US4910164A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making planarized heterostructures using selective epitaxial growth
Assignee: Texas Instruments Inc
•
Filing: 1988-07-27
•
Granted: 1990-03-20
•
Expires: 2008-07-27
Abstract
Abstract A lift-off method for forming regions of a first semiconductor such as GaAs (104) in recesses in a substrate of a second semiconductor such as silicon (102) with the surface of the first semiconductor region (104) coplanar with the surface of the second semiconductor layer (102). Also, interconnected devices in both regions. Preferred embodiment methods include growth by molecular beam epitaxy of a layer of the first semiconductor on a masked and recessed substrate of the second semiconductor followed by photolithographic removal of the grown layer outside of a neighborhood of the recesses and lift-off (by mask etching) of the remainder of the grown layer outside of the recesses.
Inventors
- 👤 Hisashi Shichijo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 04:31
CPC Classifications
H; H10; H10P; H10P10/00; H10P14/00; H10P14/20; H10P14/38; H10P14/27; H10P14/29; H10P14/2901; H10P14/2902; H10P14/2905; H10P14/2924; H10P14/2925; H10P14/34; H10P14/3402; H10P14/3414; H10P14/3421; Y; Y10; Y10S; Y10S148/00; Y10S148/026; Y10S148/072; Y10S148/10; Y10S438/00; Y10S438/933; Y10S438/942; Y10S438/948; Y10S438/951
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
99 words
A method of heteroepitaxial semiconductor fabrication, comprising the steps of: (a) form at least one masked recess in a first layer of a first semiconductor material; (b) deposit a second layer of a second semiconductor material different from said first semiconductor material on said masked, recessed first layer, said second layer of thickness approximately equal to the depth of said recess(es); (c) remove said second layer except over said recess(es) plus adjacent regions at most five microns away; and (d) remove said mask and thereby lift-off substantially all of the remainder of said second layer outside of said recess(es).
Claim 2
Independent Claim
99 words
A method of heteroepitaxial semiconductor fabrication, comprising the steps of: (a) form at least one masked recess in a first layer of a first semiconductor material; (b) deposit a second layer of a second semiconductor material different from said first semiconductor material on said masked, recessed first layer, said second layer of thickness approximately equal to the depth of said recess(es); (c) remove said second layer except over said recess(es) plus adjacent regions at most five microns away; and (d) remove said mask and thereby lift-off substantially all of the remainder of said second layer outside of said recess(es).
Claim 3
Dependent Claim
33 words
The method of claim 1, further comprising the step of: (a) apply vibrations to the product of step (d) and thereby remove any remaining portions of said second layer outside of said recess(es).
Claim 4
Dependent Claim
40 words
The method of claim 1, wherein: (a) said first semiconductor material is silicon; and (b) said second semiconductor material is In x Al y Ga 1-x-y As for various nonnegative x, y values in the range of 0 23 ×+y≦1.0.
Claim 5
Dependent Claim
36 words
The method of claim 1, wherein: (a) said first semiconductor material is silicon; (b) said second semiconductor material is GaAs; (c) said mask is silicon dioxide; and (d) said removal in step (c) is by photolithography.
Claim 6
Independent Claim
135 words
A method of heteroepitaxial semiconductor fabrication, comprising the steps of: (a) form at least one masked recess in a first layer of a first semiconductor material; (b) deposit a second layer of a second semiconductor material different from said first semiconductor material on said masked, recessed first layer, said second layer of thickness approximately equal to the depth of said recess(es); (c) remove said second layer except over said recess(es) plus adjacent regions at most five microns away.; (d) remove said mask; (e) form a planar layer on said first layer plus the remainder of said second layer with the portions of said remainder projecting above the plane of said first layer also projecting through said planar layer; (f) remove said portions using said planar layer as a mask; and (g) remove said planar layer.
Claim 7
Independent Claim
135 words
A method of heteroepitaxial semiconductor fabrication, comprising the steps of: (a) form at least one masked recess in a first layer of a first semiconductor material; (b) deposit a second layer of a second semiconductor material different from said first semiconductor material on said masked, recessed first layer, said second layer of thickness approximately equal to the depth of said recess(es); (c) remove said second layer except over said recess(es) plus adjacent regions at most five microns away.; (d) remove said mask; (e) form a planar layer on said first layer plus the remainder of said second layer with the portions of said remainder projecting above the plane of said first layer also projecting through said planar layer; (f) remove said portions using said planar layer as a mask; and (g) remove said planar layer.
Claim 8
Dependent Claim
26 words
The method of claim 5, further comprising the step of: (a) apply vibrations to the product of step (d) prior to formation of said planar layer.
Claim 9
Dependent Claim
38 words
The method of claim 5, wherein: (a) said first semiconductor material is silicon; and (b) said second semiconductor material is In x Al y Ga 1-x-y As for various nonnegative x, y values in the range of 0≦×+y≦1.0.
Claim 10
Dependent Claim
42 words
The method of claim 5, wherein: (a) said first semiconductor material is silicon; (b) said second semiconductor material is GaAs; (c) said mask is silicon dioxide; (d) said planar layer is photoresist; and (e) said removal in step (c) is by photolithography.
Claim 11
Dependent Claim
24 words
The method of claim 5, wherein: (a) said formation in step (e) is by spinning on photoresist followed by etchback to expose said portions.
Claim 12
Independent Claim
138 words
A method of heteroepitaxial fabrication of an integrated circuit, comprising the steps of: (a) form devices in a first layer of a first semiconductor material; (b) form at least one masked recess in said first layer; (c) deposit a second layer of a second semiconductor material different from said first semiconductor material on said masked, recessed first layer, said second layer of thickness approximately equal to the depth of said recess(es); (d) remove said second layer except over said recess(es) plus adjacent regions at most five microns away; (e) remove said mask; (f) form devices in said second layer part over said recess(es); (g) form electrodes for and interconnections among said devices in said first layer and in said second layer part; and (h) package said first layer and second layer part plus devices and electrodes and interconnections.
Claim 13
Independent Claim
138 words
A method of heteroepitaxial fabrication of an integrated circuit, comprising the steps of: (a) form devices in a first layer of a first semiconductor material; (b) form at least one masked recess in said first layer; (c) deposit a second layer of a second semiconductor material different from said first semiconductor material on said masked, recessed first layer, said second layer of thickness approximately equal to the depth of said recess(es); (d) remove said second layer except over said recess(es) plus adjacent regions at most five microns away; (e) remove said mask; (f) form devices in said second layer part over said recess(es); (g) form electrodes for and interconnections among said devices in said first layer and in said second layer part; and (h) package said first layer and second layer part plus devices and electrodes and interconnections.
Claim 14
Dependent Claim
66 words
The method of claim 10, comprising the further steps of: (a) after step (e) form a planar layer on said first layer plus the remainder of said second layer with the portions of said remainder projecting above the plane of said first layer also projecting through said planar layer; (b) remove said portions using said planar layer as a mask; and (c) remove said planar layer.
Claim 15
Dependent Claim
26 words
The method of claim 11, further comprising the step of: (a) apply vibrations to the product of step (e) prior to formation of said planar layer.
Claim 16
Dependent Claim
38 words
The method of claim 10, wherein: (a) said first semiconductor material is silicon; and (b) said second semiconductor material is In x Al y Ga 1-x-y As for various nonnegative x, y values in the range of 0≦×+y≦1.0.
Claim 17
Dependent Claim
42 words
The method of claim 11, wherein: (a) said first semiconductor material is silicon; (b) said second semiconductor material is GaAs; (c) said mask is silicon dioxide; (d) said planar layer is photoresist; and (e) said removal in step (d) is by photolithography.
Claim 18
Dependent Claim
24 words
The method of claim 10, wherein: (a) said formation in step (e) is by spinning on photoresist followed by etchback to expose said portions.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-19 | 1993-09-18 | 1994-03-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-19 | 1997-09-18 | 1998-03-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-19 | 2001-09-18 | 2002-03-20 | $7700.00 | Window Closed / Lapsed |