Method of shaping hard difficult-to-roll alloys
Assignee: Vapor Technologies Inc
•
Filing: 1988-12-09
•
Granted: 1990-02-06
•
Expires: 2008-12-09
Abstract
Abstract Hard difficult-to-roll alloys are shaped by forming a mold of plastic, especially a polyacrylate, with a highly smooth surface onto which the alloy is deposited by low-temperature arc vapor deposition. The alloy layer is then separated from the plastic substrate and subjected to heat treatment to increase its density.
Inventors
- 👤 Eduard Pinkhasov
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 09:41
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/0005; C22; C22C; C22C1/00; C23C14/06; C23C14/14; C23C14/20; C23C14/22; C23C14/56; C23C14/564
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
138 words
A method of making objects from difficult-to-roll alloys, comprising the steps of: (a) depositing upon a synthetic resin substrate having a shape complementary to a shape to be imparted to a difficult-to-roll alloy, a layer of said alloy of approximately a final thickness of an object of said shape to be fabricated from said alloy, by striking an arc between electrodes at least one of which is constituted of at least one metal of said alloy in an evacuated space to form a vapor of the composition of said alloy and depositing said layer from said vapor on said substrate, whereby the composition of said layer is substantially true to the composition of said vapor; (b) removing said layer from said substrate; and (c) heat-treating the layer removed from said substrate to increase the density of said layer.
Claim 2
Independent Claim
138 words
A method of making objects from difficult-to-roll alloys, comprising the steps of: (a) depositing upon a synthetic resin substrate having a shape complementary to a shape to be imparted to a difficult-to-roll alloy, a layer of said alloy of approximately a final thickness of an object of said shape to be fabricated from said alloy, by striking an arc between electrodes at least one of which is constituted of at least one metal of said alloy in an evacuated space to form a vapor of the composition of said alloy and depositing said layer from said vapor on said substrate, whereby the composition of said layer is substantially true to the composition of said vapor; (b) removing said layer from said substrate; and (c) heat-treating the layer removed from said substrate to increase the density of said layer.
Claim 3
Dependent Claim
58 words
The method defined in claim 1 wherein said arc is struck by contacting one of said electrodes with the other electrode and applying a voltage of substantially 20 to 150 volts across said electrodes in a space evacuated to a pressure of at most 10 -3 torr and has an arc current of substantially 30 to 150 amperes.
Claim 4
Dependent Claim
15 words
The method defined in claim 2 wherein at least one of said electrodes contains titanium.
Claim 5
Dependent Claim
14 words
The method defined in claim 3 wherein the other of said electrodes contains aluminum.
Claim 6
Dependent Claim
19 words
The method defined in claim 2 wherein said one of said electrodes consists of the alloy TiAl 3 .
Claim 7
Dependent Claim
16 words
The method defined in claim 2 wherein said vapor consists of the alloy TiAl 3 .
Claim 8
Dependent Claim
15 words
The method defined in claim 2 wherein said thickness is substantially 0.005 to 0.1 inch.
Claim 9
Dependent Claim
15 words
The method defined in claim 7 wherein said thickness is substantially 0.005 to 0.01 inch.
Claim 10
Dependent Claim
33 words
The method defined in claim 2 wherein heat treatment is carried out in step (c) to a density of said layer which is at least 95% of the density of the solid alloy.
Claim 11
Dependent Claim
16 words
The method defined in claim 1 wherein said alloy is an alloy of titanium and aluminum.
Claim 12
Dependent Claim
13 words
The method defined in claim 10 wherein said alloy is TiAl 3 .
Claim 13
Dependent Claim
24 words
The method defined in claim 3, further comprising the step of reducing the oxygen content in ambient gas within said space during step (a).
Claim 14
Dependent Claim
34 words
The method defined in claim 12 wherein the oxygen content of the ambient gas is reduced by allowing said gas to contact a titanium layer forming a getter for oxygen in said ambient gas.
Claim 15
Dependent Claim
21 words
The method defined in claim 13 wherein said layer is vapor deposited by the striking of an arc between titanium electrodes.
Claim 16
Dependent Claim
29 words
The method defined in claim 14 wherein said titanium layer is deposited by striking an arc with one of the electrodes used in step (a) and constituted from titanium.
Claim 17
Dependent Claim
31 words
The method defined in claim 1, further comprising the step of reducing an oxygen content in said evacuated space by evacuating same to a pressure of at most 10 -7 torr.
Claim 18
Dependent Claim
26 words
The method defined in claim 16, further comprising the step of coating a surface in said evacuated space with titanium to form a getter for oxygen.
Claim 19
Dependent Claim
44 words
The method defined in claim 1, further comprising the step of reducing oxygen in said evacuated space by communicating said evacuated space with a further space containing a layer of arc deposited titanium and evacuated to a pressure of at most 10 -7 torr.
References Cited (Backward Citations)
US3270381A
Cited
US3729046A
Cited
US4537794A
Cited
US4481999A
Cited
US4505948A
Cited
US4805294A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-02-05 | 1993-08-07 | 1994-02-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-02-05 | 1997-08-07 | 1998-02-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-02-05 | 2001-08-07 | 2002-02-06 | $7700.00 | Window Closed / Lapsed |