Process for coating a glass sheet with a semi-reflective film of tin oxide
Assignee: Saint Gobain Industries SA
•
Filing: 1978-02-16
•
Granted: 1979-10-23
•
Expires: 1998-02-16
Abstract
Abstract The surface of a transparent refractory material such as glass or a vitreous ceramic is coated with a semi-reflective film of tin oxide by projecting finely divided particles of a pyrolytically decomposable organotin compound against the surface of the substrate material that has been heated to a temperature of between about 400° and 650° C. The finely divided organotin compound has a particle size of not greater than about 20 microns and is suspended in an anhydrous carrier gas to which carrier gas has been added a gaseous fluoride compound. In an advantageous embodiment of the process the pyrolytically decomposable organotin compound is dibutyl tin oxide, the carrier gas is dry air and the added fluoride compound is dry hydrogen fluoride.
Inventors
- 👤 Jeannik Marcault
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 00:25
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/211; C03C2218/00; C03C2218/10; C03C2218/17
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
148 words
A process for forming a semi-reflective coating of tin oxide on the surface of a transparent refractory substrate material which comprises: heating the substrate material to a temperature of from about 400° to 650° C.; projecting onto the surface of the hot substrate material finely divided particles of a pyrolytically decomposable organotin compound suspended in an anhydrous carrier gas; said finely divided organotin compound having a particle size of not greater than about 20 microns, and said compound being a solid at ambient temperature and being pyrolytically decomposable at a temperature below that of the hot substrate material against the surface of which the organotin compound is projected; and said anhydrous carrier gas containing a gaseous inorganic fluoride compound; whereby said organotin compound pyrolytically decomposes as it impinges against the surface of the hot substrate material to form the aforesaid adherent coating of tin oxide on said surface.
Claim 2
Dependent Claim
148 words
A process for forming a semi-reflective coating of tin oxide on the surface of a transparent refractory substrate material which comprises: heating the substrate material to a temperature of from about 400° to 650° C.; projecting onto the surface of the hot substrate material finely divided particles of a pyrolytically decomposable organotin compound suspended in an anhydrous carrier gas; said finely divided organotin compound having a particle size of not greater than about 20 microns, and said compound being a solid at ambient temperature and being pyrolytically decomposable at a temperature below that of the hot substrate material against the surface of which the organotin compound is projected; and said anhydrous carrier gas containing a gaseous inorganic fluoride compound; whereby said organotin compound pyrolytically decomposes as it impinges against the surface of the hot substrate material to form the aforesaid adherent coating of tin oxide on said surface.
Claim 3
Dependent Claim
14 words
The process according to claim 1 in which the organotin compound is dibutyltin oxide.
Claim 4
Dependent Claim
34 words
The process according to claim 1 in which the gaseous fluoride compound is selected from the group consisting of boron trifluoride, bromine pentafluoride, chlorine trifluoride, silicon tetrafluoride, tungsten hexafluoride, molybdenum hexafluoride and hydrogen fluoride.
Claim 5
Dependent Claim
16 words
The process according to claim 1 in which the gaseous fluoride compound is anhydrous hydrofluoric acid.
Claim 6
Dependent Claim
21 words
The process according to claim 4 in which the organotin compound is dibutyltin oxide and the carrier gas is dry air.
Claim 7
Dependent Claim
49 words
The process according to claim 1 in which the gaseous fluoride compound is introduced into the anhydrous carrier gas at a point upstream from the point at which the particles of the organotin compound suspended in said carrier gas are projected against the surface of the hot substrate material.
Claim 8
Dependent Claim
35 words
The process according to claim 1 in which the substrate material is a thermally tempered or chemically reinforced glass sheet and in which the temperature of the substrate material does not exceed about 520° C.
References Cited (Backward Citations)
US2566346A
Cited
US2567331A
Cited
FR1217676A
Cited
FR1226725A
Cited
FR1293545A
Cited
US3762902A
Cited
FR2153044A1
Cited
US3759743A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-22 | 1983-04-23 | 1983-10-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-22 | 1987-04-23 | 1987-10-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-22 | 1991-04-23 | 1991-10-23 | $7700.00 | Window Closed / Lapsed |