Method of producing a heat shrinkable elastomer and articles utilizing the elastomer
Assignee: Kimberly Clark Worldwide Inc
•
Filing: 1987-12-04
•
Granted: 1989-03-28
•
Expires: 2007-12-04
Abstract
Abstract A heat-shrinkable elastomer having a first length is produced by uniaxially orienting a copolymer having hard block and elastomeric soft block polymer segments to a second length which is substantially greater than a third length at which partial permanent deformation occurs. Upon removal of the tensioning force, the stretched elastomer naturally relaxes to the third length which is substantially greater than the first length but less than the second length. Upon application of heat, the elastomer shrinks and recovers its elastic properties. The heat-shrinkable elastomer can be coextruded by conventional techniques as a core layer disposed between nonelastic outer layers or skins, and the resulting coextruded elastomer can be uniaxially tensioned as above. Articles or garments such as disposable diapers advantageously use the heat-shrinkable elastomer of the present invention as a means to shirr portions thereof, such as waistbands.
Inventors
- 👤 William S. Pomplun
- 👤 Rodney C. Christianson
- 👤 Mark C. Jacobs
- 👤 Attila Matray
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 09:11
CPC Classifications
A; A61; A61F; A61F13/00; A61F13/15; A61F13/45; A61F13/49; A61F13/49007; A61F13/49009; A61F13/15577; A61F13/15585; A61F13/15593; A61F5/00; A61F5/44; A61F5/4401; B; B29; B29C; B29C48/00; B29C48/03; B29C48/07; B29C48/08; B29C55/00; B29C55/02; B29C55/04; B29C55/06; B29C61/00; B29C61/003; B29C61/02; B32; B32B; B32B25/00; B32B25/04; B32B25/08; A61F2013/49068; A61F2013/49076; B29C35/00; B29C35/02; B29C35/08; B29C35/0805; B29C2035/0855; B29K; B29K2021/00; B29K2071/00; B29K2077/00; B29K2096/00; B29K2096/04; B29L; B29L2009/00; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1089; Y10T156/1092
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
131 words
A method for producing a heat-shrinkable elastomer, comprising the steps of: (a) uniaxially orienting an elastomer which has a first length and consists essentially of a synthetic rubber, said orienting conducted without the application of external heat at an elongation rate of at least about 9 in/min/in to uniaxially orient said elastomer above about 200% elongation to as second length which is substantially greater than a third length at which permanent deformation of said elastomer occurs; and (b) releasing the uniaxial orientation applied according to step (a) to allow said elastomer to naturally relax to said third length, said third length being substantially greater than said first length, said relaxed elastomer thereby having a heat shrinkage value of at least about 40 percent, and said heat-shrinkable elastomer produced without heat setting.
Claim 2
Independent Claim
131 words
A method for producing a heat-shrinkable elastomer, comprising the steps of: (a) uniaxially orienting an elastomer which has a first length and consists essentially of a synthetic rubber, said orienting conducted without the application of external heat at an elongation rate of at least about 9 in/min/in to uniaxially orient said elastomer above about 200% elongation to as second length which is substantially greater than a third length at which permanent deformation of said elastomer occurs; and (b) releasing the uniaxial orientation applied according to step (a) to allow said elastomer to naturally relax to said third length, said third length being substantially greater than said first length, said relaxed elastomer thereby having a heat shrinkage value of at least about 40 percent, and said heat-shrinkable elastomer produced without heat setting.
Claim 3
Dependent Claim
22 words
A method as recited in claim 1, wherein said third length is within the range of aobut 40-60% of said second length.
Claim 4
Dependent Claim
23 words
A method as recited in claim 1, wherein said elastomer is uniaxially oriented at an elongation rate of at least about 40 in/min/in.
Claim 5
Dependent Claim
24 words
A method as recited in claim 1, wherein asid elastomer consists essentially of a copolymer of alternating polyamide and polyether repeat block polymer segments.
Claim 6
Dependent Claim
24 words
A method as in claim 4, wherein said elastomer is uniaxially oriented between about 200% to about 700% elongation to achieve said second length.
Claim 7
Dependent Claim
60 words
A method as recited in claim 4, wherein said copolymer has the formula: ##STR2## wherein R 1 is a polyamide selected from the group consisting of nylon 6, nylon 10, nylon 11, nylon 12 and nylon 6,6; R 2 is a polyether selected from the group consisting of polyethylene glycol, polypropylene glycol and polytetramethylene glycol; and n is an integer.
Claim 8
Dependent Claim
39 words
A method as recited in claim 1, wherein said elastomer consists essentially of a copolymer of substantially rigid urethane block segments and elastomeric soft block segments, said soft block segments selected from the group consisting of polyethers and polyesters.
Claim 9
Dependent Claim
28 words
A method as recited in claim 1, wherein said elastomer consists essentially of a material composed of a mixture of an ethylene/vinyl acetate copolymer and an ethylene/propylene/hexadiene terpolymer.
Claim 10
Dependent Claim
25 words
A method as recited in claim 7, wherein said elastomer is uniaxially oriented between about 200% to about 700% elongation to achieve said second length.
Claim 11
Dependent Claim
25 words
A method as recited in claim 8, wherein said elastomer is uniaxially oriented between about 200% to about 700% elongation to achieve said second length.
Claim 12
Independent Claim
184 words
A method of manufacturing an article having a portion which is elastically shirred, said method comprising the steps of: (a) forming a heat-shrinkable elastomer by uniaxially orienting an elastomer having a first length and consisting essentially of a synthetic rubber, said orienting being conducted without the applicaiton of external heat at an elongation rate of at least about 9 in/min/in to uniaxially orient said elastomer above about 200% elongation to a second length substantially greater than a third length at which permanent deformation of said elastomer occurs, and releasing the uniaxial orientation to allow the elastomer to naturally relax to said third length which is substantially greater than said first length, thereby providing said elastomer with a heat shrinkage value of at least about 40% and producing said heat-shrinkable elastomer without heat setting; (b) affixing the elastomer formed according to step (a) to said portion of the article in a direction generally parallel to the desired direction of shirr; and (c) heat shrinking said affixed elastomer to thereby elastically shirr said portion of the article whereby said elastomer upon heat shrinkage becomes substantially elastomeric.
Claim 13
Independent Claim
184 words
A method of manufacturing an article having a portion which is elastically shirred, said method comprising the steps of: (a) forming a heat-shrinkable elastomer by uniaxially orienting an elastomer having a first length and consisting essentially of a synthetic rubber, said orienting being conducted without the applicaiton of external heat at an elongation rate of at least about 9 in/min/in to uniaxially orient said elastomer above about 200% elongation to a second length substantially greater than a third length at which permanent deformation of said elastomer occurs, and releasing the uniaxial orientation to allow the elastomer to naturally relax to said third length which is substantially greater than said first length, thereby providing said elastomer with a heat shrinkage value of at least about 40% and producing said heat-shrinkable elastomer without heat setting; (b) affixing the elastomer formed according to step (a) to said portion of the article in a direction generally parallel to the desired direction of shirr; and (c) heat shrinking said affixed elastomer to thereby elastically shirr said portion of the article whereby said elastomer upon heat shrinkage becomes substantially elastomeric.
Claim 14
Independent Claim
182 words
A method of producing a heat-shrinkable elastomer, comprising the steps of: (a) uniaxially orienting a composite elastomer having a first length, and including outer layers of a nonelastomer and a core layer, the core layer disposed between the outer layers and composed of an elastomer selected from the group consisting of (i) a material consisting essentially of alternating polyamide and polyether repeat block polymer segments, and (ii) a material consisting essentially of a mixture of an ethylene/vinyl acetate copolymer and an ethylene/propylene/hexadiene terpolymer, said orienting being conducted without the application of external heat at an elongation rate of at least about 9 in/min/in to uniaxially orient said elastomer above about 200% elongation to a second length substantially greater than a third length at which permanent deformation of said elastomer occurs; and (b) releasing the uniaxial orientation applied according to step (a) to allow said elastomer to naturally relax to said third length which is substantially greater than said first length, said relaxed elastomer thereby having a percent heat shrinkage of at least about 40%, and said heat-shrinkable elastomer produced without heat setting.
Claim 15
Independent Claim
182 words
A method of producing a heat-shrinkable elastomer, comprising the steps of: (a) uniaxially orienting a composite elastomer having a first length, and including outer layers of a nonelastomer and a core layer, the core layer disposed between the outer layers and composed of an elastomer selected from the group consisting of (i) a material consisting essentially of alternating polyamide and polyether repeat block polymer segments, and (ii) a material consisting essentially of a mixture of an ethylene/vinyl acetate copolymer and an ethylene/propylene/hexadiene terpolymer, said orienting being conducted without the application of external heat at an elongation rate of at least about 9 in/min/in to uniaxially orient said elastomer above about 200% elongation to a second length substantially greater than a third length at which permanent deformation of said elastomer occurs; and (b) releasing the uniaxial orientation applied according to step (a) to allow said elastomer to naturally relax to said third length which is substantially greater than said first length, said relaxed elastomer thereby having a percent heat shrinkage of at least about 40%, and said heat-shrinkable elastomer produced without heat setting.
Claim 16
Dependent Claim
27 words
A method as in claim 12, wherein prior to step (a) said composite elastomer is formed by melt laminating a coextrusiuon of said core and outer layers.
Claim 17
Dependent Claim
22 words
A method as in claim 12, wherein said core layer is between about 70% to about 90% by volume of said elastomer.
Claim 18
Dependent Claim
63 words
A method as in claim 12, wherein said core layer is a copolymer having the formula: ##STR3## wherein R 1 is a polyamide selected from the group consisting of nylon 6, nylon 10, nylon 11, nylon 12 and nylon 6,6; R 2 is a polyether selected from the group consisting of polyethylene glycol, poypropylene glycol and polytetramethylene gylcol; and n is an integer.
Claim 19
Dependent Claim
21 words
A method as in claim 10, wherein said third length is between about 20% to about 60% of said second length.
Claim 20
Dependent Claim
34 words
A method as in claim 12, wherein step (a) is conducted so as to uniaxially orient said elastomer to a first length which is between about 200% to about 700% of said first length.
Claim 21
Dependent Claim
23 words
A method as recited in claim 1, wherein said elastomer is uniaxially oriented at an elongation rate of at least about 20 in/min/in.
Claim 22
Dependent Claim
23 words
A method as recited in claim 4, wherein said elastomer is uniaxially oriented at an elongation rate of at least about 20 in/min/in.
Claim 23
Dependent Claim
23 words
A method as recited in claim 7, wherein said elastomer is uniaxially oriented at an elongation rate of at least about 20 in/min/in.
Claim 24
Dependent Claim
23 words
A method as recited in claim 8, wherein said elastomer is uniaxially oriented at an elongation rate of at least about 20 in/min/in.
Claim 25
Dependent Claim
23 words
A method as recited in claim 11, wherein said elastomer is unaiaxially oriented at an elongation rate of at least about 20 in/min/in.
Claim 26
Dependent Claim
23 words
A method as recited in claim 12, wherein said elastomer is uniaxially oriented at an elongation rate of at least about 20 in/min/in.
Claim 27
Dependent Claim
23 words
A method as recited in claim 4, wherein said elastomer is uniaxially oriented at an elongation rate of at least about 40 in/min/in.
Claim 28
Dependent Claim
23 words
A method as reicted in claim 7, wherein said elastomer is uniaxially oriented at an elongation rate of at least about 40 in/min/in.
Claim 29
Dependent Claim
23 words
A method as recited in claim 8, wherein said elastomer is uniaxially oriented at an elongation rate of at least about 40 in/min/in.
Claim 30
Dependent Claim
23 words
A method as recited in claim 11, wherein said elastomer is uniaxially oriented at an elongation rate of at least about 40 in/min/in.
Claim 31
Dependent Claim
23 words
A method as recited in claim 12, wherein said elastomer is uniaxially oriented at an elongation rate of at least about 40 in/min/in.
References Cited (Backward Citations)
US3536803A
Cited
US3479425A
Cited
US3557265A
Cited
US3639917A
Cited
US3819401A
Cited
US3912565A
Cited
US4152387A
Cited
US4418123A
Cited
US4303571A
Cited
US4467595A
Cited
US4337777A
Cited
US4486507A
Cited
US4476180A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-03-27 | 1992-09-26 | 1993-03-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-03-27 | 1996-09-26 | 1997-03-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-03-27 | 2000-09-26 | 2001-03-28 | $7700.00 | Window Closed / Lapsed |