Chemical modification of polybenzimidazole semipermeable
Assignee: Celanese Corp
•
Filing: 1975-08-21
•
Granted: 1977-04-26
•
Expires: 1995-08-21
Abstract
Abstract A preformed polybenzimidazole semipermeable membrane (e.g., a film or hollow filament) is chemically modified in accordance with the present invention. Imidazole groups of the polybenzimidazole membrane are cross-linked by reaction with a strong polybasic acid or its acid chloride (as defined). During the reaction the polybasic acid is dissolved in a relatively mild acid medium (e.g., glacial acetic acid) which serves to decrease the basicity of the imidazole groups and to promote the desired cross-linking reaction. The resulting cross-linked membrane is tougher than the untreated membrane and may be more readily handled without deleterious results. Also, the resulting cross-linked polybenzimidazole membrane no longer is soluble in N,N-dimethylacetamide, and exhibits improved service characteristics such as improved compaction resistance during prolonged usage at high pressure. The product of the present invention is particularly suited for use in separations from acid waste streams. Cross-linked polybenzimidazole membranes capable of reverse osmosis separations, ion exchange separations, and ultrafiltration separations may be formed in accordance with the present process.
Inventors
- 👤 Howard J. Davis
- 👤 Norman W. Thomas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 08:50
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/20; C08J5/22; C08J5/2287; B; B01; B01D; B01D71/00; B01D71/06; B01D71/58; B01D71/62; C08G; C08G73/00; C08G73/06; C08G73/18; C08J2379/00; C08J2379/04; C08J2379/06
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
169 words
A process for chemically modifying a preformed polybenzimidazole semipermeable membrane wherein said polybenzimidazole is soluble in N,N-dimethylacetamide and consists essentially of recurring units of the formula: ##STR4## wherein R is a tetravelent aromatic nucleus, with the nitrogen atoms forming the benzimidazole rings paired upon adjacent carbon atoms of said aromatic nucleus, and R' is selected from the group consisting of (1) an aromatic ring, (2) an alkylene group having from 4 to 8 carbon atoms, and (3) a heterocyclic ring selected from the group consisting of (a) pyridine, (b) pyrazine, (c) furan, (d) quinoline, (e) thiophene, and (f) pyran, comprising contacting said membrane with a strong polybasic acid having a pK A value below 4 or its acid halide which is dissolved in a relatively mild acid medium having a pK A value of about 4 to 5 in a concentration sufficient to form a cross-linked polybenzimidazole which is not soluble in N,N-dimethylacetamide wherein said polybasic acid or acid halide reacts with the imidazole groups of said polybenzimidazole membrane.
Claim 2
Dependent Claim
169 words
A process for chemically modifying a preformed polybenzimidazole semipermeable membrane wherein said polybenzimidazole is soluble in N,N-dimethylacetamide and consists essentially of recurring units of the formula: ##STR4## wherein R is a tetravelent aromatic nucleus, with the nitrogen atoms forming the benzimidazole rings paired upon adjacent carbon atoms of said aromatic nucleus, and R' is selected from the group consisting of (1) an aromatic ring, (2) an alkylene group having from 4 to 8 carbon atoms, and (3) a heterocyclic ring selected from the group consisting of (a) pyridine, (b) pyrazine, (c) furan, (d) quinoline, (e) thiophene, and (f) pyran, comprising contacting said membrane with a strong polybasic acid having a pK A value below 4 or its acid halide which is dissolved in a relatively mild acid medium having a pK A value of about 4 to 5 in a concentration sufficient to form a cross-linked polybenzimidazole which is not soluble in N,N-dimethylacetamide wherein said polybasic acid or acid halide reacts with the imidazole groups of said polybenzimidazole membrane.
Claim 3
Dependent Claim
20 words
A process for chemically modifying a preformed polybenzimidazole semipermeable membrane in accordance with claim 1 wherein said polybenzimidazole is poly-2,2'-(m-phenylene)-5,5'-bibenzimidazole.
Claim 4
Dependent Claim
24 words
A process for chemically modifying a preformed polybenzimidazole semipermeable membrane in accordance with claim 1 wherein said membrane has the configuration of a film.
Claim 5
Dependent Claim
27 words
A process for chemically modifying a preformed polybenzimidazole semipermeable membrane in accordance with claim 3 wherein said film has a thickness of about 0.5 to 12 mils.
Claim 6
Dependent Claim
25 words
A process for chemically modifying a preformed semipermeable polybenzimidazole membrane in accordance with claim 1 wherein said membrane has the configuration of a hollow filament.
Claim 7
Dependent Claim
29 words
A process for chemically modifying a preformed polybenzimidazole semipermeable membrane in accordance with claim 5 wherein said hollow filament has a wall thickness of about 20 to 160 microns.
Claim 8
Dependent Claim
42 words
A process for chemically modifying a preformed semipermeable polybenzimidazole membrane in accordance with claim 1 wherein said solution of said strong polybasic acid or acid halide is provided at a temperature of about 5° to 100° C. when contacted with said membrane.
Claim 9
Dependent Claim
26 words
A process for chemically modifying a preformed semipermeable polybenzimidazole membrane in accordance with claim 1 wherein said contact is conducted for about 5 to 300 minutes.
Claim 10
Dependent Claim
49 words
A process for chemically modifying a preformed polybenzimidazole semipermeable membrane in accordance with claim 1 wherein said strong polybasic acid or acid halide is selected from the group consisting essentially of perfluoroglutaric acid, isophthaloyl chloride, polyacrylic acid, sulfuric acid, 1,2,4,5-benzenetetracarboxylic acid, 1,4,5,8-naphthalene tetracarboxylic acid, and mixtures of the foregoing.
Claim 11
Dependent Claim
25 words
A process for chemically modifying a preformed polybenzimidazole semipermeable membrane in accordance with claim 1 wherein said relatively mild acid medium is glacial acetic acid.
Claim 12
Dependent Claim
19 words
A chemically modified polybenzimidazole semipermeable membrane which is insoluble N,N-dimethylacetamide formed in accordance with the process of claim 1.
Claim 13
Dependent Claim
86 words
A process for chemically modifying a preformed poly-2,2'-(m-phenylene-5,5'-bibenzimidazole semipermeable membrane comprising contacting said membrane which is soluble in N,N-dimethylacetamide with a strong polybasic organic acid having a pK A value below 4 or its acid halide which is dissolved in glacial acetic acid in a concentration of about 1 to 25 percent by weight based upon the total weight of the solution to form a cross-linked poly-2,2'-(m-phenylene)-5,5'-bibenzimidazole which is not soluble in N,N-dimethylacetamide wherein said polybasic organic acid reacts with the imidazole groups of said membrane.
Claim 14
Dependent Claim
86 words
A process for chemically modifying a preformed poly-2,2'-(m-phenylene-5,5'-bibenzimidazole semipermeable membrane comprising contacting said membrane which is soluble in N,N-dimethylacetamide with a strong polybasic organic acid having a pK A value below 4 or its acid halide which is dissolved in glacial acetic acid in a concentration of about 1 to 25 percent by weight based upon the total weight of the solution to form a cross-linked poly-2,2'-(m-phenylene)-5,5'-bibenzimidazole which is not soluble in N,N-dimethylacetamide wherein said polybasic organic acid reacts with the imidazole groups of said membrane.
Claim 15
Dependent Claim
30 words
A process for chemically modifying a preformed poly-2,2'-(m-phenylene)-5,5'-bibenzimidazole semipermeable membrane in accordance with claim 12 wherein said membrane is a film having a thickness of about 1 to 5 mils.
Claim 16
Dependent Claim
32 words
A process for chemically modifying a preformed poly-2,2'-(m-phenylene-5,5'-bibenzimidazole semipermeable membrane in accordance with claim 12 wherein said membrane is a hollow filament having a wall thickness of about 20 to 160 microns.
Claim 17
Dependent Claim
43 words
A process for chemically modifying a preformed semipermeable poly-2,2'-(m-phenylene-5,5'-bibenzimidazole membrane in accordance with claim 12 wherein said solution of strong polybasic organic acid or its acid halide is provided at a temperature of about 20° to 30° C. when contacted with said membrane.
Claim 18
Dependent Claim
26 words
A process for chemically modifying a preformed semipermeable poly-2,2'-(m-phenylene)-5,5'-bibenzimidazole membrane in accordance with claim 12 wherein said contact is conducted for about 5 to 120 minutes.
Claim 19
Dependent Claim
47 words
A process for chemically modifying a preformed semipermeable poly-2,2'-(m-phenylene-5,5'-bibenzimidazole membrane in accordance with claim 12 wherein said polybasic organic acid or acid chloride is selected from the group consisting essentially of perfluoroglutaric acid, isophthaloyl chloride polyacrylic acid, 1,2,4,5-benzenetetracarboxylic acid, 1,4,5,8-naphthalene tetracarboxylic acid, and mixtures of the foregoing.
Claim 20
Dependent Claim
26 words
A process for chemically modifying a preformed semipermeable poly-2,2'-(m-phenylene)-5,5'-bibenzimidazole membrane in accordance with claim 12 wherein said polybasic organic acid or acid chloride is perfluoroglutaric acid.
Claim 21
Dependent Claim
54 words
A process for chemically modifying a preformed semipermeable poly-2,2'-(m-phenylene)-5,5'-bibenzimidazole membrane in accordance with claim 12 wherein said strong polybasic organic acid having a pK A value below 4 is present in said glacial acetic acid in a concentration of about 1 to 10 percent by weight based upon the total weight of the solution.
References Cited (Backward Citations)
US3542735A
Cited
US3720607A
Cited
US3763107A
Cited
US3808305A
Cited
US3851025A
Cited
US3892665A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-25 | 1980-10-25 | 1981-04-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-25 | 1984-10-25 | 1985-04-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-25 | 1988-10-25 | 1989-04-26 | $7700.00 | Window Closed / Lapsed |