Abstract
Abstract A process and apparatus for treating a metal foil to enhance its ability to be bonded to a substrate comprise immersing the metal foil in an electrolytic cell having an electrolyte bath solution containing copper and applying a current having regularly recurring pulses and preferably flowing in only one direction to the cell. The current causes a dendritic layer of copper to be deposited on at least one surface of the metal foil at a first current density and bonded thereto at a second current density. The process and apparatus are particularly suited for treating copper foil.
Inventors
- 👤 Ned W. Polan
- 👤 Chung-Yao Chao
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 13:52
CPC Classifications
C; C25; C25D; C25D5/00; C25D5/60; C25D5/605; B; B32; B32B; B32B15/00; B32B15/04; B32B38/00; B32B38/0008; C25D5/18; H; H05; H05K; H05K3/00; H05K3/38; H05K3/382; H05K3/384; B32B2457/00; B32B2457/08; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0355; H05K2203/00; H05K2203/03; H05K2203/0307; H05K2203/07; H05K2203/0703; H05K2203/0723; Y; Y10; Y10S; Y10S204/00; Y10S204/09; Y10T; Y10T428/00; Y10T428/12; Y10T428/12472; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12903; Y10T428/1291; Y10T428/12993
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
189 words
A process for treating metal foil for enhancing its ability to adhere to a substrate, said process comprising: providing an electrolytic cell having an electrolytic bath solution containing a concentration of metal and an anode; immersing said foil as a cathode in said solution; providing a non-zero base cathodic current having a desired frequency and a desired waveform with recurring pulses, each said pulse comprising a first portion having a first current density for a first time period and a base portion having a second current density for a second time period, said first current density being greater than the limiting current density and substantially larger than said second current density, and said second current density being less than the limiting current density; and applying said current across said cell and subjecting said foil to a plurality of said current pulses having said first current density of each said pulse applied for less than about 0.1 seconds so that said metal from said solution is deposited onto said foil as a fine dendritic plating having improved peel strength, improved resistance to wear and stress, and improved powder transfer characteristics.
Claim 2
Dependent Claim
189 words
A process for treating metal foil for enhancing its ability to adhere to a substrate, said process comprising: providing an electrolytic cell having an electrolytic bath solution containing a concentration of metal and an anode; immersing said foil as a cathode in said solution; providing a non-zero base cathodic current having a desired frequency and a desired waveform with recurring pulses, each said pulse comprising a first portion having a first current density for a first time period and a base portion having a second current density for a second time period, said first current density being greater than the limiting current density and substantially larger than said second current density, and said second current density being less than the limiting current density; and applying said current across said cell and subjecting said foil to a plurality of said current pulses having said first current density of each said pulse applied for less than about 0.1 seconds so that said metal from said solution is deposited onto said foil as a fine dendritic plating having improved peel strength, improved resistance to wear and stress, and improved powder transfer characteristics.
Claim 3
Dependent Claim
38 words
The process of claim 1 wherein said current applying step further comprises: subjecting said foil to a plurality of said current pulses having said first current density of each said pulse applied for less than about 0.04 seconds.
Claim 4
Dependent Claim
16 words
The process of claim 1 further comprising: subjecting said foil to greater than 10 current pulses.
Claim 5
Dependent Claim
16 words
The process of claim 1 further comprising: subjecting said foil to at least 25 current pulses.
Claim 6
Dependent Claim
66 words
The process of claim 1 wherein said electrolytic cell providing step further comprises: providing a bath solution having copper in a concentration of about 10 g/l to about 60 g/l and sulfuric acid in a concentration of about 10 g/l to about 100 g/l; and maintaining said bath solution substantially at room temperature, whereby said metal deposited onto said foil from said solution comprises said copper.
Claim 7
Dependent Claim
56 words
The process of claim 1 wherein said step of applying said current further comprises: applying said current with said first current density being in the range of about 150 mA/cm 2 to about 300 mA/cm 2 and said second current density being in the range of about 10 mA/cm 2 to about 40 mA/cm 2 .
Claim 8
Dependent Claim
30 words
The process of claim 1 wherein said current applying step further comprises: applying said current with said frequency being in the range of about 4 Hz to about 1000 Hz.
Claim 9
Dependent Claim
30 words
The process of claim 1 wherein said current applying step further comprises: applying said current with said frequency being in the range of about 12 Hz to about 300 Hz.
Claim 10
Dependent Claim
24 words
The process of claim 1 further comprising: applying said current for a time in the range of about 2 seconds to about 60 seconds.
Claim 11
Dependent Claim
35 words
The process of claim 1 further comprising: providing a constant current source and a function generator; and generating said current having said desired waveform and frequency with said constant current source and said function generator.
Claim 12
Dependent Claim
36 words
The process of claim 1 further comprising: providing a constant voltage source and a function generator; and generating a voltage having a desired waveform and said current with said current voltage source and said function generator.
Claim 13
Dependent Claim
188 words
A process for treating metal foil for enhancing its ability to adhere to a substrate, said process comprising: providing an electrolytic cell having an electrolytic bath solution containing a concentration of metal and an anode; immersing said foil as a cathode in said solution; providing a non-zero base cathodic current having a desired frequency and a desired waveform with recurring pulses, each said pulse comprising a first portion having a first current density for a first time period and a base portion having a second current density for a second time period, said first current density being greater than the limiting current density and substantially larger than said second current density, said second current density being less than the limiting current density; and applying said current across said cell and subjecting said foil to more than 10 of said pulses with said first current density of each pulse being applied for less than about 0.125 seconds so that said metal from said solution is deposited onto said foil as a fine dendritic plating having improved peel strength, improved resistance to wear and stress, and improved powder transfer characteristics.
Claim 14
Dependent Claim
188 words
A process for treating metal foil for enhancing its ability to adhere to a substrate, said process comprising: providing an electrolytic cell having an electrolytic bath solution containing a concentration of metal and an anode; immersing said foil as a cathode in said solution; providing a non-zero base cathodic current having a desired frequency and a desired waveform with recurring pulses, each said pulse comprising a first portion having a first current density for a first time period and a base portion having a second current density for a second time period, said first current density being greater than the limiting current density and substantially larger than said second current density, said second current density being less than the limiting current density; and applying said current across said cell and subjecting said foil to more than 10 of said pulses with said first current density of each pulse being applied for less than about 0.125 seconds so that said metal from said solution is deposited onto said foil as a fine dendritic plating having improved peel strength, improved resistance to wear and stress, and improved powder transfer characteristics.
Claim 15
Dependent Claim
22 words
The process of claim 12 wherein said current applying step further comprises: subjecting said foil to at least 25 of said pulses.
Claim 16
Dependent Claim
66 words
The process of claim 12 wherein said electrolytic cell providing step further comprises: providing a bath solution having copper in a concentration of about 10 g/l to about 60 g/l and sulfuric acid in a concentration of about 10 g/l to about 100 g/l; and maintaining said bath solution substantially at room temperature, whereby said metal deposited onto said foil from said solution comprises said copper.
Claim 17
Dependent Claim
56 words
The process of claim 12 wherein said step of applying said current further comprises: applying said current with said first current density being in the range of about 150 mA/cm 2 to about 300 mA/cm 2 and said second current density being in the range of about 10 mA/cm 2 to about 40 mA/cm 2 .
Claim 18
Dependent Claim
30 words
The process of claim 12 wherein said current applying step further comprises: applying said current with said frequency being in the range of about 4 Hz to about 1000 Hz.
Claim 19
Dependent Claim
30 words
The process of claim 12 wherein said current applying step further comprises: applying said current with said frequency being in the range of about 12 Hz to about 300 Hz.
Claim 20
Dependent Claim
24 words
The process of claim 12 further comprising: applying said current for a time in the range of about 2 seconds to about 60 seconds.
Claim 21
Dependent Claim
80 words
A treated metal foil having improved ability to adhere to a substrate, said treated foil comprising: a metal foil having a fine dendritic plating on one of its surfaces; said dendritic plating comprising a plurality of metalic dendrites firmly bonded to said foil so as to provide said foil with improved peel strength, improved resistance to wear and stress, and improved powder transfer characteristics; and said dendritic plating being applied to the metal foil by the process of claim 1.
Claim 22
Dependent Claim
80 words
A treated metal foil having improved ability to adhere to a substrate, said treated foil comprising: a metal foil having a fine dendritic plating on one of its surfaces; said dendritic plating comprising a plurality of metallic dendrites firmly bonded to said foil so as to provide said foil with improved peel strength, improved resistance to wear and stress, and improved powder transfer characteristics; and said dendritic plating being applied to the metal foil by the process of claim 12.
References Cited (Backward Citations)
US30180A
Cited
GB591783A
Cited
GB757892A
Cited
DE1060075B
Cited
GB943872A
Cited
GB928267A
Cited
US3220897A
Cited
US3293109A
Cited
US3322656A
Cited
US3328275A
Cited
DE1496748A1
Cited
US3227637A
Cited
US3454376A
Cited
US3518168A
Cited
GB1211494A
Cited
US3585010A
Cited
US3674656A
Cited
GB1333254A
Cited
US3699018A
Cited
GB1349696A
Cited
US3857681A
Cited
US3918926A
Cited
USRE30180E
Cited
US3799847A
Cited
US3857766A
Cited
GB1396436A
Cited
US4010005A
Cited
DE2500160A1
Cited
DD112145A1
Cited
US3959088A
Cited
US4140599A
Cited
GB1515361A
Cited
US4049481A
Cited
US4082591A
Cited
US4061837A
Cited
DE2739427A1
Cited
GB1529187A
Cited
GB1543301A
Cited
GB1548550A
Cited
US4169018A
Cited
DD134785A1
Cited
GB2073778A
Cited
GB2073779A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-08-28 | 1988-02-27 | 1988-08-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-08-28 | 1992-02-27 | 1992-08-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-08-28 | 1996-02-27 | 1996-08-28 | $7700.00 | Window Closed / Lapsed |