Process for producing transparent substrate having thereon transparent conductive pattern elements separated by light-shielding insulating film, and process for producing surface-colored material

Claim 2

A process for producing a transparent substrate having on one side transparent conductive pattern elements separated by a light-shielding insulating film, which process comprising carrying out the following steps in the following order: (I) a step of forming on one side of a transparent substrate transparent conductive pattern elements having thereon light-shielding inorganic film pattern elements, (II) a step of coating a pigment- and/or dye-containing curable resin on the same side of the transparent substrate, (III) a step of applying a light to the other side (the back side) of the transparent substrate to selectively cure the portion of the curable resin by using the light-shielding inorganic film pattern elements as a mask, (IV) a step of removing the uncured portion of the curable resin to form a light-shielding insulating film consisting of a colored cured resin, and (V) a step of peeling the light-shielding inorganic film pattern elements on the transparent conductive pattern elements.

Claim 3

A process according to claim 1, wherein the step (I) of forming on one side of a transparent substrate transparent conductive pattern elements having thereon light-shielding inorganic film pattern elements is carried out by a method (A) comprising: a step (a 1 ) of forming transparent conductive pattern elements on a transparent substrate according to a given pattern formation means, and a step (a 2 ) of forming light-shielding inorganic film pattern elements on the transparent conductive pattern elements formed in the step (a 1 ), according to a given film formation means.

Claim 4

A process according to claim 1, wherein the step (I) of forming on one side of a transparent substrate transparent conductive pattern elements having thereon light-shielding inorganic film pattern elements is carried out by a method (B) comprising: a step (b 1 ) of forming a transparent conductive film on a transparent substrate, forming on the transparent conductive film a light-shielding inorganic film which is resistant to an etching to be conducted later for the transparent conductive film, and forming a resist film on the light-shielding inorganic film, and a step (b 2 ) of subjecting the resist film formed in the step (b 1 ) to selective light exposure and development to form a resist pattern, etching the light-shielding inorganic film using the resist pattern as a mask according to an appropriate etching means to form light-shielding inorganic film pattern elements, and etching the transparent conductive film using the light-shielding inorganic film pattern elements as a mask according to an appropriate etching means to form transparent conductive pattern elements.

Claim 5

A process according to claim 1, wherein the transparent conductive pattern elements consist of pixels and lead elements, said pixels forming triangular patterns or mosaic patterns and in the step (I) the light-shielding inorganic film pattern elements are formed substantially on only the pixels of the transparent conductive pattern elements.

Claim 6

A process according to claim 4, wherein the formation of the light-shielding inorganic film pattern elements on the pixels of the transparent conductive pattern elements is carried out by a method (C) comprising: a step (c 1 ) of forming on a transparent substrate transparent conductive pattern elements consisting of pixels and lead elements according to a given pattern formation means, a step (c 2 ) of forming a resist film on the transparent substrate having thereon the transparent conductive pattern elements, obtained in the step (c 1 ) and then subjecting the resist film to selective light exposure and development to form a resist pattern on the substrate portion including the lead elements but excluding the pixels, and a step (c 3 ) of forming light-shielding inorganic film pattern elements on the pixels surrounded by the resist pattern formed in the step (c 2 ), according to a given film formation means.

Claim 7

A process according to claim 4, wherein the formation of light-shielding inorganic film pattern elements on the pixels of the transparent conductive pattern elements is carried out by a method (D) comprising: a step (d 1 ) of forming a transparent conductive film on a transparent substrate, forming on the transparent conductive film a light-shielding inorganic film which is resistant to an etching to be conducted later for the transparent conductive film, and forming a resist film on the light-shielding inorganic film, a step (d 2 ) of subjecting the resist film formed in the step (d 1 ) to selective light exposure and development to form a resist pattern, etching the light-shielding inorganic film using the resist pattern as a mask according to an appropriate etching means to form light-shielding inorganic film pattern elements, and etching the transparent conductive film using the light-shielding inorganic film pattern elements as a mask according to an appropriate etching means to form transparent conductive pattern elements consisting of pixels and lead elements, and a step (d 3 ) of forming a resist film on the transparent substrate having thereon the transparent conductive pattern elements having thereon the light-shielding inorganic film pattern elements, obtained in the step (d 2 ), subjecting the resist film to selective light exposure and development to form a resist pattern on the substrate portion excluding the lead elements having thereon respective light-shielding inorganic film pattern elements, and then removing the exposed light-shielding inorganic film pattern elements on the lead elements and the resist pattern in this order.

Claim 8

A process for producing a surface-colored material comprising transparent conductive pattern elements separated by a light-shielding insulating film on a transparent substrate, as well as colored layer elements on the transparent conductive pattern elements, which process comprising carrying out the following steps in the following order: (I) a step of forming on one side of a transparent substrate transparent conductive pattern elements having thereon light-shielding inorganic film pattern elements, (II) a step of coating a pigment- and/or dye-containing curable resin on the same side of the transparent substrate, (III) a step of applying a light to the other side (the back side) of the transparent substrate to selectively cure the portion of the curable resin by using the light-shielding inorganic film pattern elements as a mask, (IV) a step of removing the uncured portion of the curable resin to form a light-shielding insulating film consisting of a colored cured resin, (V) a step of peeling the light-shielding inorganic film pattern elements on the transparent conductive pattern elements, and (VI) a step of forming colored layer elements on the transparent conductive pattern elements.

Claim 9

A process for producing a surface-colored material comprising transparent conductive pattern elements separated by a light-shielding insulating film on a transparent substrate, as well as colored layer elements on the transparent conductive pattern elements, which process comprising carrying out the following steps in the following order: (I) a step of forming on one side of a transparent substrate transparent conductive pattern elements having thereon light-shielding inorganic film pattern elements, (II) a step of coating a pigment- and/or dye-containing curable resin on the same side of the transparent substrate, (III) a step of applying a light to the other side (the back side) of the transparent substrate to selectively cure the portion of the curable resin by using the light-shielding inorganic film pattern elements as a mask, (IV) a step of removing the uncured portion of the curable resin to form a light-shielding insulating film consisting of a colored cured resin, (V) a step of peeling the light-shielding inorganic film pattern elements on the transparent conductive pattern elements, and (VI) a step of forming colored layer elements on the transparent conductive pattern elements.

Claim 10

A process according to claim 7, wherein the step (I) of forming on one side of a transparent substrate transparent conductive pattern elements having thereon light-shielding inorganic film pattern elements is carried out by a method (A) comprising: a step (a 1 ) of forming transparent conductive pattern elements on a transparent substrate according to a given pattern formation means, and a step (a 2 ) of forming light-shielding inorganic film pattern elements on the transparent conductive pattern elements formed in the step (a 1 ), according to a given film formation means.

Claim 11

A process according to claim 7, wherein the step (I) of forming on one side of a transparent substrate transparent conductive pattern elements having thereon light-shielding inorganic film pattern elements is carried out by a method (B) comprising: a step (b 1 ) of forming a transparent conductive film on a transparent substrate, forming on the transparent conductive film a light-shielding inorganic film which is resistant to an etching to be conducted later for the transparent conductive film, and forming a resist film on the light-shielding inorganic film, and a step (b 2 ) of subjecting the resist film formed in the step (b 1 ) to selective light exposure and development to form a resist pattern, etching the light-shielding inorganic film using the resist pattern as a mask according to an appropriate etching means to form light-shielding inorganic film pattern elements, and etching the transparent conductive film using the light-shielding inorganic film pattern elements as a mask according to an appropriate etching means to form transparent conductive pattern elements.

Claim 12

A process according to claim 7, wherein the transparent conductive pattern elements consist of pixels and lead elements, said pixels forming triangular patterns or mosaic patterns and in the step (I) the light-shielding inorganic film pattern elements are formed substantially on only the pixels of the transparent conductive pattern elements.

Claim 13

A process according to claim 10, wherein the formation of the light-shielding inorganic film pattern elements on the pixels of the transparent conductive pattern elements is carried out by a method (C) comprising: a step (c 1 ) of forming on a transparent substrate transparent conductive pattern elements consisting of pixels and lead elements according to a given pattern formation means, a step (c 2 ) of forming a resist film on the transparent substrate having thereon the transparent conductive pattern elements, obtained in the step (c 1 ) and then subjecting the resist film to selective light exposure and development to form a resist pattern on the substrate including the lead elements but excluding the pixels, and a step (c 3 ) of forming light-shielding inorganic film pattern elements on the pixels surrounded by the resist pattern formed in the step (c 2 ), according to a given film formation means.

Claim 14

A process according to claim 10, wherein the formation of light-shielding inorganic film pattern elements on the pixels of the transparent conductive pattern elements is carried out by a method (D) comprising: a step (d 1 ) of forming a transparent conductive film on a transparent substrate, forming on the transparent conductive film a light-shielding inorganic film which is resistant to an etching to be conducted later for the transparent conductive film, and forming a resist film on the light-shielding inorganic film, a step (d 2 ) of subjecting the resist film formed in the step (d 1 ) to selective light exposure and development to form a resist pattern, etching the light-shielding inorganic film using the resist pattern as a mask according to an appropriate etching means to form light-shielding inorganic film pattern elements, and etching the transparent conductive film using the light-shielding inorganic film pattern elements as a mask according to an appropriate etching means to form transparent conductive pattern elements consisting of pixels and lead elements, and a step (d 3 ) of forming a resist film on the transparent substrate having thereon the transparent conductive pattern elements having thereon the light-shielding inorganic film pattern elements, obtained in the step (d 2 ), subjecting the resist film to selective light exposure and development to form a resist pattern on the substrate portion excluding the lead elements having thereon respective light-shielding film pattern elements, and then removing the exposed light-shielding inorganic film pattern elements on the lead elements and the resist pattern in this order.

Claim 15

A process according to claim 7, wherein the step (VI) of forming colored layer elements on the transparent conductive pattern elements is carried out by a polymer electrodeposition method.

Claim 16

A process according to claim 1, wherein the transparent conductive pattern elements are aligned on the transparent substrate in such a way that each of them has a stripe shape, and in step (I) the light-shielding inorganic film pattern elements are formed on substantially all the transparent conductive pattern elements.

Claim 17

A process according to claim 7, wherein the transparent conductive pattern elements are aligned on the transparent substrate in such a way that each of them has a stripe shape, and in step (I) the light-shielding inorganic film pattern elements are formed on substantially all of the transparent conductive pattern elements.