Process for the production of an abrasion resistant optical element
Assignee: American Optical Corp
•
Filing: 1974-09-30
•
Granted: 1976-07-27
•
Expires: 1994-09-30
Abstract
Abstract A process for preparing an abrasion resistant allyl diglycol carbonate lens is provided. The allyl diglycol carbonate lens prepared by the process of the invention has an abrasion resistant coating thereon comprised of a transparent base of a hydrolyzed polysilicic acid ester and polyvinyl alcohol comprising 90 to 100% hydrolyzed polyvinyl acetate.
Inventors
- 👤 Albert R. LeBoeuf
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 21:45
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/04; C08J7/043; B; B29; B29D; B29D11/00; B29D11/00865; C08J7/0427; C08J7/046; C08J7/12; C09; C09D; C09D183/00; C09D183/02; G02B1/105; G; G02; G02B; G02B1/00; G02B1/10; G02B1/14; C08J2331/00; C08J2429/00; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31507
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
91 words
An allyl diglycol carbonate lens having a transparent abrasion resistant coating upon at least one surface obtained by (1) hydrolyzing said surface of said lens in an aqueous alkaline solution; (2) coating said lens with an aqueous coating composition comprising a mixture of an acid polysilicic ester of an alcohol containing from 1 to 12 carbon atoms and having up to four silicic acid ester groups per silicon atom, and a polyvinyl alcohol comprising 90% to 100% hydrolyzed polyvinyl acetate; and (3) drying and curing said coating at an elevated temperature.
Claim 2
Dependent Claim
91 words
An allyl diglycol carbonate lens having a transparent abrasion resistant coating upon at least one surface obtained by (1) hydrolyzing said surface of said lens in an aqueous alkaline solution; (2) coating said lens with an aqueous coating composition comprising a mixture of an acid polysilicic ester of an alcohol containing from 1 to 12 carbon atoms and having up to four silicic acid ester groups per silicon atom, and a polyvinyl alcohol comprising 90% to 100% hydrolyzed polyvinyl acetate; and (3) drying and curing said coating at an elevated temperature.
Claim 3
Dependent Claim
34 words
An allyl diglycol carbonate lens according to claim 1 wherein said coating composition further contains a C1 to C4 carbon chain alcohol and wherein said elevated temperature is of about 90°C to about 125°C.
Claim 4
Dependent Claim
16 words
An allyl diglycol carbonate lens according to claim 2 wherein said acid polysilicic ester is tetraethylorthosilicate.
Claim 5
Dependent Claim
93 words
A process for coating an allyl diglycol carbonate lens comprising steps of (1) treating at least one surface of said lens with an aqueous alkaline solution to hydrolyze said surface; (2) applying on said treated surface an aqueous coating composition comprising a mixture of an acid polysilicic ester of an alcohol containing from 1 to 12 carbon atoms and having up to four silicic acid ester groups per silicon atom, and a polyvinyl alcohol comprising 90% to 100% hydrolyzed polyvinyl acetate; and (3) drying and curing said coating composition at an elevated temperature.
Claim 6
Dependent Claim
93 words
A process for coating an allyl diglycol carbonate lens comprising steps of (1) treating at least one surface of said lens with an aqueous alkaline solution to hydrolyze said surface; (2) applying on said treated surface an aqueous coating composition comprising a mixture of an acid polysilicic ester of an alcohol containing from 1 to 12 carbon atoms and having up to four silicic acid ester groups per silicon atom, and a polyvinyl alcohol comprising 90% to 100% hydrolyzed polyvinyl acetate; and (3) drying and curing said coating composition at an elevated temperature.
Claim 7
Dependent Claim
72 words
The process of claim 4 wherein (a) all surfaces of said lens are coated with said coating composition, (b) said composition further contains a C1 to C4 carbon chain alcohol, (c) said drying step includes drying a proportion of the volatiles from said coating composition at approximately room temperature, and (4) said curing step includes baking said coating composition on said lens at an elevated temperature of about 90°C to about 125°C.
Claim 8
Dependent Claim
11 words
The process of claim 5 wherein said alcohol is methyl alcohol.
Claim 9
Dependent Claim
15 words
The process of claim 6 wherein said coating is applied by spin coating said lens.
Claim 10
Dependent Claim
18 words
The process of claim 6 wherein said coating is applied by dipping said lens into said coating composition.
Claim 11
Dependent Claim
24 words
The process of claim 8 wherein said hydrolyzed surface of said lens is effected by treating said lens with an aqueous solution of caustic.
Claim 12
Dependent Claim
19 words
The process of claim 9 wherein said caustic is selected from the group consisting of sodium or potassium hydroxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-27 | 1980-01-26 | 1980-07-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-27 | 1984-01-26 | 1984-07-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-27 | 1988-01-26 | 1988-07-27 | $7700.00 | Window Closed / Lapsed |