Abrasion-resistant optical element
Assignee: Individual
•
Filing: 1977-02-07
•
Granted: 1978-03-14
•
Expires: 1997-02-07
Abstract
Abstract A coated abrasion-resistant optical element, such as an eyeglass lens, formed of a typical rigid polymeric substrate of relatively low scratch resistance coated on at least one surface with a relatively soft, resilient, and tough transparent polymeric material. The essential characteristics of the coating material resulting in an abrasion-resistant protective film for the optical element are disclosed.
Inventors
- 👤 Joseph Philipson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 10:43
CPC Classifications
B; B29; B29D; B29D11/00; B29D11/00865; C; C08; C08J; C08J7/00; C08J7/04; C08J7/0427; C08J7/046; Y; Y10; Y10S; Y10S428/00; Y10S428/912; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/24983; Y10T428/31504; Y10T428/31507; Y10T428/31511; Y10T428/31551; Y10T428/31565; Y10T428/31573; Y10T428/31587; Y10T428/31591; Y10T428/31598; Y10T428/31601; Y10T428/31652; Y10T428/31663; Y10T428/31855; Y10T428/31859; Y10T428/31909; Y10T428/31913; Y10T428/31938
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
172 words
An abrasion-resistant optical element comprising a transparent and relatively rigid polymeric substrate having a pair of smooth optical surfaces; and a transparent coating of a relatively soft polymeric material bonded to at least one of said surfaces; said optical element having a light transmission value of at least 70 percent when tested in accordance with ASTM Standard D1003 and having a haze value no greater than 5 percent when tested in accordance with ASTM Standard D1003; said polymeric coating material having a durometer value within the range of 10 Shore A to 95 Shore D and a flexural modulus less than 0.2 × 10 5 psi as measured by ASTM Standard D790; said coating, when tested in accordance with ASTM Standards D673 and D1003 at a thickness of about 1/2 mil on a flat transparent test sample of poly(diethylene glycol bis allyl carbonate) and subjected to 2 kilograms of abrasive grit, producing a loss of light transmission no greater than 2.3 percent and an increase in haze no greater than 8.1 percent.
Claim 2
Dependent Claim
172 words
An abrasion-resistant optical element comprising a transparent and relatively rigid polymeric substrate having a pair of smooth optical surfaces; and a transparent coating of a relatively soft polymeric material bonded to at least one of said surfaces; said optical element having a light transmission value of at least 70 percent when tested in accordance with ASTM Standard D1003 and having a haze value no greater than 5 percent when tested in accordance with ASTM Standard D1003; said polymeric coating material having a durometer value within the range of 10 Shore A to 95 Shore D and a flexural modulus less than 0.2 × 10 5 psi as measured by ASTM Standard D790; said coating, when tested in accordance with ASTM Standards D673 and D1003 at a thickness of about 1/2 mil on a flat transparent test sample of poly(diethylene glycol bis allyl carbonate) and subjected to 2 kilograms of abrasive grit, producing a loss of light transmission no greater than 2.3 percent and an increase in haze no greater than 8.1 percent.
Claim 3
Dependent Claim
41 words
The optical element of claim 1 in which said relatively rigid polymeric substrate has a durometer value above substantially 95 Shore D and a flexural modulus of no less than 0.2 × 10 5 psi as measured by ASTM Standard D790.
Claim 4
Dependent Claim
39 words
The optical element of claim 2 in which said substrate is formed of a material selected from the group consisting of polycarbonates, polyacrylics, cellulose acetate, polystyrene, polysulfones, cellulose acetate butyrate, polyester, poly(4-methyl pentene-1), and selected polymers and copolymers thereof.
Claim 5
Dependent Claim
21 words
The optical element of claim 1 in which said coating has a thickness within the range of 0.1 to 20.0 mils.
Claim 6
Dependent Claim
21 words
The optical element of claim 4 in which said coating has a thickness within the range of 0.2 to 5 mils.
Claim 7
Dependent Claim
17 words
The optical element of claim 5 in which said coating has a thickness of about 1 mil.
Claim 8
Dependent Claim
28 words
The optical element of claim 1 in which said coating material is selected from the group consisting of polyurethane, polybutadiene, silicone, polysulfide, epoxy, polyacrylic, and selected copolymers thereof.
Claim 9
Dependent Claim
23 words
The optical element of claim 7 in which said coating material is a polyurethane reaction product of an aliphatic diisocyanate and aliphatic polyols.
Claim 10
Dependent Claim
14 words
The optical element of claim 8 in which said diisocyanate is a cycloaliphatic diisocyanate.
Claim 11
Dependent Claim
23 words
The optical element of claim 9 in which said polyols comprises a mixture of diol and polyol with more than two hydroxyl groups.
Claim 12
Dependent Claim
221 words
An abrasion-resistant optical element comprising a transparent and relatively rigid polymeric substrate having a pair of smooth optical surfaces; and a transparent coating of relatively soft polymeric material bonded to at least one of said surfaces; said optical element having a light transmission value of at least 70 percent when tested in accordance with ASTM Standard D1003 and having a haze value no greater than 5 percent when tested in accordance with ASTM Standard D1003; said polymeric coating material having a durometer value within the range 10 Shore A to 95 Shore D and a flexural modulus of less than 0.2 × 10 5 psi as measured by ASTM Standard D790; said coating, when tested in accordance with ASTM Standard D673 at a thickness of about 1/2 mil on a flat transparent test sample of poly(diethylene glycol bis allyl carbonate) and subjected to 2 kilograms of abrasive grit, producing a loss of light transmission no greater than 2.3 percent and an increase in haze no greater than 8.1 percent; said coating, when further tested in accordance with ASTM F32 at a thickness of about 1/2 mil on a flat transparent test sample of poly(diethylene glycol bis allyl carbonate), producing no permanent score visible to the naked eye following engagement by a moving stylus at a loading of up to 20 grams.
Claim 13
Dependent Claim
221 words
An abrasion-resistant optical element comprising a transparent and relatively rigid polymeric substrate having a pair of smooth optical surfaces; and a transparent coating of relatively soft polymeric material bonded to at least one of said surfaces; said optical element having a light transmission value of at least 70 percent when tested in accordance with ASTM Standard D1003 and having a haze value no greater than 5 percent when tested in accordance with ASTM Standard D1003; said polymeric coating material having a durometer value within the range 10 Shore A to 95 Shore D and a flexural modulus of less than 0.2 × 10 5 psi as measured by ASTM Standard D790; said coating, when tested in accordance with ASTM Standard D673 at a thickness of about 1/2 mil on a flat transparent test sample of poly(diethylene glycol bis allyl carbonate) and subjected to 2 kilograms of abrasive grit, producing a loss of light transmission no greater than 2.3 percent and an increase in haze no greater than 8.1 percent; said coating, when further tested in accordance with ASTM F32 at a thickness of about 1/2 mil on a flat transparent test sample of poly(diethylene glycol bis allyl carbonate), producing no permanent score visible to the naked eye following engagement by a moving stylus at a loading of up to 20 grams.
Claim 14
Dependent Claim
40 words
The optical element of claim 11 in which said relatively rigid polymeric substrate has a durometer value above substantially 95 Shore D and a flexural modulus no less than 0.2 × 10 5 psi as measured by ASTM Standard D790.
Claim 15
Dependent Claim
37 words
The optical element of claim 12 in which said substrate is formed of a material selected from the group consisting of polycarbonates, polyacrylics, cellulose acetate, polystyrene, polysulfones, cellulose acetate butyrate, polyester, poly(4-methyl pentene-1), and selected copolymers thereof.
Claim 16
Dependent Claim
21 words
The optical element of claim 11 in which said coating has a thickness within the range of 0.1 to 20.0 mils.
Claim 17
Dependent Claim
21 words
The optical element of claim 14 in which said coating has a thickness within the range of 0.2 to 5 mils.
Claim 18
Dependent Claim
17 words
The optical element of claim 15 in which said coating has a thickness of about 1 mil.
Claim 19
Dependent Claim
28 words
The optical element of claim 11 in which said coating material is selected from the group consisting of polyurethane, polybutadiene, silicone, polysulfide, epoxy, polyacrylic, and selected copolymers thereof.
Claim 20
Dependent Claim
23 words
The optical element of claim 17 in which said coating material is a polyurethane reaction product of an aliphatic diisocyanate and aliphatic polyols.
Claim 21
Dependent Claim
14 words
The optical element of claim 18 in which said diisocyanate is a cycloaliphatic diisocyanate.
Claim 22
Dependent Claim
23 words
The optical element of claim 19 in which said polyols comprises a mixture of diol and polyol having more than two hydroxyl groups.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-13 | 1981-09-12 | 1982-03-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-13 | 1985-09-12 | 1986-03-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-13 | 1989-09-12 | 1990-03-14 | $7700.00 | Window Closed / Lapsed |