Process for treating copper surface

Claim 2

A process for treating a copper surface which comprises forming a copper oxide layer on a copper surface by treating with an aqueous solution containing an oxidizing agent, and treating the copper oxide layer with an aqueous aldehyde solution having a pH of 9.0 or higher to reduce the copper oxide, said treatment of the copper oxide layer being carried out (a) while applying a potential of -1000 mV to -400 mV in terms of Ag-AgCl electrode to the copper oxide layer, or (b) after contacting the copper oxide layer with a contacting piece made of copper or a metal nobler than copper, or (c) after contacting the copper oxide layer with an aqueous solution containing an alkali borohydride so as to make the potential of copper in the range of -1000 mV to -400 mV in terms of Ag-AgCl electrode.

Claim 3

A process according to claim 1, wherein the treatment of the copper oxide layer is carried out while applying a potential of -1000 mV to -400 mV in terms of Ag-AgCl electrode to the copper oxide layer.

Claim 4

A process according to claim 2, wherein the potential is applied by contacting with copper or a metal nobler than copper.

Claim 5

A process according to claim 1, wherein the treatment of the copper oxide layer is carried out after contacting the copper oxide layer with a contacting piece made of copper or a metal nobler than copper.

Claim 6

A process according to claim 4, wherein the contacting piece is made in the form of roll covered with a copper layer or a layer of a metal nobler than copper.

Claim 7

A process according to claim 1, wherein the treatment of the copper oxide layer is carried out after contacting the copper oxide layer with an aqueous solution containing an alkali borohydride so as to make the potential of copper in the range of -1000 mV to -400 mV in terms of Ag-AgCl electrode.

Claim 8

A process according to claim 6, wherein the alkali borohydride is sodium borohydride.

Claim 9

A copper-clad laminate obtained by subjecting one or both surfaces of copper foil to the surface treatment process of claim 1, laminating one or more of the surface treated copper foils and one or more sheets of glass cloth or paper impregnated with an epoxy resin, a phenol resin or a polyimide resin or one or more sheets of an epoxy resin, a phenol resin or a polyimide resin mixed with glass fibers, or laminating one or more of the thus surface treated copper foils coated with an epoxy resin, and subjecting the resulting multiple layers to heating and pressing treatment to form a laminated unit having copper layers on the outermost surfaces.

Claim 10

A copper-clad flexible film obtained by subjecting one or both surfaces of copper foil to the surface treatment process of claim 1, and bonding a flexible resin film to the resulting copper foil using an adhesive of epoxy resin or acrylic resin so as to have copper layers on the outermost surfaces.

Claim 11

A copper-clad flexible film according to claim 9, wherein the flexible resin film is made from polyimide, polyester, polytetrafluoroethylene, polysulfone, or polyether ether ketone.

Claim 12

A multi-layer wiring board obtained by laminating one or more copper foils and one or more sheets of glass cloth or paper impregnated with an epoxy resin, a phenol resin or a polyimide resin or one or more sheets of an epoxy resin, a phenol resin or a polyimide resin mixed with glass fibers, or laminating one or more copper foils coated with an epoxy resin, a phenol resin or a polyimide resin, subjecting the resulting multiple layers to heating and pressing treatment to form a copper-clad laminate, removing unnecessary portions from the copper foil of the laminate by etching to form a circuit pattern for an internal layer, subjecting the copper foil thus treated to the surface treatment process of claim 1, laminating on the resulting copper surface an epoxy resin, a phenol resin or a polyimide resin, or a glass cloth or paper impregnated with an epoxy resin, a phenol resin or a polyimide resin, or laminating a sheet of an epoxy resin, a phenol resin or a polyimide resin mixed with glass fibers, with repetition of laminating to form multiple layers and a copper foil as an outermost layer, subjecting the multiple layers and copper foil to heating and pressing treatment to form a laminated unit having copper layers on the outermost surfaces, drilling through-holes in the laminated unit, metallizing inner walls of the through-holes, and removing unnecessary portions from the outermost copper layers by etching to form circuits.

Claim 13

A multi-layer wiring board obtained by laminating one or more copper foils and one or more sheets of glass cloth or paper impregnated with an epoxy resin, a phenol resin or a polyimide resin or one or more sheets of an epoxy resin, a phenol resin or a polyimide resin mixed with glass fibers, or laminating one or more copper foils coated with an epoxy resin, a phenol resin or a polyimide resin, subjecting the resulting multiple layers to heating and pressing treatment to form a copper-clad laminate, removing unnecessary portions from the copper foil of the laminate by etching to form a circuit pattern for an inner layer, subjecting the copper foil thus treated to the surface treatment process of claim 1, laminating on the resulting copper surface an epoxy resin, a phenol resin or a polyimide resin, or a glass cloth or paper impregnated with an epoxy resin, a phenol resin or a polyimide resin, or laminating a sheet of an epoxy resin, a phenol resin or a polyimide resin mixed with glass fibers, with repetition of laminating to form multiple layers and a copper foil subjected to the surface treatment process of claim 1 as an outermost layer, subjecting the multiple layers and copper foil to heating and pressing treatment to form a laminated unit having copper layers on the outermost surfaces, drilling through-holes in the laminated unit, metallizing inner walls of the through-holes, and removing unnecessary portions from the outermost copper layers by etching to form circuits.

Claim 14

A flexible wiring board obtained by bonding a copper foil to a flexible resin film using an adhesive of epoxy resin or acrylic resin to form a copper-clad flexible film, removing unnecessary portions from the copper foil by etching to form a circuit pattern for an inner layer, subjecting the copper foil thus treated to the surface treatment process of claim 1, and bonding a flexible resin film from which necessary portions for connection are removed to the thus treated copper surface with an adhesive of epoxy resin or acrylic resin.

Claim 15

A flexible wiring board according to claim 13, wherein the flexible resin film is made from polyimide, polyester, polytetrafluoroethylene, polysulfone, or polyether ether ketone.