Process for the preparation of hollow microspheres
Assignee: Rio Tinto Alcan International Ltd
•
Filing: 1987-09-23
•
Granted: 1988-11-01
•
Expires: 2007-09-23
Abstract
Abstract A process for forming hollow microspheres containing carbon or a polymer which is a carbon precursor. The process comprises forming a solution in a liquid solvent of a polymer having the following properties (a) a molecular weight of at least 10,000 and a long chain structure; (b) an ability to be coagulated by or precipitated from the solution by a non-solvent for the polymer; (c) an ability to form a continuous stretchable film when coagulated or precipitated from solution; (d) a chemical structure which is infusible or capable of being rendered infusible, and (e) a high carbon yield of at least 30% by weight upon being carbonized in a non-reactive atmosphere. An insoluble particulate blowing agent is incorporated into the solution and the solution is then divided into droplets and the droplets are introduced into a liquid bath containing a suitable non-solvent for the polymer. The non-solvent causes the polymer to precipitate or coagulate rapidly and simultaneously the blowing agent is decomposed to generate a gas within the droplets so that hollow microspheres are formed. The microspheres are then optionally subjected to carbonization in a non-reactive atmosphere at high temperature to convert the polymer to carbon. Uniformly-sized relatively large hollow microspheres can be produced by this process.
Inventors
- 👤 Mukesh Jain
- 👤 Sadashiv Nadkarni
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 16:51
CPC Classifications
B; B01; B01J; B01J13/00; B01J13/02; B01J13/20; B01J13/06; B01J13/12; C; C08; C08J; C08J3/00; C08J3/12; C08J3/14; C08J9/00; C08J9/04; C08J9/06; C08J9/08
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
189 words
A process of forming hollow microspheres, which comprises: forming a solution in a liquid solvent of a polymer having the following properties: (a) a molecular weight of at least 10,000 and a long chain structure of at least 200 monomer units; (b) an ability to be coagulated or precipitated from the solution upon contact of the solution with a non-solvent for the polymer; (c) an ability to form a continuous stretchable film when coagulated or precipitated from solution; (d) a chemical structure which is infusible or which is capable of being rendered infusible; and (e) a high carbon yield of at least 30% by weight upon being carbonized in a non-reactive atmosphere; incorporating into said solution an insoluble solid particulate blowing agent which is decomposable by heat to generate a gas; dividing the solution into droplets and introducing the droplets into a liquid bath containing a non-solvent for the polymer, said non-solvent being such that the polymer is rapidly coagulated or precipitated from the solution, and said bath having a temperature high enough to cause decomposition of the blowing agent; and removing the resulting hollow microspheres from the bath.
Claim 2
Dependent Claim
189 words
A process of forming hollow microspheres, which comprises: forming a solution in a liquid solvent of a polymer having the following properties: (a) a molecular weight of at least 10,000 and a long chain structure of at least 200 monomer units; (b) an ability to be coagulated or precipitated from the solution upon contact of the solution with a non-solvent for the polymer; (c) an ability to form a continuous stretchable film when coagulated or precipitated from solution; (d) a chemical structure which is infusible or which is capable of being rendered infusible; and (e) a high carbon yield of at least 30% by weight upon being carbonized in a non-reactive atmosphere; incorporating into said solution an insoluble solid particulate blowing agent which is decomposable by heat to generate a gas; dividing the solution into droplets and introducing the droplets into a liquid bath containing a non-solvent for the polymer, said non-solvent being such that the polymer is rapidly coagulated or precipitated from the solution, and said bath having a temperature high enough to cause decomposition of the blowing agent; and removing the resulting hollow microspheres from the bath.
Claim 3
Dependent Claim
28 words
A process according to claim 1, wherein said polymer is selected from the group consisting of polyacrylonitrile and copolymers and terpolymers of acrylonitrile and other monomers copolymerizable therewith.
Claim 4
Dependent Claim
27 words
A process according to claim 2 wherein said copolymers and terpolymers include up to 25% by weight of units derived from said monomers copolymerizable with the acrylonitrile.
Claim 5
Dependent Claim
28 words
A process according to claim 2 wherein said copolymers and terpolymers include up to about 10% by weight of units derived from said monomers copolymerizable with the acrylonitrile.
Claim 6
Dependent Claim
23 words
A process according to claim 2, which said monomers copolymerizable with the acrylonitrile are selected from the group consisting of methacrylate and methylmethacrylate.
Claim 7
Dependent Claim
21 words
A process according to claim 2 wherein the liquid solvent is selected from the group consisting of dimethylformamide, dimethylsulfoxide and dimethylacetamide.
Claim 8
Dependent Claim
11 words
A process according to claim 2 wherein the solvent is dimethylformamide.
Claim 9
Dependent Claim
20 words
A process according to claim 7 wherein the non-solvent is selected from the group consisting of water and water-dimethylformamide mixtures.
Claim 10
Dependent Claim
21 words
A process according to claim 1 wherein said polymer is selected from the group consisting of polyvinyl alcohol and its copolymers.
Claim 11
Dependent Claim
13 words
A process according to claim 9 wherein said liquid solvent is dimethyl formamide.
Claim 12
Dependent Claim
13 words
A process according to claim 10 wherein said non-solvent is methyl ethyl ketone.
Claim 13
Dependent Claim
22 words
A process according to claim 1 wherein the viscosity of the solution is within the range of 200-5000 cp at 25° C.
Claim 14
Dependent Claim
31 words
A process according to claim 1 wherein a particulate solid other than the blowing agent is introduced into the solution and uniformly dispersed therein before the solution is divided into droplets.
Claim 15
Dependent Claim
20 words
A process according to claim 13 wherein said particulate solid comprises particles of a size less than 100 Tyler mesh.
Claim 16
Dependent Claim
28 words
A process according to claim 13 wherein the particulate solid is selected from the group consisting of fine coke dusts, metals, metal oxides, metal fluorides, and activated carbon.
Claim 17
Dependent Claim
14 words
A process according to claim 15 wherein the particulate solid is AlF 3 .
Claim 18
Dependent Claim
23 words
A process according to claim 1 wherein a soluble material is dissolved in the polymer solution before the solution is divided into droplets.
Claim 19
Dependent Claim
22 words
A process according to claim 17 wherein said soluble material is selected from the group consisting of tar, pitch and phenolic resins.
Claim 20
Dependent Claim
33 words
A process according to claim 1 wherein the solution is divided into droplets by feeding the solution through a hollow tube and allowing droplets to fall from a free end of said tube.
Claim 21
Dependent Claim
20 words
A process according to claim 1 wherein the temperature of the bath is below the boiling point of the non-solvent.
Claim 22
Dependent Claim
22 words
A process according to claim 1 wherein the hollow microspheres removed from the bath are dried by heating them gently in air.
Claim 23
Dependent Claim
41 words
A process according to claim 1 wherein the polymer used to form the solution is heat-fusible but capable of being rendered infusible, and wherein the hollow microspheres removed from the bath are subjected to a treatment which renders the polymer infusible.
Claim 24
Dependent Claim
39 words
A process according to claim 2 wherein the hollow microspheres removed from the bath are subjected to a heat stabilization treatment which comprises heating them in air at a temperature in the range of 200°-210° C. for 8 hours.
Claim 25
Dependent Claim
35 words
A process according to claim 1, wherein the hollow microspheres are subjected to carbonization by heating the microspheres in a non-oxidizing atmosphere at a temperature and for a time which converts the polymer to carbon.
References Cited (Backward Citations)
US2797201A
Cited
US2806509A
Cited
US3312632A
Cited
US3615972A
Cited
US3607169A
Cited
DE2136288A1
Cited
US3873475A
Cited
US3927181A
Cited
DE2353090A1
Cited
US3937775A
Cited
US4009232A
Cited
DE2413930A1
Cited
GB1457013A
Cited
US3914360A
Cited
US3975194A
Cited
CA1034331A
Cited
JPS51104495A
Cited
US4126652A
Cited
US4349456A
Cited
US4133854A
Cited
WO1980000426A1
Cited
US4303729A
Cited
US4327192A
Cited
US4444894A
Cited
US4686244A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-11-01 | 1992-05-02 | 1992-11-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-11-01 | 1996-05-02 | 1996-11-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-11-01 | 2000-05-02 | 2000-11-01 | $7700.00 | Window Closed / Lapsed |