Preform with internal barrier and products made from the same
Assignee: Graham Packaging Pet Technologies Inc
•
Filing: 1986-05-12
•
Granted: 1988-11-01
•
Expires: 2006-05-12
Abstract
Abstract This relates to laminated preforms, the method of forming such preforms and products which may be beneficially formed utilizing such preforms. Most particularly, this relates to a preform which has formed as part of the injection molding thereof two layers of barrier material which are disposed within two layers of thermoplastic resin and having received therebetween a solid core of thermoplastic resin. The specific method of forming the preform permits the barrier material layers to be of a greatly reduced thickness as compared to such layer thicknesses permissible in the past, with the result that the barrier material layers in the blow molded articles are of a thickness recognized to be acceptable for the barrier function. The barrier material layers may be selectively terminated along the length of the preform so as to permit portions of the resultant blow molded article to be removed and reused. This abstract is not to be construed as limiting the claims of the application.
Inventors
- 👤 Suppayan M. Krishnakumar
- 👤 Thomas E. Nahill
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 21:44
CPC Classifications
B; B29; B29C; B29C45/00; B29C45/16; B29C45/1642; B29C45/1643; B29C49/00; B29C49/42; B29C49/78; B29C2049/7879; B29C2793/00; B29C2793/009; B29C2949/00; B29C2949/07; B29C2949/081; B29C2949/0811; B29C2949/0819; B29C2949/20; B29C2949/22; B29C2949/24; B29C2949/30; B29C2949/3008; B29C2949/3009; B29C2949/3012; B29C2949/3016; B29C2949/3018; B29C2949/302; B29C2949/3024; B29C2949/3026; B29C2949/3028; B29C2949/303; B29C2949/3032; B29C2949/3064; B29C2949/3074; B29C2949/3076; B29C49/08; B29C49/087; B29C49/42394; B29C49/72; B29C49/74; B29C49/76; B29C49/761; B29K; B29K2105/00; B29K2105/26; B29K2995/00; B29K2995/0037; B29K2995/0068; B29K2995/0069; B29L; B29L2031/00; B29L2031/712; B29L2031/7158; B29L2031/716; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1379; Y10T428/31504; Y10T428/31786; Y10T428/31797
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
90 words
A laminated preform for forming blow mold articles, said preform being of the type formed by solely injection molding in a single conventional injection mold unit and including a tubular wall having inner and outer surfaces, said tubular wall in radial cross section comprising inner and outer first layers of an identical coinjected thermoplastic resin, very thin inner and outer layers of an identical coinjected gas barrier material next to and between said inner and outer first layers, and a second layer of thermoplastic resin between said barrier material layers.
Claim 2
Dependent Claim
90 words
A laminated preform for forming blow mold articles, said preform being of the type formed by solely injection molding in a single conventional injection mold unit and including a tubular wall having inner and outer surfaces, said tubular wall in radial cross section comprising inner and outer first layers of an identical coinjected thermoplastic resin, very thin inner and outer layers of an identical coinjected gas barrier material next to and between said inner and outer first layers, and a second layer of thermoplastic resin between said barrier material layers.
Claim 3
Dependent Claim
27 words
A laminated preform according to claim 1 wherein the combined thickness of said inner and outer layers of barrier material is on the order of 0.006 inch.
Claim 4
Dependent Claim
35 words
A laminated preform according to claim 1 wherein said preform has a rounded base including an endmost part, and said endmost part is formed solely by the material of said first layers of thermoplastic resin.
Claim 5
Dependent Claim
30 words
A laminated preform according to claim 1 wherein said preform has an open end and said layers of barrier material terminate in said tubular wall remote from said open end.
Claim 6
Dependent Claim
24 words
A laminated preform according to claim 1 wherein said layers of barrier material terminate between said first and second layers of said thermoplastic resin.
Claim 7
Dependent Claim
35 words
A laminated preform according to claim 1 wherein said preform is for forming a blow molded container having a neck finish, and said barrier material layers terminate adjacent to but short of said neck finish.
Claim 8
Dependent Claim
26 words
A laminated preform according to claim 1 wherein said second layer of thermoplastic resin is of a material different from said first layers of thermoplastic resin.
Claim 9
Dependent Claim
28 words
A laminated preform according to claim 7 wherein said first layers of thermoplastic is a virgin resin and said second layer of thermoplastic resin is a reclaimed resin.
Claim 10
Dependent Claim
21 words
A laminated preform according to claim 8 wherein said virgin resin and said reclaimed resin are substantially of the same material.
Claim 11
Dependent Claim
29 words
A laminated preform according to claim 1 wherein said layers of barrier material are tightly compressed between adjacent ones of said layers to form diffusion bonds with adjacent layers.
Claim 12
Dependent Claim
13 words
A blow molded container formed by blow molding the preform of claim 1.
Claim 13
Dependent Claim
24 words
A blow molded container according to claim 11 wherein said layers of barrier material have a combined thickness on the order of 0.0006 inch.
Claim 14
Dependent Claim
19 words
A blow molded container according to claim 11 wherein said layers of barrier material extend through said neck finish.
Claim 15
Dependent Claim
22 words
A blow molded container according to claim 11 wherein said layers of barrier material extend into and terminate in said neck finish.
Claim 16
Dependent Claim
25 words
A blow molded container according to claim 11 wherein said layers of barrier material extend to and terminate in an area adjacent said neck finish.
Claim 17
Dependent Claim
27 words
A blow molded container according to claim 11 wherein said further layer of thermoplastic resin is of a material different from said first layer of thermoplastic resin.
Claim 18
Dependent Claim
28 words
A blow molded container according to claim 11 wherein there are diffusion bonds between said barrier material layers and said first layers and further layer of thermoplastic resin.
Claim 19
Dependent Claim
36 words
A blow molded container according to claim 11 wherein there are diffusion bonds between said barrier material layers and said first layers and further layer of thermoplastic resin, and all of said layers are biaxially oriented.
Claim 20
Independent Claim
223 words
A method of forming a blow molded hollow member comprising the steps of forming by injection molding in sequence in a single conventional injection mold for a preform first thermoplastic resin to form in cross section inner and outer first layers of a tubular body of a preform formed of said first thermoplastic resin, a gas barrier material to form very thin inner and outer layers of the barrier material next to and between said inner and outer first layers, and a second thermoplastic resin forming a core layer between said barrier material layers with said barrier material layers being free of heat bonds with said inner and outer first layers and said core, and with said barrier material layers being tightly compressed between said core layer and a respective one of said inner and outer first layers with each of said barrier material layers being tightly compressed between adjacent ones of said core layer and said inner and outer first layers to form compression diffusion bonds between each of said barrier layer and said core layer and the respective one of said inner and outer first layers, and blow molding the preform into a hollow member while biaxially stretching the layers and reducing the thickness of the layers with the thickness of said intermediate layer being reduced to a substantially incompressible thickness.
Claim 21
Independent Claim
223 words
A method of forming a blow molded hollow member comprising the steps of forming by injection molding in sequence in a single conventional injection mold for a preform first thermoplastic resin to form in cross section inner and outer first layers of a tubular body of a preform formed of said first thermoplastic resin, a gas barrier material to form very thin inner and outer layers of the barrier material next to and between said inner and outer first layers, and a second thermoplastic resin forming a core layer between said barrier material layers with said barrier material layers being free of heat bonds with said inner and outer first layers and said core, and with said barrier material layers being tightly compressed between said core layer and a respective one of said inner and outer first layers with each of said barrier material layers being tightly compressed between adjacent ones of said core layer and said inner and outer first layers to form compression diffusion bonds between each of said barrier layer and said core layer and the respective one of said inner and outer first layers, and blow molding the preform into a hollow member while biaxially stretching the layers and reducing the thickness of the layers with the thickness of said intermediate layer being reduced to a substantially incompressible thickness.
Claim 22
Dependent Claim
23 words
A method according to claim 19 wherein the thickness of said intermediate layer in said preform is on the order of 0.003 inch.
Claim 23
Dependent Claim
24 words
A method according to claim 19 wherein the thickness of said intermediate layer in said hollow member is on the order of 0.0003 inch.
Claim 24
Dependent Claim
31 words
A method according to claim 19 wherein in the forming of said preform said intermediate layer is compressed at a pressure of 15,000 to 17,000 p.s.i. to effect said diffusion bond.
Claim 25
Dependent Claim
52 words
A method according to claim 19 wherein in the forming of said preform said intermediate layer is compressed at a pressure of 15,000 to 17,000 p.s.i. to effect said diffusion bond, and a high pressure is maintained as said preform cools and sets to prevent separation between the layers due to shrinkage.
References Cited (Backward Citations)
US4109037A
Cited
US4174413A
Cited
US4393106A
Cited
US4532305A
Cited
US4528219A
Cited
US4534930A
Cited
US4513037A
Cited
US4550043A
Cited
US4609516A
Cited
US4710118A
Cited
US4728549A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-11-01 | 1992-05-02 | 1992-11-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-11-01 | 1996-05-02 | 1996-11-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-11-01 | 2000-05-02 | 2000-11-01 | $7700.00 | Window Closed / Lapsed |