Manufacture of monolithic infrared focal plane arrays
Assignee: Lockheed Martin Tactical Systems Inc
•
Filing: 1988-12-23
•
Granted: 1990-03-20
•
Expires: 2008-12-23
Abstract
Abstract The manufacture of monolithic HgCdTe detectors and Si circuitry in an IR focal plane array is achieved by forming a protective layer of SiO 2 or SiN x on a silicon wafer containing silicon circuits, etching steep-wall recesses into the wafer, selectively depositing epitaxial single-crystal layers of GaAs, CdTe, and HgCdTe in the recesses fabricating HgCdTe IR arrays, and depositing appropriate insulating and conductive interconnection patterns to interconnect the Si devices with one another and the HgCdTe devices with the Si devices. Little or no GaAs, CdTe, and HgCdTe grows on the SiO 2 or SiN x outside the recesses. Since material grown outside the recess is polycrystalline, it is easily chemomechanically removed.
Inventors
- 👤 Ken Zanio
- 👤 Ross C. Bean
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 00:51
CPC Classifications
H; H10; H10F; H10F39/00; H10F39/10; H10F39/12; H10F39/18; H10F39/184; H10F39/1843; Y; Y10; Y10S; Y10S148/00; Y10S148/064
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
50 words
A method of making monolithic HgCdTe infrared detectors on silicon substrates, comprising the steps of: (a) providing a silicon substrate; (b) growing on said substrate a layer of GaAs; (c) growing on said GaAs layer a layer of CdTe; and (d) growing on said CdTe layer a layer of HgCdTe.
Claim 2
Independent Claim
50 words
A method of making monolithic HgCdTe infrared detectors on silicon substrates, comprising the steps of: (a) providing a silicon substrate; (b) growing on said substrate a layer of GaAs; (c) growing on said GaAs layer a layer of CdTe; and (d) growing on said CdTe layer a layer of HgCdTe.
Claim 3
Independent Claim
154 words
A method of making interconnected monolithic IR detector HgCdTe FPAs on Si substrates containing Si circuits, comprising the steps of: (a) providing a silicon substrate; (b) forming silicon signal processing circuitry on said substrate; (c) forming on the surface of said substrate a protective layer of a material taken from the group consisting of SiO 2 and SiN x ; substrate material; (d) forming in said substrate a recess exposing the substrate material; (e) selectively growing in said recess a thin monocrystalline layer of GaAs; (f) growing in said recess on said GaAs layer a thin monocrystalline layer of CdTe; (g) selectively growing in said recess on said CdTe layer a monocrystalline layer of HgCdTe sufficiently thick to substantially fill said recess; (h) depositing a pattern of insulating material over said HgCdTe layer and said substrate surface; and (i) depositing a pattern of metallic interconnecting material over said HgCdTe layer and said substrate surface.
Claim 4
Independent Claim
154 words
A method of making interconnected monolithic IR detector HgCdTe FPAs on Si substrates containing Si circuits, comprising the steps of: (a) providing a silicon substrate; (b) forming silicon signal processing circuitry on said substrate; (c) forming on the surface of said substrate a protective layer of a material taken from the group consisting of SiO 2 and SiN x ; substrate material; (d) forming in said substrate a recess exposing the substrate material; (e) selectively growing in said recess a thin monocrystalline layer of GaAs; (f) growing in said recess on said GaAs layer a thin monocrystalline layer of CdTe; (g) selectively growing in said recess on said CdTe layer a monocrystalline layer of HgCdTe sufficiently thick to substantially fill said recess; (h) depositing a pattern of insulating material over said HgCdTe layer and said substrate surface; and (i) depositing a pattern of metallic interconnecting material over said HgCdTe layer and said substrate surface.
Claim 5
Dependent Claim
17 words
The method of claim 2, in which the growth of said GaAs, CdTe and HgCdTe is epitaxial.
Claim 6
Dependent Claim
31 words
The method of claim 2, in which at least one of said growing steps includes removing any polycrystalline material which may have formed on said substrate surface during said growing step.
Claim 7
Dependent Claim
15 words
The method of claim 2, in which said recess is formed with substantially vertical sides.
Claim 8
Dependent Claim
37 words
The method of claim 2, in which said HgCdTe layer is deposited to a thickness beyond that necessary to fill said recess, and said HgCdTe layer is then chemomechanically polished to be level with said substrate surface.
References Cited (Backward Citations)
US3793712A
Cited
US3988774A
Cited
US4141765A
Cited
US4312115A
Cited
JPS5522866A
Cited
US4273596A
Cited
US4228365A
Cited
US4276099A
Cited
US4242149A
Cited
US4251299A
Cited
JPS5649581A
Cited
US4376663A
Cited
US4376659A
Cited
US4487813A
Cited
US4648917A
Cited
US4655848A
Cited
US4743310A
Cited
US4804638A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-19 | 1993-09-18 | 1994-03-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-19 | 1997-09-18 | 1998-03-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-19 | 2001-09-18 | 2002-03-20 | $7700.00 | Window Closed / Lapsed |