Interlayer for transient liquid phase diffusion bonding
Assignee: RTX Corp
•
Filing: 1975-12-19
•
Granted: 1977-02-01
•
Expires: 1995-12-19
Abstract
Abstract A reduced melting point interlayer for transient liquid phase diffusion bonding of the nickel, cobalt and iron alloys is provided as a thin coating integral with one or more of the surfaces to be joined.
Inventors
- 👤 Daniel Francis Paulonis
- 👤 David Scott Duvall
- 👤 Gerard Casimer Sikorowicz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 08:58
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/001; B23K35/004; B23K20/00; B23K20/22; B23K20/233; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/923; Y10S428/924; Y10S428/926; Y10S428/9335; Y10S428/941; Y10T; Y10T428/00; Y10T428/12; Y10T428/12222; Y10T428/12493; Y10T428/12736; Y10T428/1275; Y10T428/12771; Y10T428/12806; Y10T428/12812; Y10T428/12826; Y10T428/12847; Y10T428/12854
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
87 words
A diffusion bonding assembly which comprises: two superalloy substrates having matched surface portions to be joined; a thin interlayer sandwiched between the surfaces, said interlayer comprising at least one coating bonded to at least one of the substrate surfaces to be joined; the overall interlayer composition having as its basis metal the same base metal as the superalloys and, containing a high boron content, having a melting temperature below that of the superalloys and a melting temperature below that causing irreversible adverse metallurgical change in the substrates.
Claim 2
Dependent Claim
87 words
A diffusion bonding assembly which comprises: two superalloy substrates having matched surface portions to be joined; a thin interlayer sandwiched between the surfaces, said interlayer comprising at least one coating bonded to at least one of the substrate surfaces to be joined; the overall interlayer composition having as its basis metal the same base metal as the superalloys and, containing a high boron content, having a melting temperature below that of the superalloys and a melting temperature below that causing irreversible adverse metallurgical change in the substrates.
Claim 3
Dependent Claim
77 words
The assembly according to claim 1 wherein the interlayer coating comprises a first layer on at least one substrate surface and a second distinct layer thereover and in intimate atomic contact with the first layer, one layer having as its basis the basis metal of the interlayer and another layer having as its basis another element of the superalloys, at least one of the layers having a high boron content providing a substantial melting temperature depressant effect.
Claim 4
Dependent Claim
22 words
The assembly according to claim 1 wherein: the superalloys are selected from the group consisting of the nickel-base, cobalt-base or iron-base superalloys.
Claim 5
Dependent Claim
16 words
The assembly according to claim 2 wherein: one of the layers of the interlayer is chromium.
Claim 6
Dependent Claim
79 words
A diffusion bonding assembly which comprises: two nickel-base superalloy substrates having matched surfaces to be joined; a thin, lamellar interlayer sandwiched between the surfaces; the overall interlayer composition being a nickel-base alloy having a melting point below that of the superalloy and below that causing irreversible, adverse metallurgical change in the superalloy; the interlayer comprising at least one layer of chromium and at least one layer of a nickel boron alloy on the surface of at least one substrate.
Claim 7
Dependent Claim
79 words
A diffusion bonding assembly which comprises: two nickel-base superalloy substrates having matched surfaces to be joined; a thin, lamellar interlayer sandwiched between the surfaces; the overall interlayer composition being a nickel-base alloy having a melting point below that of the superalloy and below that causing irreversible, adverse metallurgical change in the superalloy; the interlayer comprising at least one layer of chromium and at least one layer of a nickel boron alloy on the surface of at least one substrate.
Claim 8
Dependent Claim
18 words
The assembly according to claim 5 wherein: the melting point of the overall interlayer is about 2000° F.
Claim 9
Dependent Claim
18 words
The assembly according to claim 5 wherein: the interlayer thickness is about 0.0005 to 0.01 inch in thickness.
Claim 10
Dependent Claim
17 words
The assembly according to claim 7 wherein: the overall interlayer boron content is about 1-4 weight percent.
Claim 11
Dependent Claim
24 words
The assembly according to claim 7 wherein: the chromium content of the overall interlayer is about the same percentage as that of the superalloy.
Claim 12
Dependent Claim
89 words
A diffusion bonding assembly which comprises: two superalloy substrates having surfaces to be joined; a thin, lamellar interlayer sandwiched between the surfaces; the overall interlayer composition having as its basis metal the same basis metal as the superalloy, a melting point below that of the superalloy and a melting temperature below that causing irreversible adverse metallurgical change in the superalloy; the interlayer comprising a first layer of chromium on the surface of each substrate and a thin layer therebetween consisting of the basis metal containing a high boron content.
Claim 13
Dependent Claim
89 words
A diffusion bonding assembly which comprises: two superalloy substrates having surfaces to be joined; a thin, lamellar interlayer sandwiched between the surfaces; the overall interlayer composition having as its basis metal the same basis metal as the superalloy, a melting point below that of the superalloy and a melting temperature below that causing irreversible adverse metallurgical change in the superalloy; the interlayer comprising a first layer of chromium on the surface of each substrate and a thin layer therebetween consisting of the basis metal containing a high boron content.
Claim 14
Dependent Claim
26 words
The assembly according to claim 10 wherein: the overall interlayer boron content is about 2-3 weight percent; and the chromium content approximates that of the substrates.
Claim 15
Dependent Claim
32 words
The assembly according to claim 11 wherein: the interlayer contains one or more additional layers comprising at least one metal selected from the group consisting of tungsten, molybdenum, tantalum, hafnium and aluminum.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-01 | 1980-08-02 | 1981-02-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-01 | 1984-08-02 | 1985-02-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-01 | 1988-08-02 | 1989-02-01 | $7700.00 | Window Closed / Lapsed |