Process for preparation of a metal carbide-containing molded product
Assignee: Toyobo Co Ltd
•
Filing: 1977-02-25
•
Granted: 1978-11-21
•
Expires: 1997-02-25
Abstract
Abstract A process for preparation of a metal carbide-containing molded product which comprises heating a molded composition comprising at least one powdery metal selected from the group consisting of B, Ti, Si, Zr, Hf, V, Nb, Ta, Mo, W, Cr, Fe and U and having an average particle size of not more than about 50 μ and an acrylonitrile polymer at a temperature of about 200° to 400° C and then calcining the resulting product at a temperature of about 900° to 2500° C in an inert atmosphere.
Inventors
- 👤 Kunio Oohara
- 👤 Tatsuhiko Shizuki
- 👤 Hideyuki Mitamura
- 👤 Masahiro Sugino
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 00:45
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/62227; C04B35/62272; C04B35/62277; B; B82; B82Y; B82Y30/00; C01; C01B; C01B32/00; C01B32/90; C01B32/914; C01B32/949; C01B32/956; C01B32/963; C01B32/984; C01B32/991; C04B35/515; C04B35/56; C04B35/5607; C04B35/5611; C04B35/5622; C04B35/5626; C04B35/563; C04B35/62281; C01P; C01P2002/00; C01P2002/50; C01P2002/52; C01P2002/54; C01P2002/70; C01P2002/72; C01P2004/00; C01P2004/10; C01P2004/60; C01P2004/61; C01P2004/62; C01P2004/64; C01P2006/00; C01P2006/80; C01P2006/90; Y; Y10; Y10S; Y10S264/00; Y10S264/19
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
116 words
A process for the preparation of a metal carbide-containing molded product which comprises heating a molded composition comprising at least one powdery metal selected from the group consisting of B, Ti, Si, Zr, Hf, V, Nb, Ta, Mo, W, Cr, Fe and U and having an average particle size of not more than about 50μ and an acrylonitrile polymer at a temperture of about 200° to 400° C. and then calcining the resulting product at a temperature of about 900° to 2500° C. in an inert atmosphere, said powdery metal being present in an amount of from about 5 to 90% by weight based on the total weight of the acrylonitrile polymer and the powdery metal.
Claim 2
Dependent Claim
116 words
A process for the preparation of a metal carbide-containing molded product which comprises heating a molded composition comprising at least one powdery metal selected from the group consisting of B, Ti, Si, Zr, Hf, V, Nb, Ta, Mo, W, Cr, Fe and U and having an average particle size of not more than about 50μ and an acrylonitrile polymer at a temperture of about 200° to 400° C. and then calcining the resulting product at a temperature of about 900° to 2500° C. in an inert atmosphere, said powdery metal being present in an amount of from about 5 to 90% by weight based on the total weight of the acrylonitrile polymer and the powdery metal.
Claim 3
Dependent Claim
20 words
The process according to claim 1, wherein the heating of the molded composition is carried out in an oxidizing atmosphere.
Claim 4
Dependent Claim
12 words
The process according to claim 2, wherein the oxidizing atmosphere is air.
Claim 5
Dependent Claim
20 words
The process according to claim 1, wherein the particle size of the powdery metal is not more than about 10μ.
Claim 6
Dependent Claim
34 words
The process according to claim 1, wherein the amount of the powdery metal is from about 10 to 70% by weight based on the total weight of the acrylonitrile polymer and the powdery metal.
Claim 7
Dependent Claim
15 words
The process according to claim 1, wherein the molded composition further comprises a calcining aid.
Claim 8
Dependent Claim
18 words
The process according to claim 1, wherein the molded composition is in the form of fiber or film.
Claim 9
Dependent Claim
29 words
The process according to claim 1, wherein the heating and/or the calcining are carried out on the molded composition in the form of fiber or film under a tension.
Claim 10
Dependent Claim
128 words
A process for the preparation of a metal carbide-containing molded product which comprises forming a molded composition comprising at least one powdery metal selected from the group consisting of B, Ti, Si, Zr, Hf, V, Nb, Ta, Mo, W, Cr, Fe, and U, having an average particle size of not more than about 50 microns and an acrylonitrile polymer, heating said molded composition at a temperature of about 200° to 400° C., and then calcining the resulting product at a temperature of about 900° to 2500° C. in an inert atmosphere to directly form said metal carbide-containing molded product, said powdery metal being present in an amount of from about 5 to 90% by weight based on the total weight of the acrylonitrile polymer and the powdery metal.
Claim 11
Dependent Claim
128 words
A process for the preparation of a metal carbide-containing molded product which comprises forming a molded composition comprising at least one powdery metal selected from the group consisting of B, Ti, Si, Zr, Hf, V, Nb, Ta, Mo, W, Cr, Fe, and U, having an average particle size of not more than about 50 microns and an acrylonitrile polymer, heating said molded composition at a temperature of about 200° to 400° C., and then calcining the resulting product at a temperature of about 900° to 2500° C. in an inert atmosphere to directly form said metal carbide-containing molded product, said powdery metal being present in an amount of from about 5 to 90% by weight based on the total weight of the acrylonitrile polymer and the powdery metal.
Claim 12
Dependent Claim
52 words
The process of claim 9, wherein the molded composition is formed by subjecting a monomer mixture mainly comprising acrylonitrile to solution polymerization with the addition of the powdery metal thereto either in the course of the polymerization or after the polymerization so as to disperse said powdery metal into the polymerization mixture.
Claim 13
Dependent Claim
38 words
The process of claim 9, wherein the molded composition is formed by dispersing the powdery metal into a solution of the acrylonitrile polymer in a suitable solvent, and then subjecting the thus obtained powdery metal-containing mixture to molding.
Claim 14
Dependent Claim
35 words
The process of claim 9, wherein the molded composition is formed by admixing powdery acrylonitrile polymer with the powdery metal while adding an appropriate amount of water thereto, and subjecting the mixture to melt extrusion.
Claim 15
Dependent Claim
24 words
The process of claim 9, wherein the molded product is placed under tension during heat treatment and calcination to enhance the physical properties thereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-20 | 1982-05-22 | 1982-11-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-20 | 1986-05-22 | 1986-11-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-20 | 1990-05-22 | 1990-11-21 | $7700.00 | Window Closed / Lapsed |