Method of forming thin film by chemical vapor deposition
Assignee: Toshiba Corp
•
Filing: 1989-05-30
•
Granted: 1990-05-08
•
Expires: 2009-05-30
Abstract
Abstract A method for the formation of a thin, high melting-point metal film such as W, on a substrate surface, by means of CVD, is disclosed herein. In this method, the inner wall of the CVD reaction tube and the surface of the at least part of the fittings disposed therewithin are covered with a metal nitride film, in the process of performing the CVD operation. The method permits the formation of a high quality film, and also prevents the deposition of the high melting-point metal on the inner wall of the reaction chamber, even if the CVD operation is repeatedly performed over a long period of time.
Inventors
- 👤 Tetsuo Matsuda
- 👤 Iwao Kunishima
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 16:14
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/34; C23C16/44; C23C16/4401; C23C16/4404; C23C8/00; C23C8/06; C23C8/08; C23C8/24
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
140 words
A method of forming, by means of CVD (Chemical Vapor Deposition), a thin film of high melting-point metal selected from the group consisting of Ti, W, Mo and Ta, comprising the steps of: (a) forming a metal film of the high melting-point metal on the surface of the inner wall of a quartz CVD reaction tube and on at least a part of the fittings disposed therein; (b) forming a nitride film of the high melting-point metal on the metal film formed in step (a), by nitriding the surface of the metal film, said nitriding being carried out by heat-treatment in an atmosphere containing ammonia; (c) forming, by carrying out the CVD, the thin film of the high melting-point metal on a surface of a substrate situated in the CVD reaction tube from a fluoride of the high melting-point metal.
Claim 2
Independent Claim
140 words
A method of forming, by means of CVD (Chemical Vapor Deposition), a thin film of high melting-point metal selected from the group consisting of Ti, W, Mo and Ta, comprising the steps of: (a) forming a metal film of the high melting-point metal on the surface of the inner wall of a quartz CVD reaction tube and on at least a part of the fittings disposed therein; (b) forming a nitride film of the high melting-point metal on the metal film formed in step (a), by nitriding the surface of the metal film, said nitriding being carried out by heat-treatment in an atmosphere containing ammonia; (c) forming, by carrying out the CVD, the thin film of the high melting-point metal on a surface of a substrate situated in the CVD reaction tube from a fluoride of the high melting-point metal.
Claim 3
Dependent Claim
32 words
A method according to claim 1, wherein the fittings disposed within the reaction tube comprise a quartz boat for supporting the substrate, a supporting rod for the boat, and a heat baffle.
Claim 4
Dependent Claim
44 words
A method according to claim 1, wherein the substrate is an electrically conductive substrate having an insulation pattern formed thereon, and the high melting-point metal film is selectively formed on the conductive surface of the substrate which is not covered with the insulation pattern.
Claim 5
Dependent Claim
40 words
A method according to claim 1, wherein step (b) is repeated after step (c), with the substrate, on which the thin film of the high melting-point metal has been formed in step (c), being left in the CVD reaction tube.
Claim 6
Dependent Claim
50 words
A method according to claim 4, wherein the thin film of the high melting-point metal is formed selectively on said substrate within a contact hole therein step (c), and the nitride film of the high melting-point metal is formed selectively on the surface of the thin film in step (b).
Claim 7
Dependent Claim
29 words
A method according to claim 1, wherein the nitride film comprises a nitride of the high melting-point metal, whose stoichiometric molar ratio between the metal and nitrogen is indefinite.
Claim 8
Dependent Claim
29 words
A method according to claim 1, wherein the high melting-point metal of the metal film in step (a) is identical with that of the thin film in step (c).
Claim 9
Dependent Claim
17 words
A method according to claim 1, wherein the nitriding is conducted at the temperature of 350-1000° C.
Claim 10
Independent Claim
134 words
A method of forming, by means of CVD (Chemical Vapor Deposition), a thin film of high melting-point metal selected from the group consisting of Ti, W, Mo and Ta, comprising the steps of: (a) forming a metal film of the high melting-point metal on the surface of the inner wall of a quartz CVD reaction tube and on at least a part of the fittings disposed therein; (b) forming a nitride film of the high melting-point metal on the metal film formed in step (a), by carrying out the CVD using fluoride of the high melting-point metal and ammonia; (c) forming, by carrying out the CVD, the thin film of the high melting-point metal on a surface of a substrate situated in the CVD reaction tube from a fluoride of the high melting-point metal.
Claim 11
Independent Claim
134 words
A method of forming, by means of CVD (Chemical Vapor Deposition), a thin film of high melting-point metal selected from the group consisting of Ti, W, Mo and Ta, comprising the steps of: (a) forming a metal film of the high melting-point metal on the surface of the inner wall of a quartz CVD reaction tube and on at least a part of the fittings disposed therein; (b) forming a nitride film of the high melting-point metal on the metal film formed in step (a), by carrying out the CVD using fluoride of the high melting-point metal and ammonia; (c) forming, by carrying out the CVD, the thin film of the high melting-point metal on a surface of a substrate situated in the CVD reaction tube from a fluoride of the high melting-point metal.
Claim 12
Dependent Claim
32 words
A method according to claim 9, wherein the fittings disposed within the reaction tube comprise a quartz boat for supporting the substrate, a supporting rod for the boat, and a heat baffle.
Claim 13
Dependent Claim
44 words
A method according to claim 9, wherein the substrate is an electrically conductive substrate having an insulating pattern formed thereon, and the high melting-point metal film is selectively formed on the conductive surface of the substrate which is not covered with the insulation pattern.
Claim 14
Dependent Claim
40 words
A method according to claim 9, wherein step (b) is repeated after step (c), with the substrate, on which the thin film of the high melting-point metal has been formed in step (c), being left in the CVD reaction tube.
Claim 15
Dependent Claim
50 words
A method according to claim 12, wherein the thin film of the high melting-point metal is formed selectively within a contact hole of the substrate in step (c), and the nitride film of the high melting-point metal is formed selectively on the surface of the thin film in step (b).
Claim 16
Dependent Claim
29 words
A method according to claim 9, wherein the nitride film comprises a nitride of the high melting-point metal, whose stoichiometric molar ratio between the metal and nitrogen is indefinite.
Claim 17
Dependent Claim
29 words
A method according to claim 9, wherein the high melting-point metal of the metal film in step (a) is identical with that of the thin film in step (c).
Claim 18
Dependent Claim
21 words
A method according to claim 9, wherein the fluoride of the high melting-point metal used in step (b) is tungsten fluoride.
Claim 19
Independent Claim
86 words
A method of forming, by means of CVD (Chemical Vapor Deposition) in a quartz CVD reaction tube, a thin film of high melting-point metal selected from the group consisting of Ti, W, Mo and Ta, on a surface of a substrate situated within the CVD reaction tube, wherein the CVD is performed after a nitride film of the high melting-point metal is formed on the surface of the inner wall of the CVD reaction tube and on at least a part of the fittings disposed therein.
Claim 20
Independent Claim
86 words
A method of forming, by means of CVD (Chemical Vapor Deposition) in a quartz CVD reaction tube, a thin film of high melting-point metal selected from the group consisting of Ti, W, Mo and Ta, on a surface of a substrate situated within the CVD reaction tube, wherein the CVD is performed after a nitride film of the high melting-point metal is formed on the surface of the inner wall of the CVD reaction tube and on at least a part of the fittings disposed therein.
References Cited (Backward Citations)
US3031338A
Cited
US3178308A
Cited
US3746569A
Cited
US4123989A
Cited
EP0134645A1
Cited
US4650698A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-07 | 1993-11-06 | 1994-05-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-07 | 1997-11-06 | 1998-05-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-07 | 2001-11-06 | 2002-05-08 | $7700.00 | Window Closed / Lapsed |