Laminated glass lenses

Claim 2

A three-component laminated lens structure exhibiting optical quality transmission which does not delaminate after repeated thermal cyclings over the temperature range of -40° to +80° C. and does not delaminate or demonstrate significant haze after exposure to high humidities for extended periods of time, said lens consisting of: (a) a thin inorganic glass layer having a linear coefficient of thermal expansion within the range of about 60-120×10 -7 /° C.; (b) an organic plastic layer having a linear coefficient of thermal expansion within the range of about 200-700×10 -7 /° C.; and (c) an organic adhesive that exhibits flexibility, and can be cured at temperatures in the vicinity of room temperature which bonds said glass layer and said plastic layer into an essentially stress-free assemblage; wherein the power of said lens results from a curvature in the rear surface of said plastic layer.

Claim 3

A lens according to claim 1 wherein said glass layer is a photochromic glass.

Claim 4

A lens according to claim 1 wherein said organic plastic is a resin selected from the group consisting of an acrylic, an epoxy, a polycarbonate, a silicone, a urethane, and a polyimide.

Claim 5

A lens according to claim 3 wherein said organic plastic has a coefficient of thermal expansion within the range of about 400-600×10 -7 /° C.

Claim 6

A lens according to claim 1 wherein said organic adhesive is a resin selected from the group consisting of an acrylic, an epoxy, a polycarbonate, a silicone, and a urethane.

Claim 7

A lens according to claim 5 wherein said organic adhesive consists of an aliphatic epoxy resin cured with an aliphatic amine.

Claim 8

A lens according to claim 5 wherein said organic adhesive consists of an aliphatic epoxy resin plus an aromatic monofunctional diluent cured with an aliphatic amine curing agent.

Claim 9

A lens according to claim 5 wherein said organic adhesive consists of an aromatic epoxy resin cured with an aliphatic amine.

Claim 10

A lens according to claim 1 wherein the transition temperature T g of said adhesive ranges between about 0°-30° C.

Claim 11

A lens according to claim 1 wherein each of the three components exhibits essentially the same refractive index.

Claim 12

A lens according to claim 10 wherein each of the three components exhibits a refractive index of about 1.523.

Claim 13

A lens according to claim 1 wherein the thickness of said adhesive is essentially constant across the diameter of said lens.

Claim 14

A lens according to claim 1 wherein the thickness of said adhesive is about 0.0075"-0.020".

Claim 15

A lens according to claim 1 wherein said adhesive has a curing temperature between about 0°-30° C.

Claim 16

A lens according to claim 1 wherein the thickness of said glass layer is about 0.5-1.5 mm.

Claim 17

A lens according to claim 15 wherein the thickness of said glass layer is about 1-1.25 mm.

Claim 18

A lens according to claim 1 wherein said glass layer and said adhesive are plano layers.

Claim 19

A five-component laminated lens structure exhibiting optical quality transmission which does not delaminate after repeated thermal cyclings over the temperature range of -40° to +80° C. and does not delaminate or demonstrate significant haze after exposure to high humidities for extended periods of time, said lens consisting of: (a) a first organic plastic layer having a linear coefficient of thermal expansion within the range of about 200-700×10 -7 /° C.; (b) a first organic adhesive that exhibits flexibility and can be cured at temperatures in the vicinity of room temperature; (c) a thin inorganic glass layer having a linear coefficient of thermal expansion within the range of about 60-120×10 -7 /° C.; (d) a second organic adhesive that exhibits flexibility and can be cured at temperatures in the vicinity of room temperature; and (e) a second organic plastic layer having a linear coefficient of thermal expansion within the range of about 200-700×10 -7 /° C.; wherein said adhesive bonds said glass layer to said plastic layers into an essentially stress-free assemblage.

Claim 20

A five-component laminated lens structure exhibiting optical quality transmission which does not delaminate after repeated thermal cyclings over the temperature range of -40° to +80° C. and does not delaminate or demonstrate significant haze after exposure to high humidities for extended periods of time, said lens consisting of: (a) a first organic plastic layer having a linear coefficient of thermal expansion within the range of about 200-700×10 -7 /° C.; (b) a first organic adhesive that exhibits flexibility and can be cured at temperatures in the vicinity of room temperature; (c) a thin inorganic glass layer having a linear coefficient of thermal expansion within the range of about 60-120×10 -7 /° C.; (d) a second organic adhesive that exhibits flexibility and can be cured at temperatures in the vicinity of room temperature; and (e) a second organic plastic layer having a linear coefficient of thermal expansion within the range of about 200-700×10 -7 /° C.; wherein said adhesive bonds said glass layer to said plastic layers into an essentially stress-free assemblage.

Claim 21

A lens according to claim 18 wherein the composition of the first and second organic plastic layers is the same and the composition of the first and second organic adhesives is the same.

Claim 22

A lens according to claim 18 wherein said first and second organic plastics are resins selected from the group consisting of an acrylic, an epoxy, a polycarbonate, a silicone, a urethane, and a polyimide.

Claim 23

A lens according to claim 18 wherein said first end second organic adhesives are resins selected from the group consisting of an acrylic, an epoxy, a polycarbonate, a silicone, and a urethane.

Claim 24

A three-component laminated lens structure exhibiting optical quality transmission which does not delaminate after repeated thermal cyclings over the temperature range of -40° to +80° C. and does not delaminate or demonstrate significant haze after exposure to high humidities for extended periods of time, said lens comprising: (a) an inorganic glass layer having a thickness of about 0.5-1.5 mm and a linear coefficient of thermal expansion within the range of about 60-120×10 -7 /° C.; (b) an organic plastic layer consisting of a resin selected from the group consisting of an acrylic, an imide-modified acrylic, an epoxy, a polycarbonate, a silicone, a urethane, and a polyimide having a linear coefficient of thermal expansion within the range of about 200-700×10 -7 /° C.; and (c) an organic adhesive layer consisting of a resin selected from the group consisting of an acrylic, an epoxy, a polycarbonate, a silicone, and a urethane that exhibits flexibility and can be cured at temperatures in the vicinity of room temperature which bonds together said glass layer.

Claim 25

A three-component laminated lens structure exhibiting optical quality transmission which does not delaminate after repeated thermal cyclings over the temperature range of -40° to +80° C. and does not delaminate or demonstrate significant haze after exposure to high humidities for extended periods of time, said lens comprising: (a) an inorganic glass layer having a thickness of about 0.5-1.5 mm and a linear coefficient of thermal expansion within the range of about 60-120×10 -7 /° C.; (b) an organic plastic layer consisting of a resin selected from the group consisting of an acrylic, an imide-modified acrylic, an epoxy, a polycarbonate, a silicone, a urethane, and a polyimide having a linear coefficient of thermal expansion within the range of about 200-700×10 -7 /° C.; and (c) an organic adhesive layer consisting of a resin selected from the group consisting of an acrylic, an epoxy, a polycarbonate, a silicone, and a urethane that exhibits flexibility and can be cured at temperatures in the vicinity of room temperature which bonds together said glass layer.

Claim 26

A lens according to claim 22 wherein said organic plastic has a coefficient of thermal expansion within the range of about 400-600×10 -7 /° C.

Claim 27

A lens according to claim 22 wherein said organic adhesive consists of an aliphatic epoxy resin cured with an aliphatic amine.

Claim 28

A lens according to claim 22 wherein each of the three components exhibits essentially the same refractive index.

Claim 29

A lens according to claim 22 wherein the thickness of said adhesive is essentially constant across the diameter of said lens.

Claim 30

A three-component laminated lens structure exhibiting optical quality transmission which does not delaminate after repeated thermal cyclings over the temperature range of -40° to +80° C. and does not delaminate or demonstrate significant haze after exposure to high humidities for extended periods of time, said lens comprising: (a) an inorganic glass layer having a thickness of about 0.5-1.5 mm and a linear coefficient of thermal expansion within the range of about 60-120×10 -7 /° C.; (b) an organic plastic layer consisting of an epoxy resin and having a linear coefficient of thermal expansion within the range of about 400-600×10 -7 /° C.; and (c) an organic adhesive layer consisting of an epoxy resin cured with an aliphatic amine that exhibits flexibility and can be cured at temperatures in the vicinity of room temperature which bonds together said glass layer and said plastic layer; wherein each of the three components exhibits essentially the same refractive index and the thickness of said adhesive is essentially constant across the diameter of said lens.

Claim 31

A three-component laminated lens structure exhibiting optical quality transmission which does not delaminate after repeated thermal cyclings over the temperature range of -40° to +80° C. and does not delaminate or demonstrate significant haze after exposure to high humidities for extended periods of time, said lens comprising: (a) an inorganic glass layer having a thickness of about 0.5-1.5 mm and a linear coefficient of thermal expansion within the range of about 60-120×10 -7 /° C.; (b) an organic plastic layer consisting of an epoxy resin and having a linear coefficient of thermal expansion within the range of about 400-600×10 -7 /° C.; and (c) an organic adhesive layer consisting of an epoxy resin cured with an aliphatic amine that exhibits flexibility and can be cured at temperatures in the vicinity of room temperature which bonds together said glass layer and said plastic layer; wherein each of the three components exhibits essentially the same refractive index and the thickness of said adhesive is essentially constant across the diameter of said lens.