Diffusion brazing process for pieces of superalloys
Assignee: Safran Aircraft Engines SAS
•
Filing: 1985-03-05
•
Granted: 1986-09-30
•
Expires: 2005-03-05
Abstract
Abstract A diffusion brazing process for superalloy parts is performed on the one hand by the interposition between the pieces to be joined of a joining layer having a composition close to that of the parts and containing a "fluxing" element, which renders it more readily meltable, and on the other hand, a heat treatment effecting the brazing by the melting of the joining layer and its resolidification, by the diffusion of the flux. The process of the invention is characterized, particularly in view of permitting the use of a joining layer of a greater thickness than that of the layers used in the known diffusion brazing processes, in that said joining layer consists of a mixture of a superalloy powder and an alloy powder containing the flux.
Inventors
- 👤 Jacques Lesgourgues
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:04
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/30; B23K35/3033; B22; B22F; B22F1/00; B22F1/09; B22F7/00; B22F7/06; B22F7/062; B22F7/064
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
174 words
A process for diffusion brazing a layer of material between faces defined by an article formed by nickel or cobalt base superalloys comprising the steps of: (a) forming the layer of material from a mixture having properties identical to the superalloys and formed of at least two alloy powders in appreciably unequal proportions, the two alloy powders comprising (i) a base powder of NK17CDAT (Astroloy) forming approximately 75% by weight of the mixture and (ii) an addition powder forming approximately 25% by weight of the mixture, the addition powder being a Ni B Cr alloy such that the liquidus temperature of the addition powder is lower than the solidus temperature of the base powder and the article; (b) placing the layer of material between the faces of the article; (c) heating the assembly to a temperature sufficient to melt the addition powder, but not the base powder or the article, the melted addition powder being retained in the base powder by capillary action; and, (d) subjecting the assembly to a diffusion brazing heat treatment.
Claim 2
Dependent Claim
174 words
A process for diffusion brazing a layer of material between faces defined by an article formed by nickel or cobalt base superalloys comprising the steps of: (a) forming the layer of material from a mixture having properties identical to the superalloys and formed of at least two alloy powders in appreciably unequal proportions, the two alloy powders comprising (i) a base powder of NK17CDAT (Astroloy) forming approximately 75% by weight of the mixture and (ii) an addition powder forming approximately 25% by weight of the mixture, the addition powder being a Ni B Cr alloy such that the liquidus temperature of the addition powder is lower than the solidus temperature of the base powder and the article; (b) placing the layer of material between the faces of the article; (c) heating the assembly to a temperature sufficient to melt the addition powder, but not the base powder or the article, the melted addition powder being retained in the base powder by capillary action; and, (d) subjecting the assembly to a diffusion brazing heat treatment.
Claim 3
Dependent Claim
21 words
The process according to claim 1 wherein the addition powder alloy comprises approximately 15% Cr, 3.5% B and the rest Ni.
Claim 4
Dependent Claim
32 words
The process according to claim 2 wherein the base powder has a grain size of less than 100 microns and the alloy powder has a grain size of less than 40 microns.
Claim 5
Dependent Claim
13 words
The process according to claim 3 wherein the superalloy comprises NK15CADT (Rene 77).
Claim 6
Dependent Claim
68 words
The process according to claim 3 wherein the diffusion brazing treatment comprises: (a) heating the assembly for approximately 3 hours to 1200° C.; (b) holding the temperature at 1200° C. for approximately 12 minutes; (c) reducing the temperature to approximately 1190° C. and holding at this temperature for approximately 2 hours; and, (d) lowering the temperature in approximately 2 hours from approximately 1190° C. to approximately 540° C.
Claim 7
Dependent Claim
176 words
A process for diffusion brazing a layer of material between faces defined by an article formed by nickel or cobalt base superalloys comprising the steps of: (a) forming the layer of material from a mixture having properties identical to the superalloys and formed of at least two alloy powders in appreciabely unequal proportions, the two alloy powders comprising (i) a base powder of NK17CDAT (Astroloy) forming approximately 75% by weight of the mixture and (ii) an addition powder forming approximately 25% by weight of the mixture, the addition powder being an alloy of Ni Co Si B, such that the liquidus temperature of the addition powder is lower than the solidus temperature of the base powder and the article; (b) placing the layer of material between the faces of the article; (c) heating the assembly to a temperature sufficient to melt the addition powder, but not the base powder or the article, the melted addition powder being retained in the base powder by capillary action; and, (d) subjecting the assembly to a diffusion brazing heat treatment.
Claim 8
Dependent Claim
176 words
A process for diffusion brazing a layer of material between faces defined by an article formed by nickel or cobalt base superalloys comprising the steps of: (a) forming the layer of material from a mixture having properties identical to the superalloys and formed of at least two alloy powders in appreciabely unequal proportions, the two alloy powders comprising (i) a base powder of NK17CDAT (Astroloy) forming approximately 75% by weight of the mixture and (ii) an addition powder forming approximately 25% by weight of the mixture, the addition powder being an alloy of Ni Co Si B, such that the liquidus temperature of the addition powder is lower than the solidus temperature of the base powder and the article; (b) placing the layer of material between the faces of the article; (c) heating the assembly to a temperature sufficient to melt the addition powder, but not the base powder or the article, the melted addition powder being retained in the base powder by capillary action; and, (d) subjecting the assembly to a diffusion brazing heat treatment.
Claim 9
Dependent Claim
25 words
The process according to claim 6 wherein the addition powder comprises an alloy having approximately 17% Co, 4% Si, 2.7% B and the rest Ni.
Claim 10
Dependent Claim
32 words
The process according to claim 7 wherein the base powder has a grain size of less than 160 microns and the addition powder has a grain size of less than 40 microns.
References Cited (Backward Citations)
US2714760A
Cited
FR1218005A
Cited
US3108861A
Cited
US3496630A
Cited
US3574924A
Cited
US3692501A
Cited
US3678570A
Cited
FR2132050A1
Cited
FR2192889A1
Cited
FR2296491A1
Cited
US4008844A
Cited
US4005988A
Cited
US4299629A
Cited
US4285459A
Cited
US4381944A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-09-29 | 1990-03-31 | 1990-09-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-09-29 | 1994-03-31 | 1994-09-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-09-29 | 1998-03-31 | 1998-09-30 | $7700.00 | Window Closed / Lapsed |