Method for coating a substrate with an electrically conductive layer
Assignee: Saint Gobain Vitrage SA
•
Filing: 1986-01-22
•
Granted: 1989-08-22
•
Expires: 2006-01-22
Abstract
Abstract A method for coating a substrate, preferably of glass, with a pyrolyzed transparent, electroconductive layer. The coating is comprised of indium formate, optionally mixed with a powdered or gaseous tin compound or a gaseous organotin compound. The coating layer is deposited upon a hot substrate whereupon it pyrolytically decomposes, forming a layer which is subsequently heat treated in a reducing or an oxidizing atmosphere to optionally enhance the low emissivity and low resistivity of the coating or reduce said low emissivity and low resistivity properties.
Inventors
- 👤 Vincent Sauvinet
- 👤 Jean Bletry
- 👤 Micheline Bonnaud
- 👤 Maurice Trouve
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 08:21
CPC Classifications
H; H10; H10F; H10F71/00; H10F71/138; C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/25; C07; C07C; C07C51/00; C07C51/41; C07C51/412; C07C53/00; C07C53/02; C07C53/06; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/215; C03C2217/23; C03C2217/231; C03C2218/00; C03C2218/10; C03C2218/11; C03C2218/112; C03C2218/17; Y; Y02; Y02E; Y02E10/00; Y02E10/50
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
55 words
A method for coating a substrate with a pyrolyzed metal oxide coating which comprises depositing a predetermined amount of dry indium formate of the formula In (HCOO) 3 upon a surface of a heated substrate so as to pyrolyze said indium formate and form a coating of indium oxide upon the surface of the substrate.
Claim 2
Independent Claim
55 words
A method for coating a substrate with a pyrolyzed metal oxide coating which comprises depositing a predetermined amount of dry indium formate of the formula In (HCOO) 3 upon a surface of a heated substrate so as to pyrolyze said indium formate and form a coating of indium oxide upon the surface of the substrate.
Claim 3
Dependent Claim
14 words
The method of claim 1 wherein the indium formate is deposited as a powder.
Claim 4
Dependent Claim
23 words
The method of claim 1 which further comprises selecting the substrate from the group consisting of glass, metal, ceramic and other refractory materials.
Claim 5
Dependent Claim
31 words
The method of claim 3 wherein said glass substrate is heated to a temperature below about 650°-700° C. prior to the deposition of indium formate upon the surface of the substrate.
Claim 6
Dependent Claim
42 words
The method of claim 1 which further comprises mixing the indium formate with at least one compound having a decomposition temperature on the same order as that of indium formate prior to depositing the mixture onto the surface of the heated substrate.
Claim 7
Dependent Claim
24 words
The method of claim 5 wherein the compound is selected from the group consisting of powdered or gaseous tin compounds and gaseous organotin compounds.
Claim 8
Dependent Claim
22 words
The method of claim 6 wherein the powdered tin compounds are selected from the group consisting of dibutyltin oxide and dibutyltin fluoride.
Claim 9
Dependent Claim
28 words
The method of claim 7 wherein the powdered tin compounds are mixed with the indium formate in proportions ranging from about one to about thirty percent by weight.
Claim 10
Dependent Claim
14 words
The method of claim 6 wherein the gaseous tin compound is SnCl 4 .
Claim 11
Dependent Claim
14 words
The method of claim 6 wherein the gaseous organotin compound is BuSnCl 3 .
Claim 12
Independent Claim
59 words
A method for forming a transparent electroconductive coating on a substrate which comprises. preparing a dry metal composition containing indium formate of the formula In (HCOO) 3 ; depositing said composition onto a surface of a heated substrate with coating means so as to pyrolyze the composition; and heating the coated substrate to enhance the properties of the layer.
Claim 13
Independent Claim
59 words
A method for forming a transparent electroconductive coating on a substrate which comprises. preparing a dry metal composition containing indium formate of the formula In (HCOO) 3 ; depositing said composition onto a surface of a heated substrate with coating means so as to pyrolyze the composition; and heating the coated substrate to enhance the properties of the layer.
Claim 14
Dependent Claim
35 words
The method of claim 11 which further comprises mixing at least a powdered or gaseous tin compound or a gaseous organotin compound with the indium formate prior to depositing the metal composition upon the substrate.
Claim 15
Dependent Claim
22 words
The method of claim 12 wherein the powdered tin compounds are selected from the group consisting of dibutyltin oxide and dibutyltin fluoride.
Claim 16
Dependent Claim
28 words
The method of claim 13 wherein the powdered tin compounds are mixed with the indium formate in amounts ranging from about one to about 30 percent by weight.
Claim 17
Dependent Claim
14 words
The method of claim 12 wherein the gaseous tin compound is SnCl 4 .
Claim 18
Dependent Claim
14 words
The method of claim 12 wherein the gaseous organotin compound is BuSnCl 3 .
Claim 19
Dependent Claim
16 words
The method of claim 12 wherein the mixture is deposited upon the substrate as a powder.
Claim 20
Dependent Claim
28 words
The method of claim 17 which further comprises suspending the powdered mixture in a stream of carrier gas prior to depositing it onto the surface of the substrate.
Claim 21
Dependent Claim
53 words
The method of claim 12 wherein the coated substrate is heated by maintaining said substrate in a heated enclosure at a temperature of at least about 300° C. in a reducing atmosphere for a predetermined time period to enhance the properties of the layer and to form a metal coating upon the substrate.
Claim 22
Dependent Claim
50 words
The method of claim 12 wherein the coated substrate is heated by maintaining said substrate in a heated enclosure at a temperature of at least about 300° C. in an oxidizing atmosphere to form a metal oxide coating upon the substrate with modified properties compared with the coating as deposited.
Claim 23
Dependent Claim
31 words
The method of claim 12 wherein the substrate is heated by subjecting a coated side of the substrate to an intense heating for a period of less than about one second.
Claim 24
Dependent Claim
23 words
The method of claim 12 wherein the heat treatment may be performed upon the coated substrate on the line for manufacturing coated glass.
Claim 25
Dependent Claim
24 words
The method of claim 12 wherein a coated glass substrate is tempered or laminated prior to subjecting the coated substrate to a heat treatment.
Claim 26
Dependent Claim
30 words
The method of claim 21 wherein preselected areas of the coating are exposed to different degrees of heating so as to obtain a coating layer having portions with different properties.
Claim 27
Dependent Claim
42 words
The method of claim 21, wherein the substrate is heated by subjecting a coated side of the substrate to the flame of at least one burner fed with gas either reducing or oxidizing according to the either reducing or oxidizing treatment desired.
Claim 28
Independent Claim
93 words
A method for coating a substrate with a pyrolyzed metal oxide coating which comprises: reacting an indium compound with an inorganic acid to form an indium salt; reacting the indium salt with ammonia to form an indium hydroxide precipate; reacting the precipitate with formic acid to obtain indium formate; depositing a predetermined amount of said indium formate in dry form upon the surface of a heated substrate so as to pyrolyze said indium formate of the formula In (HCOO) 3 and form a coating of indium oxide upon the surface of said substrate.
Claim 29
Independent Claim
93 words
A method for coating a substrate with a pyrolyzed metal oxide coating which comprises: reacting an indium compound with an inorganic acid to form an indium salt; reacting the indium salt with ammonia to form an indium hydroxide precipate; reacting the precipitate with formic acid to obtain indium formate; depositing a predetermined amount of said indium formate in dry form upon the surface of a heated substrate so as to pyrolyze said indium formate of the formula In (HCOO) 3 and form a coating of indium oxide upon the surface of said substrate.
References Cited (Backward Citations)
US3676729A
Cited
US3666534A
Cited
SU454198A1
Cited
US3949259A
Cited
US4172159A
Cited
US4252841A
Cited
US4263335A
Cited
US4303554A
Cited
US4325988A
Cited
US4344986A
Cited
US4374156A
Cited
US4533571A
Cited
US4562095A
Cited
US4547400A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-08-21 | 1993-02-20 | 1993-08-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-08-21 | 1997-02-20 | 1997-08-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-08-21 | 2001-02-20 | 2001-08-22 | $7700.00 | Window Closed / Lapsed |