Assignee: RTX Corp
•
Filing: 1975-01-06
•
Granted: 1977-02-22
•
Expires: 1995-01-06
Abstract
Abstract In filling voids in or between metallic articles, as in the repair of cracks or other surface defects in castings, the void is filled with a powder mix which upon heat treatment fills the void. The filler powder mix is a blend of at least two distinct powder components and in terms of overall composition preferably corresponds to that of article being repaired. The components comprising the mix are selected to provide a transient liquid phase and isothermal resolidification of a portion of the mix at the temperature below the article melting point. A subsequent heat treatment is preferably utilized for homogenization.
Inventors
- 👤 David S. Duvall
- 👤 William A. Owczarski
- 👤 Daniel F. Paulonis
- 👤 Robert P. Schaefer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 05:11
CPC Classifications
B; B23; B23P; B23P6/00; B23P6/002; B23P6/007; B22; B22F; B22F1/00; B22F1/09; B23K; B23K35/00; B23K35/02; B23K35/0222; B23K35/0244; B23K35/22; B23K35/24; B23K35/30; B23K35/3033
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
214 words
The method of repairing surface and near-surface defects in a metallic article which comprises: mechanically removing the defects from the article forming a cavity to be filled; providing a metallic filler material mix comprising a blend of powders consisting of at least two distinct particulate components, the mix having a composition approximating that of the article, with a first powder component including in its composition a quantity of a melting point depressant such as boron substantially in excess of that in the article and sufficient to provide melting of a portion of the mix at a processing temperature below the melting temperature of the article, and a second powder component having a composition which approximates that of the article being repaired with the ratio of the second powder component to the first powder component being from about 2:1 to about 9:1; positioning the mix to fill the cavity; raising the temperature of the article to the processing temperature whereat a portion of the mix liquefies; holding the article at about the processing temperature and effecting isothermal resolidification of the mix by diffusion of the melting point depressant into the article being repaired and into the second powder component; and continuing the exposure of the article to high temperature for homogenization of the filled volume.
Claim 2
Independent Claim
214 words
The method of repairing surface and near-surface defects in a metallic article which comprises: mechanically removing the defects from the article forming a cavity to be filled; providing a metallic filler material mix comprising a blend of powders consisting of at least two distinct particulate components, the mix having a composition approximating that of the article, with a first powder component including in its composition a quantity of a melting point depressant such as boron substantially in excess of that in the article and sufficient to provide melting of a portion of the mix at a processing temperature below the melting temperature of the article, and a second powder component having a composition which approximates that of the article being repaired with the ratio of the second powder component to the first powder component being from about 2:1 to about 9:1; positioning the mix to fill the cavity; raising the temperature of the article to the processing temperature whereat a portion of the mix liquefies; holding the article at about the processing temperature and effecting isothermal resolidification of the mix by diffusion of the melting point depressant into the article being repaired and into the second powder component; and continuing the exposure of the article to high temperature for homogenization of the filled volume.
Claim 3
Dependent Claim
24 words
The method according to claim 1 wherein: the article being repaired is a nickel-base, cobalt-base or iron-base alloy having high strength at high temperature.
Claim 4
Dependent Claim
40 words
The method according to claim 2 wherein: one particulate component has a composition approximating that of the article; and the other particulate component, containing the melting point depressant, has the same basis metal as the basis metal of the article.
Claim 5
Dependent Claim
28 words
The method according to claim 3 wherein: the melting point depressant is boron, and the boron content of said other particulate component is, by weight, about 1-3 percent.
Claim 6
Dependent Claim
29 words
The method according to claim 1 wherein: prior to the step of raising the temperature to the processing temperature, the powder mix is outgassed at high temperature in vacuum.
Claim 7
Dependent Claim
29 words
The method according to claim 1 wherein: an external pressure is applied to the mix in the cavity during the period when a portion of the mix is liquid.
Claim 8
Dependent Claim
31 words
The method according to claim 1 wherein: after filling the cavity with the mix but prior to raising the article to the processing temperature, the powders are sintered in the cavity.
Claim 9
Dependent Claim
26 words
The method according to claim 6 wherein the ratio of the second powder component to the first powder component is from about 6:1 to about 9:1.
Claim 10
Dependent Claim
24 words
The method according to claim 1 wherein the particle size of the second powder component exceeds the particle size of the first powder component.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-22 | 1980-08-23 | 1981-02-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-22 | 1984-08-23 | 1985-02-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-22 | 1988-08-23 | 1989-02-22 | $7700.00 | Window Closed / Lapsed |