1-50% by weight of rare earth metal oxides, 1-20% by weight of group IV B metal oxides, or 1-20% by weight of oxides of metals selected from the group consisting of W, Co, Mo, Fe, Ni, Zn, Sn, and Cr.
Claim 16
Dependent Claim
85 words
A process for the preparation of the catalyst of claim 1 wherein the layered structure of the catalyst is built up by a sequential coating of a carrier body which includes the steps of: (1) contacting the carrier body with a washcoat slurry, (2) contacting the product obtained in step (1) with a solution containing one or more noble metals, and (3) applying one or more further layers with another noble metal composition or without a noble metal in analogy with steps (1) and (2).
Claim 17
Dependent Claim
88 words
A process for the preparation of the catalyst of claim 1 wherein the layered structure of the catalyst is built up by a sequential coating of a carrier body which includes the steps of: (1) contacting a washcoat slurry with a solution containing one or more noble metals, (2) contacting a carrier body with the noble metal treated washcoat obtained in step (1), and (3) applying one or more further layers with another noble metal composition or without a noble metal in analogy with steps (1) and (2).
Claim 18
Dependent Claim
29 words
In an automotive catalytic converter comprising a catalyst of a carrier body coated with a washcoat, the improvement which comprises using as the catalyst, the catalyst of claim 1.
Claim 19
Dependent Claim
29 words
In an automotive catalytic converter comprising a catalyst of a carrier body coated with a washcoat. The improvement which comprises using as the catalyst, the catalyst of claim 10.
References Cited (Backward Citations)
US3931050A
Cited
US3901821A
Cited
JPS50145381A
Cited
US4118199A
Cited
US4237032A
Cited
GB2000985A
Cited
US4152301A
Cited
US4128506A
Cited
US4153579A
Cited
US4283308A
Cited
EP0056729A2
Cited
GB2096482A
Cited
US4405506A
Cited
EP0091814A1
Cited
GB2122912A
Cited
US4492769A
Cited
EP0125565A2
Cited
EP0152052A2
Cited
EP0170841A1
Cited
EP0262962A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-12-03 | 1994-06-04 | 1994-12-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-12-03 | 1998-06-04 | 1998-12-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-12-03 | 2002-06-04 | 2002-12-04 | $7700.00 | Window Closed / Lapsed |