Assignee: WR Grace and Co Conn
•
Filing: 1981-04-13
•
Granted: 1983-09-20
•
Expires: 2001-04-13
Abstract
Abstract A refractory inorganic oxide support is impregnated with a mixture of a platinum sulfito complex solution and a rhodium nitrate solution or with a mixture of a platinum sulfito complex solution, a rhodium nitrate solution, and a rhodium sulfito complex solution and the impregnated support is activated. The method produces a catalyst which has a maximum platinum concentration within 20 microns of the external surface of the support and at least about 70 percent of the total platinum located within 100 microns of the external surface of the support. The catalyst also has at least about 30 percent of the total rhodium located within 20 microns of the external surface of the support and at least about 40 percent of the total rhodium located at 20 to 100 microns from the external surface of the support.
Inventors
- 👤 Gwan Kim
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 10:33
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/34; B01D53/92; B01D53/94; B01D53/9445; B01D53/945; B01J; B01J23/00; B01J23/38; B01J23/40; B01J23/46; B01J23/464; B01J35/00; B01J35/30; B01J35/396; Y; Y02; Y02T; Y02T10/00; Y02T10/10; Y02T10/12
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
128 words
A catalyst composition comprising platinum, palladium and rhodium deposited on a refractory inorganic oxide support and having a maximum platinum concentration within 20 microns of the exterior surface of the support, at least about 70 percent of the total platinum located within 100 microns of the external surface of the support, at least about 10 percent of the total palladium located within 20 microns of the external surface of the support, a maximum rhodium concentration within 20 microns of the external surface of the support, at least about 30 percent of the total rhodium located within 20 microns of the external surface of the support, and at least about 40 percent of the total rhodium located at 20 to 100 microns from the external surface of the support.
Claim 2
Dependent Claim
128 words
A catalyst composition comprising platinum, palladium and rhodium deposited on a refractory inorganic oxide support and having a maximum platinum concentration within 20 microns of the exterior surface of the support, at least about 70 percent of the total platinum located within 100 microns of the external surface of the support, at least about 10 percent of the total palladium located within 20 microns of the external surface of the support, a maximum rhodium concentration within 20 microns of the external surface of the support, at least about 30 percent of the total rhodium located within 20 microns of the external surface of the support, and at least about 40 percent of the total rhodium located at 20 to 100 microns from the external surface of the support.
Claim 3
Dependent Claim
26 words
The catalyst composition of claim 1 having at least about 35 percent of the total rhodium within 20 microns of the external surface of the support.
Claim 4
Dependent Claim
29 words
The catalyst composition of claim 1 having at least about 50 percent of the total rhodium located at 20 to 100 microns from the external surface of the support.
Claim 5
Dependent Claim
29 words
The catalyst composition of claim 1 having less than about 5 percent of the total rhodium located at more than 100 microns from the external surface of the support.
Claim 6
Dependent Claim
27 words
The catalyst composition of claim 1 having at least about 20 percent of the total rhodium located within 10 microns of the external surface of the support.
Claim 7
Dependent Claim
27 words
The catalyst composition of claim 1 having at least about 90 percent of the total platinum located within 100 microns of the external surface of the support.
Claim 8
Dependent Claim
27 words
The catalyst composition of claim 1 having at least about 20 percent of the total platinum located within 20 microns of the external surface of the support.
Claim 9
Dependent Claim
29 words
The catalyst composition of claim 1 having from about 30 to about 60 percent of the total palladium located within 100 microns of the external surface of the support.
Claim 10
Dependent Claim
29 words
The catalyst composition of claim 1 having from about 70 to about 90 percent of the total palladium located within 200 microns of the external surface of the support.
Claim 11
Dependent Claim
15 words
The catalyst composition of claim 1 in which the support comprises shaped spheroidal alumina particles.
Claim 12
Dependent Claim
15 words
The catalyst composition of claim 1 in which the support comprises shaped spheroidal ceria-alumina particles.
Claim 13
Dependent Claim
84 words
A method of preparing the catalyst composition of claim 11 comprising impregnating shaped spheroidal ceria-alumina particles with a palladium sulfito complex solution; impregnating the particles with a mixture of an acid in situ platinum sulfito complex solution, a rhodium nitrate solution, and an acid in situ rhodium sulfito complex solution, said mixture containing sufficient amounts of each rhodium solution so that each rhodium solution provides from about 40 to about 60 percent of the total rhodium in the mixture; and activating the impregnated particles.
Claim 14
Dependent Claim
88 words
A method of preparing the catalyst composition of claim 1 comprising impregnating a refractory inorganic oxide support with a palladium sulfito complex solution; impregnating the support with a mixture of a platinum sulfito complex solution, a rhodium nitrate solution, and a rhodium sulfito complex solution, said rhodium nitrate solution and rhodium sulfito complex solution being present in the mixture in amounts such that from about 30 to about 70 weight percent of the total rhodium in the mixture is provided by each solution; and activating the impregnated support.
Claim 15
Dependent Claim
44 words
The method of claim 13 in which the amounts of rhodium nitrate solution and rhodium sulfito complex solution in the mixture are such that from about 40 to about 60 weight percent of the total rhodium in the mixture is provided by each solution.
Claim 16
Dependent Claim
19 words
The method of claim 13 in which the rhodium sulfito complex solution is an acid complex in situ solution.
Claim 17
Dependent Claim
18 words
The method of claim 13 in which the platinum sulfito complex solution is an acid in situ solution.
Claim 18
Dependent Claim
20 words
The method of claim 13 in which the palladium sulfito complex solution is impregnated prior to impregnation of the mixture.
Claim 19
Dependent Claim
19 words
The method of claim 13 in which the palladium sulfito complex solution is an acid complex in situ solution.
Claim 20
Dependent Claim
17 words
The method of claim 13 in which the palladium sulfito complex solution further comprises dibasic ammonium citrate.
Claim 21
Dependent Claim
22 words
The method of claim 13 further comprising adjusting the pH of the mixture to about 1 to about 7 prior to impregnation.
Claim 22
Dependent Claim
22 words
The method of claim 13 further comprising adjusting the pH of the mixture to about 1.5 to about 5 prior to impregnation.
Claim 23
Dependent Claim
24 words
The method of claim 13 in which the platinum sulfito complex contains from about 1 to about 4 sulfito groups per atom of platinum.
Claim 24
Dependent Claim
24 words
The method of claim 13 in which the rhodium sulfito complex contains from about 1 to about 3 sulfito groups per atom of rhodium.
Claim 25
Dependent Claim
32 words
The method of claim 13 in which the rhodium sulfito complex is prepared by reacting rhodium trichloride with sulfurous acid for 1/2 to 2 hours at about 40 to about 80° C.
Claim 26
Dependent Claim
34 words
The method of claim 13 in which the rhodium sulfito complex is prepared by reacting rhodium trichloride with sulfurous acid for about 16 to about 24 hours at about 20 to about 30° C.
Claim 27
Dependent Claim
14 words
The method of claim 13 in which the support comprises shaped spheroidal alumina particles.
Claim 28
Dependent Claim
14 words
The method of claim 13 in which the support comprises shaped spheroidal ceria-alumina particles.
Claim 29
Dependent Claim
161 words
A catalyst composition comprising platinum, palladium, and rhodium deposited on shaped spheroidal ceria-alumina particles and having a maximum platinum concentration within 20 microns of the external surface of the particles, at least about 70 percent of the total platinum located within 100 microns of the external surface of the particles, at least about 10 percent of the total palladium located within 20 microns of the external surface of the particles, at least about 20 percent of the total rhodium and a maximum rhodium concentration located within 10 microns of the external surface of the particles, at least about 35 percent of the total rhodium located within 20 microns of the external surface of the particles, from about 45 to about 55 percent of the total rhodium located at 20 to 100 microns from the external surface of the particles, and less than about 5 percent of the total rhodium located more than 100 microns from the external surface of the support.
Claim 30
Dependent Claim
161 words
A catalyst composition comprising platinum, palladium, and rhodium deposited on shaped spheroidal ceria-alumina particles and having a maximum platinum concentration within 20 microns of the external surface of the particles, at least about 70 percent of the total platinum located within 100 microns of the external surface of the particles, at least about 10 percent of the total palladium located within 20 microns of the external surface of the particles, at least about 20 percent of the total rhodium and a maximum rhodium concentration located within 10 microns of the external surface of the particles, at least about 35 percent of the total rhodium located within 20 microns of the external surface of the particles, from about 45 to about 55 percent of the total rhodium located at 20 to 100 microns from the external surface of the particles, and less than about 5 percent of the total rhodium located more than 100 microns from the external surface of the support.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-09-19 | 1987-03-21 | 1987-09-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-09-19 | 1991-03-21 | 1991-09-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-09-19 | 1995-03-21 | 1995-09-20 | $7700.00 | Window Closed / Lapsed |