Method for finishing the surface of plasma sprayed TI-alloy foils
Assignee: General Electric Co
•
Filing: 1987-02-04
•
Granted: 1989-02-21
•
Expires: 2007-02-04
Abstract
Abstract An improved method of forming titanium alloy in sheet form is taught. The sheet is formed by plasma spraying larger particles of greater than 100 μm diameter onto a receiving surface to form a sheet having a rough surface due to the larger particles. An RF powered gun is employed to form the deposit using the larger particles. The formed sheet is separated from the substrate and rolled to reduce the sheet thickness as well as to render the rough surface smoother and more even.
Inventors
- 👤 Paul A. Siemers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 06:10
CPC Classifications
C; C23; C23C; C23C4/00; C23C4/18; C23C4/185; B; B22; B22F; B22F3/00; B22F3/115; C22; C22C; C22C49/00; C22C49/02; C22C49/10; C22C49/11; B22F2998/00; B22F2998/10; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/4998; Y10T29/49988; Y10T29/49991
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
107 words
A method of forming a thin sheet of a titanium alloy which comprises providing a RF powered plasma gun, providing a supply of powder of the titanium alloy to be formed into a sheet, said powder having a particle size of greater than about 100 μm, supplying said powder to a plasma in said gun to cause a plasma deposit of said powder to form on a receiving surface, separating said plasma deposit from said surface as a free standing sheet having at least one rough surface, rolling the as-deposited sheet to reduce the thickness of said sheet and to increase the smoothness of the surfaces thereof.
Claim 2
Independent Claim
107 words
A method of forming a thin sheet of a titanium alloy which comprises providing a RF powered plasma gun, providing a supply of powder of the titanium alloy to be formed into a sheet, said powder having a particle size of greater than about 100 μm, supplying said powder to a plasma in said gun to cause a plasma deposit of said powder to form on a receiving surface, separating said plasma deposit from said surface as a free standing sheet having at least one rough surface, rolling the as-deposited sheet to reduce the thickness of said sheet and to increase the smoothness of the surfaces thereof.
Claim 3
Dependent Claim
21 words
The method of claim 1 in which the particle size of the powder is between about 100 μm and 250 μm.
Claim 4
Dependent Claim
11 words
The method of claim 1 in which the alloy is Ti-6Al-4V.
Claim 5
Dependent Claim
14 words
The method of claim 1 in which the thickness reduction is greater than 40%.
Claim 6
Independent Claim
99 words
The method of forming a composite of high strength fibers in a titanium alloy matrix which comprises providing the titanium alloy in the form of powder having particles of at least 100 μm, plasma spray depositing the powder onto a substrate to form a rough surface titanium alloy sheet, separating the titanium alloy sheet from the substrate, rolling the titanium alloy sheet to reduce the roughness of its surface, including the sheet in a compact of alternate layers of titanium alloy and reinforcing fiber, and HIPing the compact to form a reinforced composite of titanium alloy and reinforcing fibers.
Claim 7
Independent Claim
99 words
The method of forming a composite of high strength fibers in a titanium alloy matrix which comprises providing the titanium alloy in the form of powder having particles of at least 100 μm, plasma spray depositing the powder onto a substrate to form a rough surface titanium alloy sheet, separating the titanium alloy sheet from the substrate, rolling the titanium alloy sheet to reduce the roughness of its surface, including the sheet in a compact of alternate layers of titanium alloy and reinforcing fiber, and HIPing the compact to form a reinforced composite of titanium alloy and reinforcing fibers.
Claim 8
Dependent Claim
21 words
The method of claim 5 in which the particle size of the powder is between about 100 μm and 250 μm.
Claim 9
Dependent Claim
13 words
The method of claim 5 in which the titanium alloy powder is Ti-6Al-4V.
Claim 10
Dependent Claim
14 words
The method of claim 5 in which the thickness reduction is greater than 40%.
Claim 11
Dependent Claim
14 words
The method of claim 5 in which the reinforcing fiber is silicon carbide fiber.
Claim 12
Dependent Claim
13 words
The method of claim 1 in which the alloy is Ti-14Al-21Cb by weight.
Claim 13
Dependent Claim
13 words
The method of claim 5 in which they alloy is Ti-14Al-21Cb by weight.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-21 | 1992-08-22 | 1993-02-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-21 | 1996-08-22 | 1997-02-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-21 | 2000-08-22 | 2001-02-21 | $7700.00 | Window Closed / Lapsed |