Method of improving membrane properties via reaction of diazonium compounds or precursors
Assignee: Filmtec Corp
•
Filing: 1988-12-19
•
Granted: 1989-12-19
•
Expires: 2008-12-19
Abstract
Abstract A method of improving the properties of a reverse osmosis membrane having a polyamide discriminating layer containing residual aromatic primary amine groups is described. In this method, the polyamide discriminating layer of the membrane is treated with an aqueous solution of a reagent which reacts with primary amine groups to form diazonium salt groups or derivatives of diazonium salt groups. This method results in a membrane possessing improved chlorine resistance. When nitrous acid is employed as the reagent in the treatment, the water flux of the polyamide membrane is frequently increased with little or no effect on the salt rejection of the membrane.
Inventors
- 👤 John E. Cadotte
- 👤 Donald L. Schmidt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:08
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0081; B01D67/0093; B01D69/00; B01D69/12; B01D69/125; B01D69/1251; B01D2323/00; B01D2323/30
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
55 words
A method of improving the properties of a reverse osmosis membrane having a polyamide discriminating layer containing a plurality of residual aromatic primary amine groups, comprising treating the polyamide discriminating layer with an aqueous solution of a reagent which reacts with primary amine groups to form diazonium salt groups or derivatives of diazonium salt groups.
Claim 2
Independent Claim
55 words
A method of improving the properties of a reverse osmosis membrane having a polyamide discriminating layer containing a plurality of residual aromatic primary amine groups, comprising treating the polyamide discriminating layer with an aqueous solution of a reagent which reacts with primary amine groups to form diazonium salt groups or derivatives of diazonium salt groups.
Claim 3
Dependent Claim
22 words
The method as described in claim 1 further comprising treating the membrane with a wetting agent prior to treatment with the reagent.
Claim 4
Dependent Claim
15 words
The method as described in claim 1 wherein the aqueous solution includes a wetting agent.
Claim 5
Dependent Claim
28 words
The method as described in claim 1 wherein the polyamide is derived from an aromatic or cycloaliphatic compound bearing at least two acyl halide groups and a phenylenediamine.
Claim 6
Dependent Claim
27 words
The method as described in claim 4 wherein the compound bearing at least two acyl halide groups is trimesoyl halide, isophthaloyl halide, terephthaloyl halide or mixtures thereof.
Claim 7
Dependent Claim
21 words
The method as described in claim 5 wherein the acyl halide compound consists of at least 50 mole percent trimesoyl chloride.
Claim 8
Dependent Claim
15 words
The method as described in claim 6 wherein the acyl halide compound is cyclohexane-1,3,5-tricarbonyl chloride.
Claim 9
Dependent Claim
29 words
The method as described in claim 1 wherein the polyamide discriminating layer is treated with nitrous acid or a precursor which forms nitrous acid during treatment of the membrane.
Claim 10
Dependent Claim
28 words
The method as described in claim 8 wherein the polyamide is treated with nitrous acid at a temperature in the range from about 0° to about 30° C.
Claim 11
Dependent Claim
23 words
The method as described in claim 9 wherein the aqueous solution contains from about 0.01 to about 1 percent nitrous acid by weight.
Claim 12
Dependent Claim
73 words
The method as described in claim 1 wherein the reagent is nitrous acid or a precursor which forms nitrous acid during treatment of the membrane and the water flux of the treated membrane at a pressure of 200 psi and a temperature of 25° C. using a 0.2 weight percent aqueous NaCl solution is at least 10 percent greater than the water flux of the same membrane at these conditions prior to treatment.
References Cited (Backward Citations)
US3551331A
Cited
US3721623A
Cited
US3951920A
Cited
US3806564A
Cited
JPS4945147A
Cited
US3850797A
Cited
US4005012A
Cited
US4087388A
Cited
US4080296A
Cited
US4340480A
Cited
US4340479A
Cited
US4340479B1
Cited
US4259183A
Cited
US4277344A
Cited
US4584103A
Cited
US4673504A
Cited
US4512893A
Cited
JPS5980304A
Cited
US4415455A
Cited
US4606943A
Cited
US4701186A
Cited
US4472175A
Cited
US4627992A
Cited
US4520044A
Cited
US4601827A
Cited
US4605526A
Cited
US4704324A
Cited
US4661254A
Cited
US4719062A
Cited
US4626468A
Cited
US4812238A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-12-18 | 1993-06-19 | 1993-12-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-12-18 | 1997-06-19 | 1997-12-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-12-18 | 2001-06-19 | 2001-12-19 | $7700.00 | Window Closed / Lapsed |