Abstract Barriers used for separating silicone pressurizing medium from articles during curing, thereby protecting the article from silicone contamination. A composite precursor is substantially encapsulated by a barrier coating that is capable of substantially separating the composite precursor from silicone polymers at elevated temperatures during curing. The barrier coating is also capable of being chemically removed from the composite precursor subsequent to its cure without substantially damaging the composite. Composites are molded by protecting a composite precursor from a silicone pressurizing medium during curing utilizing a barrier coating. The method comprises encapsulating a composite precursor with a coating that is substantially capable of separating the composite precursor from silicone polymers at elevated temperatures. The coating is also capable of being chemically removed from the composite without damaging the composite. The precursor is cured by causing a silicone polymer to apply pressure to the precursor and exposing the precursor to elevated temperatures. Then the coating is chemically removed from the composite.
A method for molding a composite precursor to form a composite comprising (a) encapsulating said composite precursor with a chemically dissolvable metal foil coating that (i) is substantially capable of separating said composite precursor from particulate silicone at elevated temperatures; and (ii) is capable of being chemically removed from said composite without damaging said composite; (b) curing said precursor by causing said particulate silicone to apply pressure through said foil to said precursor and exposing said precursor to elevated temperatures; and (c) chemically removing said coating from said composite; whereby said composite precursor is protected from silicone contamination during curing.
Claim 2
Independent Claim
100 words
A method for molding a composite precursor to form a composite comprising (a) encapsulating said composite precursor with a chemically dissolvable metal foil coating that (i) is substantially capable of separating said composite precursor from particulate silicone at elevated temperatures; and (ii) is capable of being chemically removed from said composite without damaging said composite; (b) curing said precursor by causing said particulate silicone to apply pressure through said foil to said precursor and exposing said precursor to elevated temperatures; and (c) chemically removing said coating from said composite; whereby said composite precursor is protected from silicone contamination during curing.
Claim 3
Dependent Claim
14 words
The method as recited in claim 1 wherein said coating comprises aluminum alloys .
Claim 4
Dependent Claim
26 words
The method as recited in claim 2 wherein said coating is chemically removed with a mixture comprising tetrasodium pyrophosphate, trisodium phosphate and a suitable wetting agent.
Claim 5
Dependent Claim
22 words
The method as recited in claim 2 wherein said composite precursor is wrapped in said metal foil and sealed with conventional tape.
Claim 6
Dependent Claim
18 words
The method as recited in claim 2 wherein said metal foil is less than about 0.25 cm thick.
Claim 7
Dependent Claim
21 words
The method as recited in claim 2 wherein said metal foil is about 0.0015 cm to about 0.01 cm in thickness.
Claim 8
Dependent Claim
41 words
The method as recited in claim 5 wherein said particulate silicone polymer and said foil covered composite precursor are disposed in a pressure vessel and said foil confines any condensation products and ducts said condensation products out of said pressure vessel.
Claim 9
Dependent Claim
41 words
The method as recited in claim 6 wherein said particulate silicone polymer and said foil covered composite precursor are disposed in a pressure vessel and said foil confines any condensation products and ducts said condensation products out of said pressure vessel.
Claim 10
Dependent Claim
41 words
The method as recited in claim 4 wherein said particulate silicone polymer and said foil covered composite precursor are disposed in a pressure vessel and said foil confines any condensation products and ducts said condensation products out of said pressure vessel.