Method of making mixed nitride films with at least two metals
Assignee: Siemens AG
•
Filing: 1988-03-09
•
Granted: 1989-06-27
•
Expires: 2008-03-09
Abstract
Abstract In particular for coating tools and product components, which are subject to extremely high wear, metal nitride films are used. It has been found that if the metals have markedly different melting points, in accordance with the invention, the concentrations of the metals can be varied as a function of the film thickness. For manufacturing such mixed nitride films by vaporization of metal alloy cathodes by means of an arc while simultaneously introducing nitrogen as reaction gas, a variable voltage is applied to the substrate during vaporization of the metal alloy and varied as a function of the film thickness on the substrate.
Inventors
- 👤 Helmut Freller
- 👤 Peter Schack
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 11:28
CPC Classifications
C; C23; C23C; C23C30/00; C23C30/005; C23C14/00; C23C14/06; C23C14/0641
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
194 words
A method for producing a reactively deposited compound film on a substrate to provide a coating for a surface subject to wear, the method comprises the steps of: using at least one cathode comprising an alloy including at least two metallic elements wherein at least one of the metallic elements has a markedly different melting point from the melting point of the other metallic element; producing a highly ionized metal vapor from the alloy of the at least one cathode by using at least one electric arc wherein the metal vapor includes ions of a first metallic element and ions of a second metallic element and the amount of ionization for the first metallic element is different from the second metallic element, controlling the ratio between at least the first and the second metallic elements in the deposited compound film by applying a variable voltage potential to the substrate for attracting the ions of the first metallic element to a different extent than the ions of the second metallic element; and varying the voltage potential applied to the substrate over time and as a function of thickness of the deposited film on the substrate.
Claim 2
Independent Claim
194 words
A method for producing a reactively deposited compound film on a substrate to provide a coating for a surface subject to wear, the method comprises the steps of: using at least one cathode comprising an alloy including at least two metallic elements wherein at least one of the metallic elements has a markedly different melting point from the melting point of the other metallic element; producing a highly ionized metal vapor from the alloy of the at least one cathode by using at least one electric arc wherein the metal vapor includes ions of a first metallic element and ions of a second metallic element and the amount of ionization for the first metallic element is different from the second metallic element, controlling the ratio between at least the first and the second metallic elements in the deposited compound film by applying a variable voltage potential to the substrate for attracting the ions of the first metallic element to a different extent than the ions of the second metallic element; and varying the voltage potential applied to the substrate over time and as a function of thickness of the deposited film on the substrate.
Claim 3
Dependent Claim
21 words
A method in accordance with claim 1, wherein the voltage applied to the substrate is varied between zero and -400 volts.
Claim 4
Dependent Claim
13 words
A method in accordance with claim 1, wherein the voltage is varied continuously.
Claim 5
Dependent Claim
19 words
A method in accordance with claim 1, wherein the voltage applied to the substrate is varied in incremental steps.
Claim 6
Dependent Claim
27 words
A method according to claim 4, further comprising vaporizing a second cathode having a different alloy wherein the difference between the two alloys is in aluminum content.
Claim 7
Dependent Claim
43 words
A method in accordance with claim 1, wherein the cathode comprises a TiAl alloy of predetermined Al concentration and the concentration of the aluminum in the initial alloy of the coating being higher than that present at an extreme portion of the coating.
Claim 8
Dependent Claim
26 words
A method according to claim 6, wherein the ratio of the aluminum concentration of the film is determined by the voltage value applied to the substrate.
Claim 9
Dependent Claim
28 words
A method according to claim 6, further comprises vaporizing a second cathode and the one cathode and the second cathode comprise two material sources having different aluminum content.
Claim 10
Dependent Claim
26 words
A method according to claim 1 characterized in that by changing the voltage on the substrate in increments mixed nitride films with sandwich-like structure are grown.
Claim 11
Dependent Claim
45 words
A method according to claim 1, characterized in that changing of the concentration of the metals in the deposited film is varied to promote adhesion to the substrate and then to provide an increase in wear resistance for an outer extreme of the deposited film.
Claim 12
Dependent Claim
17 words
A method according to claim 1, wherein one of the at least two metallic elements in vanadium.
References Cited (Backward Citations)
FR2156413A1
Cited
US4060471A
Cited
US4346123A
Cited
EP0038294A2
Cited
US4419202A
Cited
US4467437A
Cited
GB2117009A
Cited
US4716083A
Cited
FR2557562A1
Cited
US4620913A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-06-26 | 1992-12-26 | 1993-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-06-26 | 1996-12-26 | 1997-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-06-26 | 2000-12-26 | 2001-06-27 | $7700.00 | Window Closed / Lapsed |