Intumescent foamable compositions
Assignee: Dow Silicones Corp
•
Filing: 1986-12-17
•
Granted: 1987-08-11
•
Expires: 2006-12-17
Abstract
Abstract The intumescent material of this invention comprises a filled polyorganosiloxane composition that is elastomeric in the cured form and up to 70 parts by weight per 100 parts by weight of said composition of hollow, thermoplastic microspheres filled with a volatile liquid. The materials are particularly useful as flame and smoke barriers in passages of partitions that are traversed by thermoplastic articles such as pipes and conduits, and can optionally contain chemical blowing agents.
Inventors
- 👤 John E. Dietlein
- 👤 Thomas C. Hampton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 22:44
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/12; C08J9/14; C08J9/141; C08K; C08K9/00; C08K9/10; C09; C09K; C09K21/00; C09K21/14; C08J2383/00; C08J2383/04; Y; Y10; Y10S; Y10S428/00; Y10S428/92; Y10S521/00; Y10S521/907
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
107 words
A method for forming a flame and smoke barrier in a passage through a partition where said passage is traversed by at least one thermoplastic article, said method comprising sealing at least a portion of the length of said passage with an intumescent material comprising 100 parts by weight of a curable, filled polyorganosiloxane composition containing a latent curing agent that is convertible upon curing to a flame retardant elastomer; and from 1 to 70 parts by weight of expandable hollow microspheres formed from a thermoplastic organic polymer and containing therein a liquid having a boiling point of from 50° to about 200° C. under atmospheric pressure.
Claim 2
Independent Claim
107 words
A method for forming a flame and smoke barrier in a passage through a partition where said passage is traversed by at least one thermoplastic article, said method comprising sealing at least a portion of the length of said passage with an intumescent material comprising 100 parts by weight of a curable, filled polyorganosiloxane composition containing a latent curing agent that is convertible upon curing to a flame retardant elastomer; and from 1 to 70 parts by weight of expandable hollow microspheres formed from a thermoplastic organic polymer and containing therein a liquid having a boiling point of from 50° to about 200° C. under atmospheric pressure.
Claim 3
Dependent Claim
65 words
A method according to claim 1, where the polyorganosiloxane composition comprises a polydiorganosiloxane wherein the repeating units are of the formula RR'SiO. where R and R' represent identical or different monovalent hydrocarbon or halogenated hydrocarbon radicals, a curing agent for said polydiorganosiloxane and at least one filler, and the boiling point of said organic liquid is from 50° to 200 degrees C. under atmospheric pressure.
Claim 4
Dependent Claim
74 words
A method according to claim 2 where R and R' are individually selected from the group consisting of alkyl radicals containing from 1 to 4 carbon atoms, alkenyl containing 2 or 3 carbon atoms, fluoroalkyl containing from 1 to 4 carbon atoms and phenyl, the filler comprises at least one member selected from the group consisting of silica, quartz and alkali metal silicates, and said polyorganosiloxane composition includes at least one flame retarding agent.
Claim 5
Dependent Claim
35 words
A method according to claim 3 where R is methyl and R' is either methyl or 3,3,3-trifluoropropyl and the flame retarding agent comprises platinum, a platinum compound, a metal oxide or a hydrated metal oxide.
Claim 6
Dependent Claim
39 words
A method according to claim 4 where said flame retarding agent comprises the combination of platinum or a platinum compound with at least one member selected from the group consisting of carbon black, hydrated alumina and hydrated cerri oxide.
Claim 7
Dependent Claim
47 words
A method according to claim 3 where said polydiorganosiloxane contains two vinyl radicals per molecule, said curing agent is a polyorganohydrogensiloxane containing an average of at least three silicon bonded hydrogen atoms per molecule and the polyorganosiloxane composition includes a catalytically effective amount of a hydrosilation catalyst.
Claim 8
Dependent Claim
14 words
A method according to claim 6 where said hydrosilation catalyst is a platinum compound.
Claim 9
Dependent Claim
14 words
A method according to claim 3 where said curing agent is an organic peroxide.
Claim 10
Dependent Claim
36 words
A method according to claim 3 where the concentration of said microspheres constitutes from 10 to 50 parts by weight per 100 parts by weight of said material and said composition contains a chemical blowing agent.
Claim 11
Dependent Claim
17 words
A method according to claim 9 where said blowing agent is an alkali metal carbonate or bicarbonate.
Claim 12
Dependent Claim
42 words
A method according to claim 10 where blowing agent is sodium bicarbonate and said intumescent material is in the form of a putty or paste that remains in an uncured form until exposed to a temperature of at least 150 degrees C.
Claim 13
Dependent Claim
16 words
A method according to claim 3 where said article is formed from a thermoplastic organic polymer.
Claim 14
Dependent Claim
23 words
A method according to claim 12 where said thermoplastic polymer is selected from the group consisting of polyvinyl chloride, polybutadiene and acrylonitrile/butadiene/styrene terpolymers.
Claim 15
Dependent Claim
14 words
A method according to claim 13 where said article is a pipe or conduit.
References Cited (Backward Citations)
CA715140A
Cited
US3317455A
Cited
US3429838A
Cited
US3553002A
Cited
US4072635A
Cited
US4000108A
Cited
US4031059A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-10 | 1991-02-09 | 1991-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-10 | 1995-02-09 | 1995-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-10 | 1999-02-09 | 1999-08-11 | $7700.00 | Window Closed / Lapsed |