Treatment of metal foil
Assignee: GBC Metals LLC
•
Filing: 1989-04-05
•
Granted: 1990-10-09
•
Expires: 2009-04-05
Abstract
Abstract A treatment for metal foil, particularly copper or copper alloy foil, to be used in electrical and electronic applications wherein the bond strength of the foil is improved. The treatment includes applying an aqueous solution of chromic acid phosphoric acid to the foil, rinsing the foil in an aqueous solution having a pH of at least 8 and thereafter forming a plurality of copper or copper oxide dendritic structures on at least one side of the foil. The foil may be further treated by applying a coating of zinc or other suitable material over the dentritic structure and an anti-tarnish treatment applied. The anti-tarnish treatment includes applying a thin coating of zinc to the smooth side of the foil followed by treating the foil with a chromic acid sulfuric acid solution to provide a layer of chromate on both surfaces. The foil is then further treated by rinsing with an aqueous solution of a pH of at least 8 and dried.
Inventors
- 👤 Lifun Lin
- 👤 Ned W. Polan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 14:22
CPC Classifications
C; C25; C25D; C25D5/00; C25D5/10; C25D5/34; C25D5/48; C25D5/60; C25D5/605; H; H05; H05K; H05K3/00; H05K3/38; H05K3/382; H05K3/384; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0355; H05K2203/00; H05K2203/03; H05K2203/0307; H05K2203/0392; H05K2203/07; H05K2203/0703; H05K2203/0723
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
57 words
A process of treating metal foil comprising applying an aqueous chromic acid solution to said foil, said solution having a concentration of chromic acid in the range of about 0.002 g/l to about 1.0 g/l and thereafter forming a plurality of copper or copper oxide dentritic or nodular structures on at least one surface of said foil.
Claim 2
Dependent Claim
57 words
A process of treating metal foil comprising applying an aqueous chromic acid solution to said foil, said solution having a concentration of chromic acid in the range of about 0.002 g/l to about 1.0 g/l and thereafter forming a plurality of copper or copper oxide dentritic or nodular structures on at least one surface of said foil.
Claim 3
Dependent Claim
39 words
The process of claim 1 further comprising applying an aqueous rinse solution to said foil after applying said chromic acid solution and before forming said dendritic or nodular structures, said rinse solution having a pH of at least 8.
Claim 4
Dependent Claim
39 words
The process of claim 2 wherein said aqueous rinse solution comprises an aqueous solution having a pH in the range of about 9 to about 11.5 and temperature in the range of about room temperature to about 100° C.
Claim 5
Dependent Claim
43 words
The process of claim 2 wherein said rinse solution contains a material selected from the group consisting of the salts of alkali metals, the salts of alkaline earth metals, the hydroxides of the alkali metals, and the hydroxides of the alkaline earth metals.
Claim 6
Dependent Claim
32 words
The process of claim 2 wherein said rinse solution contains at least 1 ppm of a material selected from the group consisting of calcium hydroxide, sodium hydroxide, potassium hydroxide, and ammonium hydroxide.
Claim 7
Dependent Claim
26 words
The process of claim 2 further comprising rinsing said foil in a dilute solution of sulfuric acid after said aqueous rinse and before forming said structure.
Claim 8
Dependent Claim
22 words
The process of claim 6 wherein said sulfuric acid solution comprises from about 1.0 to about 50 percent by weight sulfuric acid.
Claim 9
Dependent Claim
20 words
The process of claim 7 wherein said sulfuric acid solution comprises from about 5 to about 15 percent by weight.
Claim 10
Dependent Claim
77 words
A process of treating metal foil comprising applying an aqueous solution of chromic acid and phosphoric acid to said foil, said solution having a concentration of chromic acid in the range of about 0.002 g/l to about 1.00 g/l and a concentration of phosphoric acid in the range of about 0.002 g/l to about 1.00 g/l, thereafter forming a plurality of copper or copper oxide dentritic or nodular structures on at least one surface of said foil.
Claim 11
Dependent Claim
77 words
A process of treating metal foil comprising applying an aqueous solution of chromic acid and phosphoric acid to said foil, said solution having a concentration of chromic acid in the range of about 0.002 g/l to about 1.00 g/l and a concentration of phosphoric acid in the range of about 0.002 g/l to about 1.00 g/l, thereafter forming a plurality of copper or copper oxide dentritic or nodular structures on at least one surface of said foil.
Claim 12
Dependent Claim
41 words
The process of claim 9 further comprising applying an aqueous rinse solution to said foil after applying said chromic acid phosphoric acid solution and before forming said dentritic or nodular structures, said rinse solution having a pH of at least 8.
Claim 13
Dependent Claim
40 words
The process of claim 10 wherein said rinsing step comprises applying an aqueous solution having a pH in the range of about 9 to about 11.5 and a temperature in the range of about room temperature to about 100° C.
Claim 14
Dependent Claim
43 words
The process of claim 10 wherein said rinse solution contains a material selected from the group consisting of the salts of alkali metals, the salts of alkaline earth metals, the hydroxides of the alkali metals, and the hydroxides of the alkaline earth metals.
Claim 15
Dependent Claim
32 words
The process of claim 10 wherein said rinse solution contains at least 1 ppm of a material selected from the group consisting of calcium hydroxide, sodium hydroxide, potassium hydroxide, and ammonium hydroxide.
Claim 16
Dependent Claim
26 words
The process of claim 10 further comprising rinsing said foil in a dilute solution of sulfuric acid after said aqueous rinse and before forming said structure.
Claim 17
Dependent Claim
22 words
The process of claim 14 wherein said sulfuric acid solution comprises from about 1.0 to about 50 percent by weight sulfuric acid.
Claim 18
Dependent Claim
20 words
The process of claim 15 wherein said sulfuric acid solution comprises from about 5 to about 15 percent by weight.
Claim 19
Dependent Claim
33 words
The process of claim 9 wherein said acid solution applying step comprises immersing said material in said acid solution for a time in the range of about 1 second to about 120 seconds.
Claim 20
Dependent Claim
53 words
The process of claim 9 wherein said acid solution applying step comprises immersing said material in said acid solution while said acid solution in at a temperature in the range of about ambient temperature to about 90° C. for a time period in the range of about 5 seconds to about 20 seconds.
Claim 21
Dependent Claim
44 words
The process of claim 9 wherein said acid solution applying step comprises immersing said foil in a solution obtaining from about 0.1 g/l to about 0.3 g/l of said chromic acid and from about 0.1 g/l to about 0.5 g/l of said phosphoric acid.
Claim 22
Dependent Claim
35 words
The process of claim 9 wherein said dentritic or nodular forming step comprises electrolytically forming a layer of nodular copper or copper oxide particles on said at least one surface and bonding the particles thereto.
Claim 23
Dependent Claim
57 words
The process of claim 9 wherein said nodular or dendritic structures are applied to one side of said foil, said process further comprising applying a layer of zinc on at least the side of said foil opposite said side having said structures thereon, and thereafter treating said foil with a solution of chromic acid and sulfuric acid.
Claim 24
Dependent Claim
20 words
The process of claim 21 wherein said layer of zinc is from about 0.06 to about 0.003 mg/cm 2 .
Claim 25
Dependent Claim
46 words
The process of claim 21 wherein the layer of zinc is applied to both sides of said foil, the side of the foil having said structures thereon, said layer of zinc on said structure side of said being thicker than said layer on said other side.
Claim 26
Dependent Claim
45 words
The process of claim 21 wherein said chromic acid/sulfuric acid solution has a concentration of chromic acid in the range of about 0.02 g/l to about 100 g/l and a concentration of sulfuric acid in the range of about 0.02 g/l to about 20 g/l.
Claim 27
Dependent Claim
36 words
The process of claim 24 wherein said concentration of said chromic acid is from about 0.1 g/l to about 0.3 g/l and the concentration of said sulfuric acid is about 0.02 g/l to about 0.7 g/l.
Claim 28
Dependent Claim
22 words
The process of claim 21 further comprising applying an aqueous rinse solution to said foil having a pH of at least 8.
Claim 29
Dependent Claim
39 words
The process of claim 26 wherein said rinsing step comprises applying an aqueous solution having a pH in the range of about 9 to about 11.5 and temperature in the range of about room temperature to about 100° C.
Claim 30
Dependent Claim
43 words
The process of claim 26 wherein said rinse solution contains a material selected from the group consisting of the salts of alkali metals, the salts of alkaline earth metals, the hydroxides of the alkali metals, and the hydroxides of the alkaline earth metals.
Claim 31
Dependent Claim
32 words
The process of claim 26 wherein said rinse solution contains at least 1 ppm of a material selected from the group consisting of calcium hydroxide, sodium hydroxide, potassium hydroxide, and ammonium hydroxide.
Claim 32
Dependent Claim
58 words
The process of claim 9 wherein said nodular or dendritic structures are applied to one side of said foil, said process further comprising applying a layer of zinc on at least the side of said foil opposite said side having said structures therein, and thereafter treating said foil with a solution of chromic acid and a sulfate compound.
Claim 33
Dependent Claim
47 words
The process of claim 21 wherein said solution of chromic acid and a sulfate compound has a concentration of chromic acid in the range of abut 0.02 g/l to about 100 g/l and a sulfate concentration in the amount of about 0.02 g/l to about 20 g/l.
References Cited (Backward Citations)
DE112145C
Cited
US2030601A
Cited
US2418608A
Cited
US2412543A
Cited
US2647865A
Cited
US3220897A
Cited
US3293109A
Cited
US3322656A
Cited
GB1211494A
Cited
US3585010A
Cited
GB1293801A
Cited
US3625844A
Cited
US3677828A
Cited
US3716427A
Cited
US3699018A
Cited
US3857681A
Cited
US3764400A
Cited
US3918926A
Cited
USRE30180E
Cited
US3853716A
Cited
US4053370A
Cited
US4049481A
Cited
US4131517A
Cited
GB2030176A
Cited
GB2073779A
Cited
US4387006A
Cited
US4468293A
Cited
US4432846A
Cited
US4515671A
Cited
US4529486A
Cited
US4532014A
Cited
US4549950A
Cited
US4568431A
Cited
US4652346A
Cited
US4647315A
Cited
US4789438A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-08 | 1994-04-09 | 1994-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-08 | 1998-04-09 | 1998-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-08 | 2002-04-09 | 2002-10-09 | $7700.00 | Window Closed / Lapsed |