Selective backside plating of gaas monolithic microwave integrated circuits
Assignee: Raytheon Co
•
Filing: 1987-05-01
•
Granted: 1988-12-27
•
Expires: 2007-05-01
Abstract
Abstract A technique for etching tub structures and vias on the backside of a wafer comprised of gallium arsenide and for providing a planar surface on said backside of the gallium arsenide wafer is described. The tubs are formed by providing a layer of resist over the backside of the gallium arsenide substrate, and this layer is patterned to provide selected areas covering regions where tub structures and vias will be provided. In the selectively exposed regions, palladium and gold are sequentially deposited. The resist pattern is then stripped, and a second resist layer pattern is deposited masking portions of the continuous conductive layer and areas where vias are to be provided. The tub structures are then provided by suitably etching the tub to undercut portions of the resist and the palladium layer. A second continuous conductive coating is then provided in the tub structure to provide a plating layer for subsequent plating of a gold film over the palladium. Preferably, the gold is plated to completely or substantially completely fill the tub. The vias are then provided on the backside of the wafer by masking the first continuous conductive coating and the tub regions and etching the unexposed regions of the substrate to provide the via holes. The via holes are then plated with a continuous conductive layer of palladium and then gold to substantially fill the via.
Inventors
- 👤 Elsa K. Tong
- 👤 Thomas E. Kazior
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 17:49
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/021; H10D; H10D62/00; H10D62/10; H10D62/117; H10P; H10P50/00; H10P50/69; H10P50/691; H10W20/023; H10W20/0234; H10W20/0242; H10W20/20; H10W40/00; H10W40/20; H10W40/22; H10W40/226; H10W40/228; Y; Y10; Y10S; Y10S148/00; Y10S148/026; Y10S148/05; Y10S148/105; Y10S148/135
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
133 words
A method comprising the steps of: providing a first continuous conductive layer over selected portions of a surface of a substrate; masking said first continuous conductive layer and a first portion of exposed portion of said substrate surface; forming a first recess in said substrate having a first depth from said unmasked second portions of said exposed portions of said substrate; disposing a solid deposit of a conductive material in said first recess; masking said first continuous conductive layer and said conductive material disposed in said first recess, leaving said first portion of said substrate exposed; forming a second recess in said substrate having a second depth from said unmasked first portion of said substrate; and disposing a solid deposit of a conductive material in at least a portion of said second recess.
Claim 2
Independent Claim
133 words
A method comprising the steps of: providing a first continuous conductive layer over selected portions of a surface of a substrate; masking said first continuous conductive layer and a first portion of exposed portion of said substrate surface; forming a first recess in said substrate having a first depth from said unmasked second portions of said exposed portions of said substrate; disposing a solid deposit of a conductive material in said first recess; masking said first continuous conductive layer and said conductive material disposed in said first recess, leaving said first portion of said substrate exposed; forming a second recess in said substrate having a second depth from said unmasked first portion of said substrate; and disposing a solid deposit of a conductive material in at least a portion of said second recess.
Claim 3
Dependent Claim
132 words
The method as recited in claim 1 wherein said first disposing step comprises the steps of: providing a second continuous conductive layer on exposed portions of said substrate formed in said first recess, with said second continuous conductive layer being disposed in electrical contact with said first continuous conductive layer; and plating a conductive material over said second continuous conductive layer, to provide the solid deposit to substantially fill said first recess; and wherein said second disposing step comprises the steps of: providing a third continuous conductive layer on exposed portions of said substrate formed by said second recess, with said third continuous conductive layer being disposed in electrical continuity with said first continuous conductive layer; and plating a conductive layer over said third continuous conductive layer to fill said second recess.
Claim 4
Dependent Claim
85 words
The method as recited in claim 2 wherein the step of providing the first continuous conductive layer comprises the steps of: providing a pair of masked regions over the surface of the substrate, the locations of said masked regions corresponding to the location of the first recess and the second recess; and bringing exposed portions of the substrate into contact with a conductive material containing solution to provide a layer of said conductive material over said exposed portions to provide said first continuous conductive layer.
Claim 5
Dependent Claim
36 words
The method as recited in claim 3 wherein the step of providing the first continuous conductive layer further comprises the step of plating over said layer of conductive material, to provide the first continuous conductive layer.
Claim 6
Dependent Claim
53 words
The method as recited in claim 2 wherein the step of providing the second continuous conductive layer comprises the step of bringing the exposed portions of the substrate formed by the first recess into contact with a conductive material containing solution which leaves said conductive material to form the second continuous conductive layer.
Claim 7
Dependent Claim
52 words
The method as recited in claim 2 wherein the step of providing the third continuous conductive layer comprises the step of bringing the exposed portions of the substrate formed by the second recess into contact with a conductive material containing solution which leaves said conductive material to form the third continuous conductive.
Claim 8
Dependent Claim
23 words
The method as recited in claim 2 wherein the substrate is comprised of gallium arsenide and the conductive material containing solution comprises palladium.
Claim 9
Dependent Claim
21 words
The method as recited in claim 3 wherein the substrate comprises gallium arsenide and the conductive material containing solution comprises palladium.
Claim 10
Dependent Claim
21 words
The method as recited in claim 4 wherein the substrate comprises gallium arsenide and the conductive material containing solution comprises palladium.
Claim 11
Independent Claim
215 words
A method of providing tub and via structures in a semiconductor substrate, with said substrate having a substantially uniformly thick conductive layer disposed over a surface of said substrate in contact with said tub and via structures comprises the steps of: providing a first, patterned continuous conductive layer over selected portions of the surface of said substrate; masking said first continuous conductive layer and a first portion of exposed portions of said substrate; etching an unmasked second portion of said exposed portions of said substrate to provide a first recess having a first depth; electrolessly plating said first recess to provide a second continuous conductive layer in said recess disposed in electrical continuity with said first layer; plating a conductive material over said second continuous conductive layer to substantially fill said recess; masking said first continuous conductive layer and said plated recess, leaving said first portion of said exposed portions exposed; etching said unmasked first portions of said second exposed portions of said substrate to provide a second recess having a second depth; electrolessly plating said second recess to provide a third continuous conductive layer in said second recess disposed in electrical continuity with said first continuous conductive layer; and plating a conductive material over said third continuous conductive layer to substaniially fill said recess.
Claim 12
Independent Claim
215 words
A method of providing tub and via structures in a semiconductor substrate, with said substrate having a substantially uniformly thick conductive layer disposed over a surface of said substrate in contact with said tub and via structures comprises the steps of: providing a first, patterned continuous conductive layer over selected portions of the surface of said substrate; masking said first continuous conductive layer and a first portion of exposed portions of said substrate; etching an unmasked second portion of said exposed portions of said substrate to provide a first recess having a first depth; electrolessly plating said first recess to provide a second continuous conductive layer in said recess disposed in electrical continuity with said first layer; plating a conductive material over said second continuous conductive layer to substantially fill said recess; masking said first continuous conductive layer and said plated recess, leaving said first portion of said exposed portions exposed; etching said unmasked first portions of said second exposed portions of said substrate to provide a second recess having a second depth; electrolessly plating said second recess to provide a third continuous conductive layer in said second recess disposed in electrical continuity with said first continuous conductive layer; and plating a conductive material over said third continuous conductive layer to substaniially fill said recess.
Claim 13
Dependent Claim
37 words
The method as recited in claim 10 further comprising the step of forming a relatively thick layer of a metal over said first continuous conductive layer, and the plated material disposed in said first and second recesses.
Claim 14
Dependent Claim
79 words
The method as recitdd in claim 11 wherein during the providing step, a layer of a metal masking material is disposed over the continuous conductive layer, and during the first plating step, a layer of said metal masking material is disposed over the plated conductive material which fills the first recess, and wherein said second masking step is provided by forming the metal masking layers over the first continuous conductive layer and the conductive material disposed in said recess.
Claim 15
Dependent Claim
83 words
The method as recited in claim 12 wherein the step of providing the first continuous conductive layer comprises the steps of: providing a pair of masked regions over the surface of the substrate, the locations of said masked regions corresponding to the location of the first recess and the second recess; and bringing exposed portions of the substrate into contact with a solution to electrolessly plate a layer of a conductive material over said exposed portions to provide said first continuous conductive layer.
Claim 16
Dependent Claim
38 words
The method as recited in claim 13 wherein the step of providing the first continuous conductive layer further comprises the step of plating over said layer of electrolessly plated conductive material to provide the first continuous conductive layer.
Claim 17
Dependent Claim
42 words
The method as recited in claim 14 wherein the layer of conductive material has a thickness in the range of 100 A to 1,000 A, and the plated layer thereover has a thickness in the range of 1,000 A to 20,000 A.
Claim 18
Dependent Claim
32 words
The method as recited in claim 12 wherein the substrate comprises gallium arsenide and wherein each electroless plating step includes bringing a solution comprising palladium into contact with the exposed gallium arsenide.
Claim 19
Dependent Claim
32 words
The method as recited in claim 15 wherein the substrate comprises gallium arsenide and wherein each electroless plating step includes bringing a solution comprising palladium into contact with the exposed gallium arsenide.
Claim 20
Dependent Claim
42 words
The method as recited in claim 11 wherein the second masking step is provided by disposing a layer of resist over the backside of the substrate and patterning said layer of resist to leave said first portion of said exposed portions exposed.
Claim 21
Dependent Claim
84 words
The method as recited in claim 18 wherein the step of providing the first continuous conductive layer comprises the steps of: providing a pair of masked regions over the surface of the substrate, the locations of said masked regions corresponding to the location of the first recess and the second recess; and bringing exposed portions of the substrate into contact with a plating solution to electrolessly plate a layer of a conductive material over said exposed portions to provide said first continuous conductive layer.
Claim 22
Dependent Claim
38 words
The method as recited in claim 19 wherein the step of providing the first continuous conductive layer further comprises the step of plating over said layer of electrolessly plated conductive material to provide the first continuous conductive layer.
Claim 23
Dependent Claim
42 words
The method as recited in claim 20 wherein the layer of conductive material has a thickness in the range of 100 A to 1,000 A, and the plated layer thereover has a thickness in the range of 1,000 A to 20,000 A.
Claim 24
Dependent Claim
32 words
The method as recited in claim 18 wherein the substrate comprises gallium arsenide and wherein each electroless plating step includes bringing a solution comprising palladium into contact with the exposed gallium arsenide.
Claim 25
Dependent Claim
32 words
The method as recited in claim 21 wherein the substrate comprises gallium arsenide and wherein each electrolessly plating step includes bringing a solution containing palladium into contact with the exposed gallium arsenide.
References Cited (Backward Citations)
US3614558A
Cited
US3657029A
Cited
US3833842A
Cited
US3653999A
Cited
US3667008A
Cited
US3783044A
Cited
US3751292A
Cited
US3911559A
Cited
US3900944A
Cited
JPS5384483A
Cited
US4109372A
Cited
US4316203A
Cited
US4631806A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-12-27 | 1992-06-27 | 1992-12-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-12-27 | 1996-06-27 | 1996-12-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-12-27 | 2000-06-27 | 2000-12-27 | $7700.00 | Window Closed / Lapsed |