Thin film inorganic scintillator and method of making same
Assignee: GIMMEL GERALD K PERSONAL REPRESENTATIVE OF ESTATE OF JOSEPH LINDMAYER
•
Filing: 1988-06-30
•
Granted: 1990-07-10
•
Expires: 2008-06-30
Abstract
Abstract An article, having particular use as a scintillator, includes a thin film of calcium sulfide on a substrate, such as alumina, quartz, sapphire, or most glasses. The material is first formed in bulk with cerium sulfide, cerium oxide, or cerium, and lithium fluoride. The material is applied by physical vapor deposition in a relatively thin film to the substrate, and then at least the luminescent material is subjected to a high temperature for a period of time to effect recrystallization and activation of the material, such that the material acquires luminescent characteristics.
Inventors
- 👤 Peter K. Soltani
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 23:05
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/80; C04B41/81; C04B41/85; C03; C03C; C03C17/00; C03C17/22; C04B41/45; C04B41/50; C04B41/5007; C04B41/5014; C04B41/5053; C04B41/87; C09; C09K; C09K11/00; C09K11/08; C09K11/77; C09K11/7715; C09K11/7716; C09K11/7718; H; H01; H01J; H01J9/00; H01J9/20; H01J9/22; H01J9/221; C03C2217/00; C03C2217/20; C03C2217/28; C03C2217/287; C03C2217/29; C03C2218/00; C03C2218/10; C03C2218/15; C03C2218/151
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
88 words
A process for making a luminescent article, comprising the steps of: providing a substrate; depositing upon said substrate using thin film deposition techniques a material comprising a base material selected from the group consisting of alkaline earth metal sulfides and alkaline earth metal selenides, a dopant selected from the group of cerium and emporium, and a flux; and heating said material to a sufficient temperature for a sufficient period of time to affect recrystallization and activation of said material such that said material becomes a non-storage luminescent material.
Claim 2
Dependent Claim
88 words
A process for making a luminescent article, comprising the steps of: providing a substrate; depositing upon said substrate using thin film deposition techniques a material comprising a base material selected from the group consisting of alkaline earth metal sulfides and alkaline earth metal selenides, a dopant selected from the group of cerium and emporium, and a flux; and heating said material to a sufficient temperature for a sufficient period of time to affect recrystallization and activation of said material such that said material becomes a non-storage luminescent material.
Claim 3
Dependent Claim
25 words
A process as recited in claim 1, further comprising the step of providing an interlayer upon said substrate before said step of depositing said material.
Claim 4
Dependent Claim
23 words
A process as recited in claim 1, further comprising the step of providing an overcoat upon said material after said step of heating.
Claim 5
Dependent Claim
22 words
A process as recited in claim 1, wherein said temperature is in the range of about 400 to about 1200 degrees Centigrade.
Claim 6
Dependent Claim
21 words
A process as recited in claim 1, wherein said time is from a fraction of a second to about 5 minutes.
Claim 7
Dependent Claim
35 words
A process as recited in claim 1, wherein said article is a scintillator for detecting a particle having a predetermined stopping distance, said material is deposited to a thickness about equal to said stopping distance.
Claim 8
Dependent Claim
21 words
A process as recited in claim 1, wherein said material is deposited to a thickness of up to about 20 microns.
Claim 9
Dependent Claim
33 words
A process as recited in claim 1, wherein said dopant is cerium derived from a material selected from the group consisting of cerium oxide, cerium sulfide, cerium fluoride, cerium chloride and elemental cerium.
Claim 10
Dependent Claim
14 words
A process as recited in claim 1, wherein said base material comprises calcium sulfide.
Claim 11
Dependent Claim
33 words
A process as recited in claim 1, wherein said dopant is derived from cerium oxide provided in said material at a concentration of about 23 to about 23,000 parts per million by weight.
Claim 12
Dependent Claim
33 words
A process as recited in claim 1, wherein said dopant is derived from cerium sulfide provided in said material at a concentration of about 25 to about 25,000 parts per million by weight.
Claim 13
Dependent Claim
27 words
A process as recited in claim 1, wherein the dopant is cerium provided at a concentration of about 19 to about 19,000 parts per million by weight.
Claim 14
Dependent Claim
25 words
A process as recited in claim 1, wherein said flux is lithium fluoride and comprises from about 0.5 to about 10 percent of said material.
Claim 15
Dependent Claim
18 words
A process as recited in claim 1, wherein said heating step is performed subsequently to the depositing step.
Claim 16
Dependent Claim
18 words
A process as recited in claim 1, wherein said heating step is performed simultaneously with said depositing step.
References Cited (Backward Citations)
CA599073A
Cited
US31847A
Cited
US2527365A
Cited
US2468452A
Cited
US2468714A
Cited
US2522074A
Cited
US2521124A
Cited
US2523306A
Cited
US2485903A
Cited
US2979467A
Cited
US3347693A
Cited
US3700479A
Cited
USRE31847E
Cited
US3894164A
Cited
US4348299A
Cited
US4507562A
Cited
WO1985000089A1
Cited
US4857228A
Cited
US4806772A
Cited
US4812660A
Cited
US4812659A
Cited
US4822520A
Cited
US4830875A
Cited
US4725344A
Cited
US4877994A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-07-09 | 1994-01-08 | 1994-07-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-07-09 | 1998-01-08 | 1998-07-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-07-09 | 2002-01-08 | 2002-07-10 | $7700.00 | Window Closed / Lapsed |