Novel wear resistant fluoropolymer-containing flexible composites and method for preparation thereof
Assignee: Saint Gobain Performance Plastics Corp
•
Filing: 1986-06-16
•
Granted: 1987-03-31
•
Expires: 2006-06-16
Abstract
Abstract Fluoropolymer containing coatings are applied to substrates, preferably textile substrates, to obtain composites which are flexible and not brittle, and which exhibit a low coefficient of friction, good wear resistance and excellent release properties. This invention comprises the technique of initially coating a flexible substrate, such as glass fabric or a metal mesh, with a fluoropolymer, which serves to prevent cracking upon flexing. The precoated substrate is thereafter coated with a blend of a hard polymer and a fluoropolymer which adheres well to the pre-coated intermediate substrate. Significantly, the composites of the invention are flexible, yet possess the wear resistance of the hard polymer component as well as the frictional and release characteristics of the fluoropolymer components.
Inventors
- 👤 John A. Effenberger
- 👤 Robert C. Ribbans, III
- 👤 Frank M. Keese
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 20:15
CPC Classifications
D; D06; D06N; D06N3/00; D06N3/04; D06N3/047; D06N7/00; D06N7/0094; D06N2201/00; D06N2201/08; D06N2201/082; D06N2203/00; D06N2203/04; D06N2203/044; D06N2209/00; D06N2209/16; D06N2209/1685
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
66 words
A method for preparing a flexible, wear resistant textile composite comprising the steps of: (a) initially coating a suitable substrate with a fluoropolymer which includes a fluoroplastic, a curative-free fluoroelastomer or blends or combinations thereof; and thereafter (b) applying an overcoat layer comprising a blend of a hard polymer and a fluoropolymer wherein the fluoropolymer includes a fluoroplastic, a curative-free fluoroelastomer or blends or combinations thereof.
Claim 2
Independent Claim
66 words
A method for preparing a flexible, wear resistant textile composite comprising the steps of: (a) initially coating a suitable substrate with a fluoropolymer which includes a fluoroplastic, a curative-free fluoroelastomer or blends or combinations thereof; and thereafter (b) applying an overcoat layer comprising a blend of a hard polymer and a fluoropolymer wherein the fluoropolymer includes a fluoroplastic, a curative-free fluoroelastomer or blends or combinations thereof.
Claim 3
Dependent Claim
12 words
A method according to claim 1 wherein the substrate is a textile.
Claim 4
Dependent Claim
18 words
A method according to claim 1 wherein the fluoropolymer of the initial layer is a low modulus fluoropolymer.
Claim 5
Dependent Claim
22 words
A method according to claim 1 wherein the low modulus fluoropolymer is a fluoroplastic, a fluoroelastomer or any blend or combination thereof.
Claim 6
Dependent Claim
24 words
A method according to claim 1 wherein the hard polymer is selected from the group comprising polyimides, polyamidimide, polyphenylene sulfide, epoxy and polyether ketone.
Claim 7
Dependent Claim
23 words
A method according to claim 1 wherein the hard polymer comprises about 40 to 90 percent by weight of the hard polymer/fluoropolymer blend.
Claim 8
Dependent Claim
31 words
A method according to claim 1 wherein the fluoropolymer component of the blend of the outermost layer is selected from the group comprising fluoroplastics, fluoroelastomers, or any blend or combination thereof.
Claim 9
Independent Claim
100 words
A method for preparing a flexible, wear resistant composite comprising the steps of: (a) applying an initial layer comprising any suitable adhesion promoting chemical compatible with the substrate; (b) separately forming an overcoat layer as a film comprising a blend of (1) a hard polymer and (2) a fluoropolymer, wherein the fluoropolymer includes a fluoroplastic, a curative-free fluoroelastomer or blends or combinations thereof such that the most proximate resin components of the said film are bondable to the adhesion promoting chemical on the substrate; and (c) thereafter applying the said film to the adhesion-treated face or faces of the substrate.
Claim 10
Independent Claim
100 words
A method for preparing a flexible, wear resistant composite comprising the steps of: (a) applying an initial layer comprising any suitable adhesion promoting chemical compatible with the substrate; (b) separately forming an overcoat layer as a film comprising a blend of (1) a hard polymer and (2) a fluoropolymer, wherein the fluoropolymer includes a fluoroplastic, a curative-free fluoroelastomer or blends or combinations thereof such that the most proximate resin components of the said film are bondable to the adhesion promoting chemical on the substrate; and (c) thereafter applying the said film to the adhesion-treated face or faces of the substrate.
Claim 11
Dependent Claim
27 words
A method for making a composite according to claim 8 wherein the outermost layer is separately formed by a cast coating process, such as a decalcomania process.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-30 | 1990-09-29 | 1991-03-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-30 | 1994-09-29 | 1995-03-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-30 | 1998-09-29 | 1999-03-31 | $7700.00 | Window Closed / Lapsed |