Topcoat composition and method

Claim 2

A topcoat paste for improving the wear resistance of asphalt concrete surfaces, which is cured under atmospheric conditions, comprising the combination of: a dry mix material, the dry mix material comprising sand, cement, and a resinous cellulosic binder, the ratio of sand to cement being between about 1:1 and about 4:1, by weight; and, a liquid mix material, the liquid mix material comprising water, styrene acrylate monomer, and a solvent for at least one of the styrene acrylate monomer and the resinous binder, the ratio of water to styrene acrylate monomer being between about 1:2 and about 6:1, by volume, the ratio of said dry mix material to said liquid mix material being about 50 pounds of said dry mix material to between about one and about three gallons of said liquid mix material, whereby said composition when applied to a cement or asphalt concrete surface improves the resistance of said surface to cracking, water permeability and chemical degradation.

Claim 3

The topcoat paste of claim 1, wherein the ratio of sand to cement is about 2:1, by weight.

Claim 4

The topcoat paste of claim 1, wherein the ratio of water to styrene acrylate monomer is about 3:1, by volume.

Claim 5

The topcoat paste of claim 1, wherein the ratio of said dry mix material to said liquid mix material is about 50 pounds of said dry mix material to about two gallons of said liquid mix material.

Claim 6

The topcoat paste of claim 1, wherein said cement is portland cement.

Claim 7

The topcoat paste of claim 1, wherein said cellulosic binder is a hydroxyalkyl cellulose.

Claim 8

The topcoat paste of claim 6, wherein said hydroxyalkyl cellulose is hydroxyethyl cellulose.

Claim 9

The topcoat paste of claim 1, wherein said solvent for said styrene acrylate monomer and said resinous binder is ethylene glycol butyl ether.

Claim 10

The topcoat paste of claim 1, further comprising at least one additive selected from the group consisting of defoaming agents, preservatives, and fungicides.

Claim 11

The topcoat past of claim 1, wherein said defoaming agent is a vegetable oil.

Claim 12

A topcoat paste composition for improving the wear resistance of asphalt concrete surfaces which is cured under atmospheric conditions, comprising the combination of: a dry mix material, the dry mix material comprising sand, cement, and a resinous cellulosic binder, the ratio of sand to cement being between about 1:1 and about 4:1, by weight; and, a liquid mix material, the liquid mix material comprising water, at least one of the group consisting of vinyl acrylate monomers and vinyl methacrylate monomers, the ratio of water to said vinyl acrylate monomers and vinyl methacrylate monomers being between about 1:2 and about 6:1, by volume, and a solvent for at least one of the vinyl acrylate monomers and vinyl methacrylate monomers, and said resinous binder, the ratio of said dry mix material to said liquid mix material being about 50 pounds of said dry mix material to between about 1 and about 3 gallons of said liquid mix material, whereby said composition when applied to a cement or asphalt concrete surface and will improves the resistance of said surface to cracking, water permeability and chemical degradation.

Claim 13

A topcoat paste composition for improving the wear resistance of asphalt concrete surfaces which is cured under atmospheric conditions, comprising the combination of: a dry mix material, the dry mix material comprising sand, cement, and a resinous cellulosic binder, the ratio of sand to cement being between about 1:1 and about 4:1, by weight; and, a liquid mix material, the liquid mix material comprising water, at least one of the group consisting of vinyl acrylate monomers and vinyl methacrylate monomers, the ratio of water to said vinyl acrylate monomers and vinyl methacrylate monomers being between about 1:2 and about 6:1, by volume, and a solvent for at least one of the vinyl acrylate monomers and vinyl methacrylate monomers, and said resinous binder, the ratio of said dry mix material to said liquid mix material being about 50 pounds of said dry mix material to between about 1 and about 3 gallons of said liquid mix material, whereby said composition when applied to a cement or asphalt concrete surface and will improves the resistance of said surface to cracking, water permeability and chemical degradation.

Claim 14

The topcoat paste composition of claim 11, wherein the ratio of sand to cement is about 2:1, by weight.

Claim 15

The topcoat paste composition of claim 11, wherein the ratio of water to said vinyl acrylate monomers and vinyl methacrylate monomers is about 3:1, by volume.

Claim 16

The topcoat paste composition of claim 11, wherein the ratio of said dry mix material to said liquid mix material is about 50 pounds of said dry mix material to about two gallons of said liquid mix material.

Claim 17

The topcoat paste composition of claim 11, wherein said cement is portland cement.

Claim 18

The topcoat paste composition of claim 11, wherein said cellulosic binder is a hydroxyalkyl cellulose.

Claim 19

The topcoat composition of claim 16, wherein said hydroxyalkyl cellulose is hydroxyethyl cellulose.

Claim 20

The topcoat paste composition of claim 11, wherein said solvent for at least one of said vinyl acrylate monomers and vinyl methacrylate monomers, and said cellulosic binder, is ethylene glycol butyl ether.

Claim 21

The topcoat paste composition of claim 11, further comprising at least one additive selected from the group consisting of defoaming agents, preservatives and fungicides.

Claim 22

A topcoat paste composition for improving the wear resistance of asphalt concrete surfaces, which is cured under atmospheric conditions, comprising the combination of: a dry mix material comprising about 67.9% silica sand, about 31.9% portland cement, and about 0.2% hydroxyethyl cellulose by weight; and, a liquid mix material comprising, by volume, about 24.2% styrene acrylate monomer, about 1.4% ethylene glycol butyl ether, and about 74.1% water, the balance consisting of an agent selected from the group consisting of preservatives, fungicides, and defoaming agents.

Claim 23

A topcoat paste composition for improving the wear resistance of asphalt concrete surfaces, which is cured under atmospheric conditions, comprising the combination of: a dry mix material comprising about 67.9% silica sand, about 31.9% portland cement, and about 0.2% hydroxyethyl cellulose by weight; and, a liquid mix material comprising, by volume, about 24.2% styrene acrylate monomer, about 1.4% ethylene glycol butyl ether, and about 74.1% water, the balance consisting of an agent selected from the group consisting of preservatives, fungicides, and defoaming agents.