Method of forming a thin unbacked metal foil
Assignee: ENERGY United States, Department of
•
Filing: 1982-02-23
•
Granted: 1984-11-13
•
Expires: 2002-02-23
Abstract
Abstract In a method of forming a thin (<2 μm) unbacked metal foil having a desired curviplanar shape, a soluble polymeric film, preferably comprising polyvinyl alcohol, is formed on a supporting structure having a shape that defines the desired shape of the foil product. A layer of metal foil is deposited onto one side of the soluble film, preferably by vacuum vapor deposition. The metallized film is then immersed in a suitable solvent to dissolve the film and thereby leave the metal foil as an unbacked metal foil element mounted on the supporting structure. Aluminum foils less than 0.2 μm (2,000 Å) thick and having an areal density of less than 54 μg/cm 2 have been obtained.
Inventors
- 👤 David V. Duchane
- 👤 Barry L. Barthell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 00:25
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/0005
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
108 words
A method of forming a thin unbacked metal foil, comprising the steps of: (a) forming on a suitable mold a film comprising polyvinyl alcohol and a plasticizer; (b) transferring said film to a supporting structure; (c) shrinking said film about said supporting structure by immersing said supporting structure and said film in a solvent selected to preferentially dissolve said plasticizer without dissolving said polyvinyl alcohol in said film; (d) depositing a continuous layer of metal at least approximately 1700 Angstroms thick onto said film by vacuum vapor deposition; and (e) immersing said film with said layer of metal deposited thereon in a suitable solvent to dissolve said film.
Claim 2
Independent Claim
108 words
A method of forming a thin unbacked metal foil, comprising the steps of: (a) forming on a suitable mold a film comprising polyvinyl alcohol and a plasticizer; (b) transferring said film to a supporting structure; (c) shrinking said film about said supporting structure by immersing said supporting structure and said film in a solvent selected to preferentially dissolve said plasticizer without dissolving said polyvinyl alcohol in said film; (d) depositing a continuous layer of metal at least approximately 1700 Angstroms thick onto said film by vacuum vapor deposition; and (e) immersing said film with said layer of metal deposited thereon in a suitable solvent to dissolve said film.
Claim 3
Dependent Claim
50 words
The method defined in claim 1 wherein said film is formed by immersing said mold in an aqueous solution comprising between 6 and 15% by weight polyvinyl alcohol, said polyvinyl alcohol being from 85 to 95% hydrolyzed, and subsequently removing said mold from said solution and allowing it to dry.
References Cited (Backward Citations)
US1447683A
Cited
US1889905A
Cited
US3181209A
Cited
US3195199A
Cited
GB1465908A
Cited
SU697244A1
Cited
US4128121A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-13 | 1988-05-14 | 1988-11-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-13 | 1992-05-14 | 1992-11-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-13 | 1996-05-14 | 1996-11-13 | $7700.00 | Window Closed / Lapsed |