Reverse osmosis membrane

Claim 2

A process for preparation of a composite reverse osmosis membrane comprising the steps of: (a) coating a porous support with a layer comprising an aqueous solution containing, dissolved therein, an essentially monomeric, polyfunctional, essentially water-soluble secondary amine; (b) contacting the said layer with an relatively water-insoluble, essentially monomeric, volatilizable polyfunctional acid halide component having an average acid halide functionality greater than 2.05, for a time sufficient to effect in-situ chain extension and crosslinking reactions between the secondary amine and the polyfunctional acid halide; and (c) drying the product of step (b) to form the composite reverse osmosis membrane.

Claim 3

The process of claim 1 in which the porous support comprises a polysulfone film.

Claim 4

The process of claim 1 in which said secondary amine is selected from the group consisting of piperazine and substituted piperazine.

Claim 5

The process of claim 1 in which the acyl halide comprises trimesoyl chloride.

Claim 6

The process of claim 1 in which the acyl halide comprises a mixture of trimesoyl chloride and isophthaloyl chloride.

Claim 7

A composite reverse osmosis membrane prepared by the process of claim 1.

Claim 8

A process for preparation of a composite reverse osmosis membrane comprising the steps of: (a) coating a porous support with a layer of an aqueous medium containing, dissolved therein, an essentially water-soluble polyamide prepolymer terminated with secondary amine functional groups, the secondary amine functionality of said prepolymer being greater than 2.0; (b) contacting the said layer with a polyfunctional acid halide for a time sufficient to effect in-situ chain extension and crosslinking reactions between the polyamide prepolymer and the polyfunctional acid halide; and (c) drying the product of step (b) to form the composite reverse osmosis membrane.

Claim 9

A process for preparation of a composite reverse osmosis membrane comprising the steps of: (a) coating a porous support with a layer of an aqueous medium containing, dissolved therein, an essentially water-soluble polyamide prepolymer terminated with secondary amine functional groups, the secondary amine functionality of said prepolymer being greater than 2.0; (b) contacting the said layer with a polyfunctional acid halide for a time sufficient to effect in-situ chain extension and crosslinking reactions between the polyamide prepolymer and the polyfunctional acid halide; and (c) drying the product of step (b) to form the composite reverse osmosis membrane.

Claim 10

The process of claim 7 wherein the amine-terminated polyamide prepolymer comprises the reaction product of the reaction mixture comprising piperazine and trimesoyl chloride, and wherein the ratio of equivalents of secondary amine to equivalents of carboxylic acid chloride in said reaction mixture is greater than 1:1.

Claim 11

The process of claim 1 in which the polyfunctional halide of step (b) comprises isophthaloyl chloride.

Claim 12

A process according to claim 7 wherein said layer of step (a) is contacted with a solution comprising the polyfunctional acid chloride dissolved in a nonpolar organic liquid solvent, and said reactions of said step (b) occur at the interface between said layer and said solution.

Claim 13

A process according to claim 10 wherein said organic liquid solvent comprises a liquid alkane.

Claim 14

A process according to claim 7 comprising the steps of: (a) reacting an excess over stoichiometry of an essentially water soluble, polyfunctional secondary amine component with a polyfunctional acid halide component in a nonpolar liquid organic reaction medium, said polyfunctional acid halide having an average acid halide functionality above 2.05, thereby obtaining an essentially water-soluble, secondary-amine terminated polyamide prepolymer; (b) isolating said prepolymer from said nonpolar liquid organic reaction medium and dissolving the thus-isolated prepolymer in an aqueous medium to obtain an aqueous solution containing said prepolymer; (c) coating a layer, comprising said aqueous solution, onto a porous support; (d) contacting said layer with a polyfunctional acid halide to obtain a crosslinked, interfacially polymerized, water insoluble polyamide on said porous support; and (e) drying the product of step (d).

Claim 15

A composite reverse osmosis membrane prepared by the process of claim 7.

Claim 16

In a process for desalination of saline water by reverse osmosis comprising contacting the saline water under pressure with a reverse osmosis membrane, the improvement comprising using the membrane of claim 6 as the reverse osmosis membrane.

Claim 17

The process of claim 14 wherein the saline water contains at least about 3,000 parts per million by weight of an alkaline earth metal salt or a sulfate salt.

Claim 18

In a process for desalination of saline water by reverse osmosis comprising contacting the saline water under pressure with a reverse osmosis membrane, the improvement comprising using the membrane of claim 13 as the reverse osmosis membrane.

Claim 19

The process of claim 16 wherein the saline water contains at least about 3,000 parts per million by weight of an inorganic chloride salt.