Method of diffusing plurality of dopants simultaneously from vapor phase into semiconductor substrate
Assignee: Microsemi Semiconductor ULC
•
Filing: 1984-09-28
•
Granted: 1990-07-03
•
Expires: 2004-09-28
Abstract
Abstract This invention relates to the manufacture of semiconductor devices and more particularly to a method of diffusing an impurity layer into a substrate. The disclosed method comprises the steps of placing a body of semiconductor in a vacuum doping chamber, evacuating air from the chamber, subjecting the body to a dopant in the form of a gas or vapor while simultaneously heating the chamber to at least the diffusion temperature. The diffusion process is controlled by monitoring and controlling the pressure and the temperature of the dopant gas in the chamber. The diffusion method can also be carried out with the further admittance of a reactive gas or with the further admittance of a second dopant gas and a reactive gas together.
Inventors
- 👤 Laszlo Szolgyemy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 02:53
CPC Classifications
C; C30; C30B; C30B31/00; C30B31/06; H; H10; H10P; H10P32/00; H10P32/10; H10P32/12; H10P32/17; H10P32/171; Y; Y10; Y10S; Y10S438/00; Y10S438/935
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
201 words
A method of diffusing a plurality of impurities into a semiconductor substrate, comprising the steps of: (a) placing said substrate in a vacuum chamber, said substrate having a surface, (b) creating a vacuum in said chamber, (c) admitting a plurality of continuous flows of gas or vapor phase forms of different dopants in predetermined proportions into said chamber so as to simultaneously react with the surface of the substrate, (d) controlling a plurality of flows so as to maintain a predetermined pressure of the flows against said surface of said substrate, and (e) heating said substrate to a predetermined temperature for a predetermined length of time sufficient to initiate one or a plurality of reactions between respective ones of the dopants and said semiconductor surface, so that predetermined amounts of respective ones of the dopants diffuse into said substrate to a depth which is proportional to said temperature and time and in accordance with respective dopant concentrations which are proportional to said predetermined proportions and said pressure, whereby said controlling so as to maintain a predetermined pressure and said heating to a predetermined temperature for a predetermined time enables various dopant densities and dopant distributions in said substrate to be achieved.
Claim 2
Independent Claim
201 words
A method of diffusing a plurality of impurities into a semiconductor substrate, comprising the steps of: (a) placing said substrate in a vacuum chamber, said substrate having a surface, (b) creating a vacuum in said chamber, (c) admitting a plurality of continuous flows of gas or vapor phase forms of different dopants in predetermined proportions into said chamber so as to simultaneously react with the surface of the substrate, (d) controlling a plurality of flows so as to maintain a predetermined pressure of the flows against said surface of said substrate, and (e) heating said substrate to a predetermined temperature for a predetermined length of time sufficient to initiate one or a plurality of reactions between respective ones of the dopants and said semiconductor surface, so that predetermined amounts of respective ones of the dopants diffuse into said substrate to a depth which is proportional to said temperature and time and in accordance with respective dopant concentrations which are proportional to said predetermined proportions and said pressure, whereby said controlling so as to maintain a predetermined pressure and said heating to a predetermined temperature for a predetermined time enables various dopant densities and dopant distributions in said substrate to be achieved.
Claim 3
Dependent Claim
36 words
A method as defined in claim 1 wherein the semiconductor substrate is comprised of silicon, one dopant is comprised of phosphine, the predetermined temperature is approximately 700°-1200° C. and the predetermined pressure is approximately 400 mTorr.
Claim 4
Dependent Claim
23 words
A method as defined in claim 1 wherein the semiconductor substrate is comprised of germanium and the predetermined temperature is approximately 500-900° C.
Claim 5
Independent Claim
250 words
A method of diffusing a plurality of impurities into a semiconductor substrate, comprising the steps of: (a) placing said substrate in a vacuum chamber, said substrate having a surface, (b) creating a vacuum in said chamber, (c) admitting a plurality of continuous flows of gas or vapor phase forms of different dopant compounds into said chamber so as to simultaneously react with the surface of the substrate, (d) admitting a continuous flow of a reactive gas into said chamber, (e) controlling said continuous flows of dopant compounds and reactive gas so as to maintain a predetermined pressure of the flows against said surface of said substrate, and (f) heating said substrate to a predetermined temperature for a predetermined length of time, so that respective ones of the dopant compounds react with the reactive gas to produce respective ones of elementary dopants, or intermediate compounds which react with said surface of the substrate to produce the elementary dopants, said temperature being sufficient to initiate one or a plurality of reactions between respective ones of the elementary dopants and said surface such that a predetermined amount of respective ones of the elementary dopants diffuse into said substrate to a depth which is proportional to said temperature and time and in accordance with respective dopant concentrations which are proportional to said predetermined proportions and said pressure, whereby said controlling so as to maintain a predetermined temperature for a predetermined time enables various dopant densities and dopant distribution in said substrate to be achieved.
Claim 6
Independent Claim
250 words
A method of diffusing a plurality of impurities into a semiconductor substrate, comprising the steps of: (a) placing said substrate in a vacuum chamber, said substrate having a surface, (b) creating a vacuum in said chamber, (c) admitting a plurality of continuous flows of gas or vapor phase forms of different dopant compounds into said chamber so as to simultaneously react with the surface of the substrate, (d) admitting a continuous flow of a reactive gas into said chamber, (e) controlling said continuous flows of dopant compounds and reactive gas so as to maintain a predetermined pressure of the flows against said surface of said substrate, and (f) heating said substrate to a predetermined temperature for a predetermined length of time, so that respective ones of the dopant compounds react with the reactive gas to produce respective ones of elementary dopants, or intermediate compounds which react with said surface of the substrate to produce the elementary dopants, said temperature being sufficient to initiate one or a plurality of reactions between respective ones of the elementary dopants and said surface such that a predetermined amount of respective ones of the elementary dopants diffuse into said substrate to a depth which is proportional to said temperature and time and in accordance with respective dopant concentrations which are proportional to said predetermined proportions and said pressure, whereby said controlling so as to maintain a predetermined temperature for a predetermined time enables various dopant densities and dopant distribution in said substrate to be achieved.
Claim 7
Dependent Claim
68 words
A method as defined in claim 4 wherein said semiconductor substrate is comprised of silicon, one dopant is comprised of phosphine, said flow of phosphine is approximately 10 ml/min., said reactive gas is oxygen, said flow of oxygen is approximately 40 ml/min., said predetermined temperature is approximately 800° C., said time is about one hour, said pressure is approximately 400 mTorr., and an intermediate compound is phosphorous pentoxide.
Claim 8
Dependent Claim
104 words
A method as defined in claim 4 wherein said semiconductor substrate is comprised of silicon, said plurality of continuous flows are admitted into said chamber so as to provide a plurality of dopants, said plurality of dopants being comprised of arsenic trichloride and phosphorous oxychloride, said flow of arsenic trichloride is approximately 15 ml/min., said flow of phosphorous oxychloride is approximately 15 ml/min., said reactive gas is oxygen, said flow of oxygen is approximately 50 ml/min., said predetermined temperature is approximately 900° C., said time is 20 minutes, said intermediate compounds are phosphorous pentoxide and arsenic trioxide, and said depth is approximately 0.3 micrometers.
Claim 9
Dependent Claim
29 words
A method as defined in claim 4 wherein said semiconductor body is comprised of gallium arsenide, one dopant is comprised of diethylzinc, and said temperature is approximately 400-700° C.
References Cited (Backward Citations)
US3492175A
Cited
US3829382A
Cited
US3916034A
Cited
US3764414A
Cited
US3949119A
Cited
US3948696A
Cited
US4204893A
Cited
US4233093A
Cited
US4526632A
Cited
US4525224A
Cited
US4618381A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-07-02 | 1994-01-01 | 1994-07-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-07-02 | 1998-01-01 | 1998-07-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-07-02 | 2002-01-01 | 2002-07-03 | $7700.00 | Window Closed / Lapsed |