Agglomerate absorbents comprising copper and zinc for sulphur compounds removal

Claim 2

Agglomerates capable of absorbing carbonyl sulphide, mercaptans, and hydrogen sulphide, said agglomerates having a size in the range 1 to 10 mm; a BET surface area of at least 80 m 2 ·g -1 , measured on samples of the agglomerates that have been calcined for 4 hours at 350° C.; a calcined density of not more than 1.5 g·cm -3 ; a porosity of not less than 0.6; and comprising (i) compounds of (a) copper, and (b) zinc and aluminum, said compounds being in the form of at least one compound selected from oxides, hydroxides, carbonates and/or basic carbonates; and (ii) calcium aluminate cement binder; said compounds being in such proportions that the copper atoms form 30-97% of the total number of copper, zinc, and aluminum atoms in said agglomerates; said agglomerates having a total copper and zinc compound content such that, after ignition at 900° C., the cupric oxide plus zinc oxide content of the ignited composition is at least 70% by weight; and said binder constituting 5-10% by weight of said agglomerates.

Claim 3

Agglomerates according to claim 1 containing zinc oxide, hydroxide, carbonate and/or basic carbonate, in such proportions that the zinc atoms constitute 10 to 40% of the total number of copper, zinc, and aluminum atoms in said agglomerates.

Claim 4

Agglomerates according to claim 1 containing at least one aluminum compound in addition to said calcium aluminate binder in such proportions that the total number of aluminum atoms in the agglomerates constitutes 5 to 20% of the total number of copper, zinc, and aluminum atoms.

Claim 5

Agglomerates according to claim 1 containing at least one precipitated aluminum compound intimately mixed with precipitates of said copper and zinc compounds, the aluminum atoms in said at least one precipitated aluminum compound constituting at least 50% of the total aluminum atoms in said agglomerates.

Claim 6

Agglomerates capable of absorbing carbonyl sulphide, mercaptans, and hydrogen sulphide, said agglomerates having a size in the range 1 to 10 mm; a BET surface area of at least 80 m 2 ·g -1 , measured on samples of the agglomerates that have been calcined for 4 hours at 350° C.; a calcined density of not more than 1.5 g·cm -3 ; a porosity of not less than 0.6; and comprising (i) compounds of (a) copper, and (b) zinc and aluminum, said compounds being in the form of at least one compound selected from oxides, hydroxides, carbonates and/or basic carbonates; and (ii) a calcium aluminate cement binder; said compounds being in such proportions that the copper atoms form 30-97% of the total number of copper, zinc, and aluminum atoms in said agglomerates; and said agglomerates having a total copper and zinc compound content such that, after ignition at 900° C., the cupric oxide plus zinc oxide content of the ignited composition is at least 80% by weight and said binder constitutes 5-10% by weight of said agglomerates.

Claim 7

Agglomerates capable of absorbing carbonyl sulphide, mercaptans, and hydrogen sulphide, said agglomerates having a size in the range 1 to 10 mm; a BET surface area of at least 80 m 2 ·g -1 , measured on samples of the agglomerates that have been calcined for 4 hours at 350° C.; a calcined density of not more than 1.5 g·cm -3 ; a porosity of not less than 0.6; and comprising (i) compounds of (a) copper, and (b) zinc and aluminum, said compounds being in the form of at least one compound selected from oxides, hydroxides, carbonates and/or basic carbonates; and (ii) a calcium aluminate cement binder; said compounds being in such proportions that the copper atoms form 30-97% of the total number of copper, zinc, and aluminum atoms in said agglomerates; and said agglomerates having a total copper and zinc compound content such that, after ignition at 900° C., the cupric oxide plus zinc oxide content of the ignited composition is at least 80% by weight and said binder constitutes 5-10% by weight of said agglomerates.

Claim 8

Agglomerates according to claim 5 wherein the copper, and zinc compounds are in the form of at least one compound selected from carbonates and basic carbonates, and porosity is calculated from the mercury density of the agglomerates and the weighted average of the single crystal densities of the components expressed as oxides.

Claim 9

Agglomerates capable of absorbing carbonyl sulphide, mercaptans, and hydrogen sulphide, said agglomerates having a size in the range 1 to 10 mm; a BET surface area of at least 80 m 2 ·g -1 , measured on samples of the agglomerates that have been calcined for 4 hours at 350° C.; a calcined density of not more than 1.5 g·cm -3 ; a porosity of not less than 0.6; and comprising (i) compounds of (a) copper, and (b) zinc and aluminum, said copper and zinc compounds being in the form of carbonates and/or basic carbonates; and said element aluminum being in the form of at least one compound selected from aluminum oxide of aluminum hydroxide; and (ii) a calcium aluminate cement binder; said compounds being in such proportions that the copper atoms form 30-97% of the total number of copper, zinc, and aluminum atoms in said agglomerates; and said agglomerates having a total copper and zinc compound content such that, after ignition at 900° C., the cupric oxide plus zinc oxide content of the ignited composition is at least 70% by weight and said binder constitutes 5-10% by weight of said agglomerates.

Claim 10

Agglomerates capable of absorbing carbonyl sulphide, mercaptans, and hydrogen sulphide, said agglomerates having a size in the range 1 to 10 mm; a BET surface area of at least 80 m 2 ·g -1 , measured on samples of the agglomerates that have been calcined for 4 hours at 350° C.; a calcined density of not more than 1.5 g·cm -3 ; a porosity of not less than 0.6; and comprising (i) compounds of (a) copper, and (b) zinc and aluminum, said copper and zinc compounds being in the form of carbonates and/or basic carbonates; and said element aluminum being in the form of at least one compound selected from aluminum oxide of aluminum hydroxide; and (ii) a calcium aluminate cement binder; said compounds being in such proportions that the copper atoms form 30-97% of the total number of copper, zinc, and aluminum atoms in said agglomerates; and said agglomerates having a total copper and zinc compound content such that, after ignition at 900° C., the cupric oxide plus zinc oxide content of the ignited composition is at least 70% by weight and said binder constitutes 5-10% by weight of said agglomerates.

Claim 11

A process for the manufacture of agglomerates capable of absorbing carbonyl sulphide, mercaptans, and hydrogen sulphide, having a size in the range 1 to 10 mm; a BET surface area of at least 80 m 2 ·g -1 , measured on samples of the agglomerates that have been calcined for 4 hours at 350° C.; a calcined density of not more than 1.5 g·cm -3 ; a porosity of not less than 0.6; said process comprising (i) precipitating compounds of (a) copper, and (b) zinc and aluminum, as hydroxides, carbonates and/or basic carbonates; (ii) mixing said compounds with a calcium aluminate cement binder; and (iii) agglomerating the resultant mixture to form said agglomerates; said compounds being in such proportions that the copper atoms from 30-97% of the total number of copper, zinc, and aluminum atoms in said agglomerates; and said agglomerates having a total copper and zinc compound content such that, after ignition at 90° C., the cupric oxide plus zinc oxide content of the ignited composition is at least 70% by weight and said binder constitutes 5-10% by weight of said agglomerates.

Claim 12

A process for the manufacture of agglomerates capable of absorbing carbonyl sulphide, mercaptans, and hydrogen sulphide, having a size in the range 1 to 10 mm; a BET surface area of at least 80 m 2 ·g -1 , measured on samples of the agglomerates that have been calcined for 4 hours at 350° C.; a calcined density of not more than 1.5 g·cm -3 ; a porosity of not less than 0.6; said process comprising (i) precipitating compounds of (a) copper, and (b) zinc and aluminum, as hydroxides, carbonates and/or basic carbonates; (ii) mixing said compounds with a calcium aluminate cement binder; and (iii) agglomerating the resultant mixture to form said agglomerates; said compounds being in such proportions that the copper atoms from 30-97% of the total number of copper, zinc, and aluminum atoms in said agglomerates; and said agglomerates having a total copper and zinc compound content such that, after ignition at 90° C., the cupric oxide plus zinc oxide content of the ignited composition is at least 70% by weight and said binder constitutes 5-10% by weight of said agglomerates.