US4340480A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for preparing liquophilic polyamide membrane filter media and product
Assignee: Pall Corp
•
Filing: 1980-10-20
•
Granted: 1982-07-20
•
Expires: 2000-10-20
Abstract
Abstract A process is provided for preparing skinless liquophilic alcohol-insoluble polyamide membranes by preparing at a first temperature a solution in a polyamide solvent having a temperature coefficient of solubility within the range from about 0.01 to about 5 weight percent per degree Centigrade of an alcohol-insoluble polyamide resin having a ratio CH 2 :NHCO of methylene CH 2 to amide NHCO groups within the range from about 7:1 to about 12:1; inducing nucleation of the solution by controlled addition to the solution of a nonsolvent for the polyamide resin, under controlled conditions of concentration, temperature, addition rate, and degree of agitation to obtain a visible precipitate of polyamide resin particles which may or may not thereafter partially or completely redissolve, thereby forming a casting solution; spreading the casting solution on a substrate to form a thin film thereof on the substrate; cooling the film of casting solution to a second temperature sufficiently lower than the first temperature to precipitate polyamide resin from the casting solution; contacting and diluting the film of casting solution with a nonsolvent liquid, preferably containing a substantial proportion of the solvent liquid but less than the proportion in the casting solution, to precipitate polyamide resin from the casting solution in the form of a thin skinless liquophilic membrane; and washing and drying the resulting membrane.
Inventors
- 👤 David B. Pall
- 👤 Frank Model
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 21:20
CPC Classifications
B; B01; B01D; B01D71/00; B01D71/06; B01D71/56; B01D61/00; B01D61/14; B01D61/145; B01D65/00; B01D65/10; B01D65/102; B01D67/00; B01D67/0002; B01D67/0009; B01D69/00; B01D69/12; B01D69/1214; B01D2313/00; B01D2313/44; B01D2323/00; B01D2323/08; B01D2323/12; B01D2325/00; B01D2325/36; B01D2325/38
Claims Analysis
Total Claims: 85
Claim 1
Independent Claim
193 words
A process for preparing skinless liquophilic alcohol insoluble polyamide membranes which comprises preparing at a first dissolution temperature a solution in a polyamide solvent having a temperature coefficient of solubility within the range from about 0.01 to about 5 weight percent per degree Centigrade of an alcohol-insoluble polyamide resin having a ratio CH 2 :NHCO of methylene CH 2 to amide NHCO groups within the range from about 7:1 to about 12:1; inducing nucleation of the solution by controlled addition to the solution of a nonsolvent for the polyamide resin, under controlled conditions of concentration, temperature, addition rate and degree of agitation to obtain a visible precipitate of polyamide resin particles, thereby forming a casting solution; spreading the casting solution on a substrate to form a thin film thereof on the substrate; cooling the film of casting solution to a second gelation temperature sufficiently lower than the first temperature to precipitate polyamide resin from the casting solution; contacting and diluting the film of casting solution with a nonsolvent liquid to precipitate polyamide resin from the casting solution in the form of a thin skinless liquophilic membrane; and washing and drying the resulting membrane.
Claim 2
Dependent Claim
193 words
A process for preparing skinless liquophilic alcohol insoluble polyamide membranes which comprises preparing at a first dissolution temperature a solution in a polyamide solvent having a temperature coefficient of solubility within the range from about 0.01 to about 5 weight percent per degree Centigrade of an alcohol-insoluble polyamide resin having a ratio CH 2 :NHCO of methylene CH 2 to amide NHCO groups within the range from about 7:1 to about 12:1; inducing nucleation of the solution by controlled addition to the solution of a nonsolvent for the polyamide resin, under controlled conditions of concentration, temperature, addition rate and degree of agitation to obtain a visible precipitate of polyamide resin particles, thereby forming a casting solution; spreading the casting solution on a substrate to form a thin film thereof on the substrate; cooling the film of casting solution to a second gelation temperature sufficiently lower than the first temperature to precipitate polyamide resin from the casting solution; contacting and diluting the film of casting solution with a nonsolvent liquid to precipitate polyamide resin from the casting solution in the form of a thin skinless liquophilic membrane; and washing and drying the resulting membrane.
Claim 3
Dependent Claim
22 words
A process according to claim 1 in which precipitated polyamide resin particles are redissolved before spreading the casting solution on a substrate.
Claim 4
Dependent Claim
23 words
A process according to claim 1 in which precipitated polyamide resin particles are filtered out before spreading the casting solution on a substrate.
Claim 5
Dependent Claim
30 words
A process according to claim 1 in which part of the precipitated polyamide resin particles are redissolved and part are filtered out before spreading the casting solution on a substrate.
Claim 6
Dependent Claim
43 words
A process according to claim 1 in which the nonsolvent used to contact and dilute the casting solution is a mixture of solvent and nonsolvent liquids containing a substantial proportion of the solvent liquid, but less than the proportion in the casting solution.
Claim 7
Dependent Claim
14 words
A process according to claim 1 in which the polyamide resin is polyhexamethylene dodecandiamide.
Claim 8
Dependent Claim
13 words
A process according to claim 1 in which the polyamide resin is poly-11-amino-undecanamide.
Claim 9
Dependent Claim
32 words
A process according to claim 1 in which the polyamide resin is polyhexamethylene dodecandiamide, the solvent for the polyamide resin solution is formic acid, and the nonsolvent added for dilution is water.
Claim 10
Dependent Claim
31 words
A process according to claim 1 in which the polyamide resin is polyundecanamide, the solvent for the polyamide resin solution is formic acid, and the nonsolvent added for dilution is water.
Claim 11
Dependent Claim
39 words
A process according to claim 1 in which the first dissolution temperature is within the range from about 50° to about 200° C. and the second gelation temperature is within the range from about 10° to about 35° C.
Claim 12
Dependent Claim
41 words
A process according to claim 10 in which the polyamide resin solution film is air-cooled for at least ten seconds and is then contacted with the nonsolvent by immersing the film carried on the substrate in a bath of nonsolvent liquid.
Claim 13
Dependent Claim
16 words
A process according to claim 11 in which the bath comprises both solvent and nonsolvent liquids.
Claim 14
Dependent Claim
40 words
A process according to claim 12 in which the bath comprises an amount within the range from about 0.1 to about 50% of a solvent for the resin; washing the resulting membrane substantially free of solvent; and drying the membrane.
Claim 15
Dependent Claim
18 words
A process according to claim 11 in which precipitation is substantially carried to completion during the air-cooling step.
Claim 16
Dependent Claim
12 words
A process according to claim 10 in which the membrane is air-dried.
Claim 17
Dependent Claim
15 words
A process according to claim 10 in which the membrane is washed directly following precipitation.
Claim 18
Dependent Claim
60 words
A process according to claim 1 in which the polyamide resin is polyhexamethylene dodecandiamide, the solvent is formic acid, and the nonsolvent is water, and the polyamide resin concentration in the casting solution is within the range from about 10 to about 20% by weight, and the formic acid concentration is within the range from about 70 to about 85%.
Claim 19
Dependent Claim
37 words
A process according to claim 17 in which the polyamide resin concentration of the casting solution is within the range from about 10 to about 20%, and the nonsolvent is added at a fixed intensity of mixing.
Claim 20
Dependent Claim
88 words
A process according to claim 10 in which the casting resin is continuously spread onto the substrate, the thin film of casting solution is continuously air-cooled through a gap which assures a minimum cooling time of seconds, and then immersed in a bath of nonsolvent liquid, and the bath is maintained at a substantially constant composition with respect to nonsolvent and solvent by continuous addition of nonsolvent to the bath in a quantity to compensate for solvent diffusion into the bath from the thin film of casting solution.
Claim 21
Dependent Claim
29 words
A process according to claim 19 in which the substrate is a nonporous synthetic polymer film having a surface that is wetted by the casting solution and the bath.
Claim 22
Dependent Claim
41 words
A process according to claim 19 in which the substrate is a porous web having an open structure which is wetted and impregnated by the casting solution, thereby forming a membrane film having the porous web incorporated as a part thereof.
Claim 23
Dependent Claim
15 words
A process according to claim 19 in which the substrate is a fibrous polyester sheet.
Claim 24
Dependent Claim
36 words
A process according to claim 19 in which the substrate is a porous web which is not wetted by the casting solution, thereby forming a membrane film having the porous web attached to one surface thereof.
Claim 25
Dependent Claim
34 words
A process according to claim 10 in which the casting and gelation temperatures are within the range from about 10° C. to the boiling temperature of the lowest boiling solvent or nonsolvent component present.
Claim 26
Dependent Claim
30 words
A process according to claim 1 in which the polyamide resin solution has a viscosity within the range from about 5,000 centipoises to about 50,000 centipoises at the operating temperature.
Claim 27
Dependent Claim
29 words
A process according to claim 1 in which the casting resin solution is clear, and free from suspended material, before being spread upon the substrate to form a film.
Claim 28
Dependent Claim
20 words
A process according to claim 1 in which the membrane is stripped from the substrate after washing and before drying.
Claim 29
Dependent Claim
30 words
A process according to claim 1 in which the substrate is not stripped from the polyamide resin membrane before drying, and after drying remains attached to the polyamide resin membrane.
Claim 30
Dependent Claim
14 words
A process according to claim 1 in which the substrate is of polypropylene resin.
Claim 31
Dependent Claim
14 words
A process according to claim 1 in which the substrate is of polyester resin.
Claim 32
Dependent Claim
79 words
A process according to claim 1 in which the solvent for the polyamide resin solution is formic acid maintained at a first dissolution temperature of at least 50° C. and the nonsolvent is water, and the polyamide resin solution film is allowed to cool in air for at least 10 seconds followed by contact with the nonsolvent by immersing the film carried on the substrate in a bath of nonsolvent comprising water containing a substantial proportion of formic acid.
Claim 33
Dependent Claim
210 words
A process for preparing skinless liquophilic alcohol-insoluble poly-11-amino-undecanamide resin membranes having pores that are substantially uniform from surface to surface which comprises preparing a flowable solution of the alcohol-insoluble liquophobic polyundecanamide resin in a concentration within the range from about 10 to about 20 by weight at a first dissolution temperature of at least 50° C. in a solution in aqueous formic acid containing from about 70 to about 85% formic acid; inducing nucleation of the solution by addition of water to the solution under controlled conditions of concentration, temperature, addition rate, and degree of agitation to obtain a visible precipitate of polyamide resin particles, thereby forming a casting solution; removing any undissolved resin by filtration; spreading the casting solution on a substrate to form a thin film thereof on the substrate; cooling the film of casting solution to a second gelation temperature sufficiently lower than the first temperature to precipitate polyamide resin from the casting solution; contacting and diluting the film of casting solution with either water or an aqueous solution of formic acid containing up to 50% formic acid by weight, to precipitate polyamide resin from the casting solution in the form of a thin skinless liquophilic membrane; washing the membrane to remove solvent; and drying the membrane.
Claim 34
Dependent Claim
210 words
A process for preparing skinless liquophilic alcohol-insoluble poly-11-amino-undecanamide resin membranes having pores that are substantially uniform from surface to surface which comprises preparing a flowable solution of the alcohol-insoluble liquophobic polyundecanamide resin in a concentration within the range from about 10 to about 20 by weight at a first dissolution temperature of at least 50° C. in a solution in aqueous formic acid containing from about 70 to about 85% formic acid; inducing nucleation of the solution by addition of water to the solution under controlled conditions of concentration, temperature, addition rate, and degree of agitation to obtain a visible precipitate of polyamide resin particles, thereby forming a casting solution; removing any undissolved resin by filtration; spreading the casting solution on a substrate to form a thin film thereof on the substrate; cooling the film of casting solution to a second gelation temperature sufficiently lower than the first temperature to precipitate polyamide resin from the casting solution; contacting and diluting the film of casting solution with either water or an aqueous solution of formic acid containing up to 50% formic acid by weight, to precipitate polyamide resin from the casting solution in the form of a thin skinless liquophilic membrane; washing the membrane to remove solvent; and drying the membrane.
Claim 35
Dependent Claim
20 words
A process according to claim 32 in which the membrane is stripped from the substrate after washing and before drying.
Claim 36
Dependent Claim
22 words
A process according to claim 32 in which precipitated polyamide resin particles are dissolved before spreading the casting solution on a substrate.
Claim 37
Dependent Claim
23 words
A process according to claim 32 in which precipitated polyamide resin particles are filtered out before spreading the casting solution on a substrate.
Claim 38
Dependent Claim
30 words
A process according to claim 32 in which part of the precipitated polyamide resin particles are redissolved and part are filtered out before spreading the casting solution on a substrate.
Claim 39
Dependent Claim
226 words
A continuous process for preparing skinless liquophilic alcohol-insoluble polyamide membranes which comprises preparing at a first dissolution temperature a solution in a polyamide solvent having a temperature coefficient of solubility within the range from about 0.01 to about 5 weight percent per degree Centigrade of an alcohol-insoluble polyamide resin having a ratio CH 2 :NHCO of methylene CH 2 to amide NHCO groups within the range from about 7:1 to about 12:1; inducing nucleation of the solution by controlled addition to the solution of a nonsolvent for the polyamide resin, under controlled conditions of concentration, temperature, addition rate, and degree of agitation to obtain a visible precipitate of polyamide resin particles thereby forming a casting solution; removing any undissolved resin by filtration; spreading the casting solution on a substrate which is nonporous and whose surface is wetted by the casting solution to form a thin film thereof on the substrate; cooling the film of casting solution to a second gelation temperature sufficiently lower than the first temperature to precipitate polyamide resin from the casting solution; contacting and diluting the film of casting solution with a nonsolvent liquid to precipitate polyamide resin from the casting solution in the form of a thin skinless liquophilic membrane; and continuously washing and drying the resulting membrane, while maintaining constant the relative proportion of solvent and nonsolvent liquid in the bath.
Claim 40
Dependent Claim
226 words
A continuous process for preparing skinless liquophilic alcohol-insoluble polyamide membranes which comprises preparing at a first dissolution temperature a solution in a polyamide solvent having a temperature coefficient of solubility within the range from about 0.01 to about 5 weight percent per degree Centigrade of an alcohol-insoluble polyamide resin having a ratio CH 2 :NHCO of methylene CH 2 to amide NHCO groups within the range from about 7:1 to about 12:1; inducing nucleation of the solution by controlled addition to the solution of a nonsolvent for the polyamide resin, under controlled conditions of concentration, temperature, addition rate, and degree of agitation to obtain a visible precipitate of polyamide resin particles thereby forming a casting solution; removing any undissolved resin by filtration; spreading the casting solution on a substrate which is nonporous and whose surface is wetted by the casting solution to form a thin film thereof on the substrate; cooling the film of casting solution to a second gelation temperature sufficiently lower than the first temperature to precipitate polyamide resin from the casting solution; contacting and diluting the film of casting solution with a nonsolvent liquid to precipitate polyamide resin from the casting solution in the form of a thin skinless liquophilic membrane; and continuously washing and drying the resulting membrane, while maintaining constant the relative proportion of solvent and nonsolvent liquid in the bath.
Claim 41
Dependent Claim
27 words
A process according to claim 37, in which the rates of withdrawal and addition of solvent and nonsolvent to and from the bath are maintained substantially constant.
Claim 42
Dependent Claim
15 words
A process according to claim 37, in which the polyamide is poly-11-amino-undecanamide or polyhexamethylene dodecandiamide.
Claim 43
Dependent Claim
71 words
A liquophilic skinless alcohol-insoluble polyamide resin membrane sheet of alcohol-insoluble liquophobic polyamide resin, capable when completely immersed in an organic liquid having a surface tension of from about 40 to about 60 dynes/cm of being wetted through within no more than one second, and reverting when heated to a temperature just below the softening temperature of the membrane to a liquophobic material which is no longer wetted by such organic liquids.
Claim 44
Dependent Claim
71 words
A liquophilic skinless alcohol-insoluble polyamide resin membrane sheet of alcohol-insoluble liquophobic polyamide resin, capable when completely immersed in an organic liquid having a surface tension of from about 40 to about 60 dynes/cm of being wetted through within no more than one second, and reverting when heated to a temperature just below the softening temperature of the membrane to a liquophobic material which is no longer wetted by such organic liquids.
Claim 45
Dependent Claim
28 words
A liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 40 having through pores extending from surface to surface that are substantially uniform in shape and size.
Claim 46
Dependent Claim
37 words
A liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 40 having through pores extending from surface to surface that are tapered, wider at one surface and narrowing towards the other surface of the membrane sheet.
Claim 47
Dependent Claim
23 words
A liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 40 having absolute particle removal ratings of 0.10 μM to 5 μM.
Claim 48
Dependent Claim
19 words
A liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 40 in which the polyamide resin is poly-11-amino-undecanamide.
Claim 49
Dependent Claim
20 words
A liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 40 in which the polyamide resin is polyhexamethylene dodecandiamide.
Claim 50
Dependent Claim
38 words
A liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 40 having two membrane layers adherent to each other and forming a single membrane sheet with particle removal characteristics superior to those of the individual membrane layers.
Claim 51
Dependent Claim
22 words
A liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 46 in which the two membrane layers have the same porosities.
Claim 52
Dependent Claim
21 words
A liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 46 in which the two membrane layers having differing porosities.
Claim 53
Dependent Claim
19 words
A liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 46 in which the membranes have tapered pores.
Claim 54
Dependent Claim
19 words
A liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 46 in which the membranes have uniform pores.
Claim 55
Dependent Claim
18 words
A liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 46 in which the membranes are supported.
Claim 56
Dependent Claim
18 words
A liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 46 in which the membranes are unsupported.
Claim 57
Dependent Claim
25 words
A liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 40 having a thickness within the range from about 0.025 to about 0.8 mm.
Claim 58
Dependent Claim
67 words
A filter and separator element comprising a liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 40 formed in a tubular configuration with the ends of the tube sealed to end caps of which at least one end cap has a central aperture giving access to the interior of the tube, and with the sides of the sheet lapped and sealed together, all seals being fluid-tight.
Claim 59
Dependent Claim
15 words
A filter and separator element according to claim 54 in which the sheet is corrugated.
Claim 60
Dependent Claim
28 words
A filter and separator element according to claim 54 in which at least one of the exterior faces of the sheet is adhered to a porous support layer.
Claim 61
Dependent Claim
21 words
A filter and separator element according to claim 56 in which both the membrane sheet and the support layer are corrugated.
Claim 62
Dependent Claim
22 words
A filter and separator element according to claim 54 comprising a multilayer membrane sheet, the layers being adhered together as one sheet.
Claim 63
Dependent Claim
29 words
A filter and separator element according to claim 58 in which the layers of membrane are separated by a porous support layer to which each membrane layer is adhered.
Claim 64
Dependent Claim
40 words
A filter and separator element according to claim 46 in which the end caps are of polyester resin and the filter element including the end caps is liquophilic and rapidly wetted by liquids with surface tension below about 60 dynes/cm.
Claim 65
Dependent Claim
16 words
A filter and separator element according to claim 52 in which the polyester is polybutylene terephthalate.
Claim 66
Dependent Claim
16 words
A filter and separator element according to claim 52 in which the polyester is polyethylene terephthalate.
Claim 67
Dependent Claim
264 words
A process for preparing skinless liquophilic alcohol-insoluble polyamide membrane sheets having multimembrane layers, which comprises preparing at a first dissolution temperature at least two starting solutions in a polyamide solvent having a temperature coefficient of solubility within the range from about 0.01 to about 5 weight percent per degree Centigrade of an alcohol-insoluble polyamide resin having a ratio CH 2 :NHCO of methylene CH 2 to amide NHCO groups within the range from about 7:1 to about 12:1; inducing nucleation of the solution by controlled addition to the solutions of a nonsolvent for the polyamide resin, under controlled conditions of concentration, temperature, addition rate, and degree of agitation to obtain a visible precipitate of polyamide resin particles which may or may not thereafter partially or completely redissolve, thereby forming a casting solution; removing any undissolved resin by filtration; spreading the casting solutions on a substrate to form thin films thereof on the substrate; cooling the films of casting solution to a second gelation temperature sufficiently lower than the first temperature to precipitate polyamide resin from the casting solution; contacting and diluting the films of casting solution with a nonsolvent liquid to precipitate polyamide resin from the casting solution in the form of a thin skinless liquophilic membrane; washing the resulting two membranes; combining the two membranes so formed as a dual layer; and drying the dual layer under conditions of restraint to prevent more than minor reduction of the length and width of the membrane; the membranes so dried forming a single sheet with particle removal characteristics superior to those of the individual layers.
Claim 68
Dependent Claim
264 words
A process for preparing skinless liquophilic alcohol-insoluble polyamide membrane sheets having multimembrane layers, which comprises preparing at a first dissolution temperature at least two starting solutions in a polyamide solvent having a temperature coefficient of solubility within the range from about 0.01 to about 5 weight percent per degree Centigrade of an alcohol-insoluble polyamide resin having a ratio CH 2 :NHCO of methylene CH 2 to amide NHCO groups within the range from about 7:1 to about 12:1; inducing nucleation of the solution by controlled addition to the solutions of a nonsolvent for the polyamide resin, under controlled conditions of concentration, temperature, addition rate, and degree of agitation to obtain a visible precipitate of polyamide resin particles which may or may not thereafter partially or completely redissolve, thereby forming a casting solution; removing any undissolved resin by filtration; spreading the casting solutions on a substrate to form thin films thereof on the substrate; cooling the films of casting solution to a second gelation temperature sufficiently lower than the first temperature to precipitate polyamide resin from the casting solution; contacting and diluting the films of casting solution with a nonsolvent liquid to precipitate polyamide resin from the casting solution in the form of a thin skinless liquophilic membrane; washing the resulting two membranes; combining the two membranes so formed as a dual layer; and drying the dual layer under conditions of restraint to prevent more than minor reduction of the length and width of the membrane; the membranes so dried forming a single sheet with particle removal characteristics superior to those of the individual layers.
Claim 69
Dependent Claim
18 words
A process according to claim 63 in which the separate membranes are stripped from the substrate before drying.
Claim 70
Dependent Claim
28 words
A process according to claim 63 in which the separate membranes are dried while supported on the substrate, which thereby becomes an integral part of the multilayer membrane.
Claim 71
Dependent Claim
15 words
A process according to claim 65 in which the substrate is a porous fibrous web.
Claim 72
Dependent Claim
15 words
A process according to claim 66 in which the fibrous web is of polyester resin.
Claim 73
Dependent Claim
15 words
A process according to claim 66 in which the fibrous web is of polypropylene resin.
Claim 74
Dependent Claim
14 words
A process according to claim 64 in which the polyamide resin is polyhexamethylene dodecandiamide.
Claim 75
Dependent Claim
13 words
A process according to claim 64 in which the polyamide resin is poly-11-amino-undecanamide.
Claim 76
Dependent Claim
18 words
A process according to claim 64 in which the membranes are dried under restraint to limit dimensional change.
Claim 77
Dependent Claim
15 words
A process according to claim 64 in which the membranes are corrugated and then dried.
Claim 78
Dependent Claim
82 words
A multilayer liquophilic skinless alcohol-insoluble polyamide resin membrane sheet of alcohol-insoluble hydrophobic polyamide resin, capable when completely immersed in an organic liquid having a surface tension of from about 40 to about 60 dynes/cm of being wetted through within no more than one second, and reverting when heated to a temperature just below the softening temperature of the membrane to a liquophobic material which is no longer wetted by such organic liquids, and having at least two membrane layers integrally adhered together.
Claim 79
Dependent Claim
82 words
A multilayer liquophilic skinless alcohol-insoluble polyamide resin membrane sheet of alcohol-insoluble hydrophobic polyamide resin, capable when completely immersed in an organic liquid having a surface tension of from about 40 to about 60 dynes/cm of being wetted through within no more than one second, and reverting when heated to a temperature just below the softening temperature of the membrane to a liquophobic material which is no longer wetted by such organic liquids, and having at least two membrane layers integrally adhered together.
Claim 80
Dependent Claim
23 words
A multilayer liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 73 in which the membrane layers are supported on a substrate.
Claim 81
Dependent Claim
22 words
A multilayer liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 74 in which the substrate is a porous fibrous web.
Claim 82
Dependent Claim
22 words
A multilayer liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 74 in which the fibrous web is of polyester resin.
Claim 83
Dependent Claim
22 words
A multilayer liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 75 in which the fibrous web is of polypropylene resin.
Claim 84
Dependent Claim
21 words
A multilayer liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 73 in which the polyamide resin is polyhexamethylene dodecandiamide.
Claim 85
Dependent Claim
20 words
A multilayer liquophilic skinless alcohol-insoluble polyamide resin membrane sheet according to claim 73 in which the polyamide resin is poly-11-amino-undecanamide.
References Cited (Backward Citations)
US2783894A
Cited
US3524753A
Cited
US3389206A
Cited
US3457339A
Cited
US3894166A
Cited
US3876738A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-19 | 1986-01-18 | 1986-07-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-19 | 1990-01-18 | 1990-07-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-19 | 1994-01-18 | 1994-07-20 | $7700.00 | Window Closed / Lapsed |