Abradable article, and powder and method for making
Assignee: General Electric Co
•
Filing: 1986-11-28
•
Granted: 1989-06-27
•
Expires: 2006-11-28
Abstract
Abstract A mixture of two powdered alloys of the M, Cr, Al type, M being Co and/or Ni, is disclosed, in one form, for use in providing an abradable surface of an article and is characterized by the substantial absence of B. The first alloy has substantially no Si and has a higher melting range than that of the second alloy. The second alloy has substantially no Y and consists essentially of, by weight, 8-12% Si, 1.5-4% Al, 10-30% Cr, with the balance M and incidiental impurities. The total mixture composition consists essentially of, by weight, 10-35% Cr, 4-10% Al, from a small but effective amount up to about 0.09% Y, 2-6% Si, with the balance M and incidental impurities.
Inventors
- 👤 Roger J. Perkins
- 👤 Murray S. Smith, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:35
CPC Classifications
B; B22; B22F; B22F7/00; B22F7/06; B22F7/062; B22F1/00; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/30; B23K35/3046; C; C22; C22C; C22C1/00; C22C1/04; C22C1/0433; B22F2007/068; B22F2998/00; B22F2998/10; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12063
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
192 words
A mixture of two powdered alloys each comprising a base of elements M, Cr and Al in which M is at least one element selected from the group consisting of Co and Ni, the mixture having a total mixture composition consisting essentially of, by weight, 10-35% Cr, 4-10% Al, from a small but effective amount up to about 0.09% Y, 2-6% Si, with the balance M and incidental impurities, and further characterized by the substantial absence of B; a first of the powdered alloys having a solidus and a liquidus, consisting of 50-70 wt % of the mixture and having a melting range higher than a second of the powdered alloys; the first alloy characterized by the substantial absence of Si and the presence of Y in an amount, up to 0.15 wt %, which will provide the Y content in the total mixture composition; the second of the powdered alloys having a solidus and a liquidus, consisting essentially of the balance of the mixture, being characterized by the substantial absence of Y, and consisting essentially of, by weight, 8-12% Si, 1.5-4% Al, 10-30% Cr, with the balance M and incidental impurities.
Claim 2
Dependent Claim
192 words
A mixture of two powdered alloys each comprising a base of elements M, Cr and Al in which M is at least one element selected from the group consisting of Co and Ni, the mixture having a total mixture composition consisting essentially of, by weight, 10-35% Cr, 4-10% Al, from a small but effective amount up to about 0.09% Y, 2-6% Si, with the balance M and incidental impurities, and further characterized by the substantial absence of B; a first of the powdered alloys having a solidus and a liquidus, consisting of 50-70 wt % of the mixture and having a melting range higher than a second of the powdered alloys; the first alloy characterized by the substantial absence of Si and the presence of Y in an amount, up to 0.15 wt %, which will provide the Y content in the total mixture composition; the second of the powdered alloys having a solidus and a liquidus, consisting essentially of the balance of the mixture, being characterized by the substantial absence of Y, and consisting essentially of, by weight, 8-12% Si, 1.5-4% Al, 10-30% Cr, with the balance M and incidental impurities.
Claim 3
Dependent Claim
90 words
The mixture of claim 1 in which the total mixture composition consists essentially of, by weight, 20-25% Cr, 6-8% Al, 0.02-0.09% Y, 2-4% Si, with the balance M; the first of the powdered alloys consists essentially of, by weight, 20-25% Cr, 8-10% al, 0.05-0.15% Y, with the balance M and further characterized by the absence of Si; and the second of the powdered alloys consists essentially of, by weight, 15-20% Cr, 2-4% Al, 8-11% Si, with the balance M and incidental impurities and further characterized by the absence of Y.
Claim 4
Dependent Claim
102 words
The mixture of claim 2 in which the total mixture composition consists essentially of, by weight, 20-35% Ni, 20-25% Cr, 6.5-8% Al, 0.04-0.09% Y, 2.5-3.5% Si, with the balance Co and incidental impurities; the first of the powdered alloys consists essentially of, by weight, 15-35% Ni, 20-25% Cr, 8-10% Al, 0.05-0.15% Y, with the balance Co and incidental impurities and further characterized by the absence of Si; and the second of the powdered alloys consists essentially of, by weight, 13-30% Co, 18-20% Cr, 2-4% Al, 8-12% Si with the balance Ni and incidental impurities and further characterized by the absence of Y.
Claim 5
Dependent Claim
99 words
The mixture of claim 3 in which the total mixture composition consists essentially of, by weight, 25-35% Ni, 20-25% Cr, 7-8% Al, 0.05-0.09% Y, 3-3.5% Si, with the balance Co and incidental impurities; the first of the powdered alloys consists essentially of, by weight, 15-35% Ni, 20-25% Cr, 8-10% Al, 0.05-0.15% Y, with the balance Co and incidental impurities and further characterized by the absence of Si; and the second of the powdered alloys consists essentially of, by weight, 25-30% Co, 18-20% Cr, 3-4% Al, 9.5-10.5% Si with the balance Ni and incidental impurities in the absence of Y.
Claim 6
Dependent Claim
43 words
An improved powdered brazing alloy characterized by the substantial absence of Y and consisting essentially of, by weight, 8-12% Si, 1.5-4% Al, 10-30% Cr with the balance at least one element selected from the group consisting of Co and Ni, and incidental impurities.
Claim 7
Dependent Claim
43 words
An improved powdered brazing alloy characterized by the substantial absence of Y and consisting essentially of, by weight, 8-12% Si, 1.5-4% Al, 10-30% Cr with the balance at least one element selected from the group consisting of Co and Ni, and incidental impurities.
Claim 8
Dependent Claim
17 words
The alloy of claim 5 in which Cr is 15-20%, Al is 2-4% and Si is 8-11%.
Claim 9
Dependent Claim
25 words
The alloy of claim 6 consisting essentially of, by weight, 18-20% Cr, 2-4% Al, 8-11% Si, 13-30% Co, with a balance Ni and incidental impurities.
Claim 10
Dependent Claim
27 words
The alloy of claim 7 in which the Cr is 18-20%, Al is 3-4%, Si is 9.5-10.5%, Co is 25-30% with a balance Ni and incidental impurities.
Claim 11
Dependent Claim
68 words
An article including an environmentally resistant, abradable surface portion comprising: an inner portion of a superalloy selected from a group consisting of Co-base and Ni-base superalloys and having an incipient melting temperature; and an outer portion metallurgically bonded with the inner portion, and consolidated and liquid phase sintered from the mixture of claim 1; the outer portion having a thickness in the range of at least about 0.05".
Claim 12
Dependent Claim
42 words
The article of claim 9 in the form of a turbine shroud in which: the outer portion is consolidated and liquid phase sintered from the mixture of claim 2; and the outer portion has a thickness in the range of about 0.08-0.15".
Claim 13
Dependent Claim
19 words
The article of claim 10 in which the outer portion has an apparent density of at least about 99%.
References Cited (Backward Citations)
US3073269A
Cited
US3155491A
Cited
US3342563A
Cited
US3383207A
Cited
US3676085A
Cited
US3838981A
Cited
US4022587A
Cited
US3928026A
Cited
US3964877A
Cited
US4093454A
Cited
US4034142A
Cited
US4080204A
Cited
US4614296A
Cited
US4381944A
Cited
US4497669A
Cited
US4613368A
Cited
US4676829A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-06-26 | 1992-12-26 | 1993-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-06-26 | 1996-12-26 | 1997-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-06-26 | 2000-12-26 | 2001-06-27 | $7700.00 | Window Closed / Lapsed |