Low temperature plasma nitridation process and applications of nitride films formed thereby
Assignee: National Semiconductor Corp
•
Filing: 1985-11-26
•
Granted: 1988-08-09
•
Expires: 2005-11-26
Abstract
Abstract A silicon nitride layer is prepared on the surface of a silicon substrate by carrying out a surface reaction on the substrate in a vacuum chamber that contains an electrode which is capacitively coupled to an rf generator. A second electrode within the chamber, or a metal wall of the chamber itself, is connected to ground. The silicon substrates to be treated are placed on one of the electrodes to be in electrical and physical contact therewith, and a reagent gas that contains nitrogen is introduced into the chamber. An rf voltage is then applied between the electrodes to ionize and activate the gas, and cause ions and other active species thereof to be directed into the silicon substrate. The nitrogen ions and other active species that are created as a result of the application of the rf power can be directed at the surface of a number of wafers simultaneously. The thin nitride films that are formed by the process have application both as barriers for device isolation and as dielectric components of electrical devices.
Inventors
- 👤 Thomas Keyser
- 👤 Bruce R. Cairns
- 👤 Kranti V. Anand
- 👤 William G. Petro
- 👤 Michael L. Barry
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 06:38
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6336; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/013; H10D64/01302; H10D64/01332; H10D64/01336; H10D64/0134; H10D64/01344; H10D64/60; H10D64/66; H10D64/68; H10D64/681; H10D64/685; H10D64/693; H10P14/65; H10P14/6516; H10P14/6529; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/014; H10W10/041; H10W10/10; H10W10/13; H10W10/17; H10W10/40; H10P14/6302; H10P14/6319; H10P14/69; H10P14/692; H10P14/6921; H10P14/69215; H10P14/694; H10P14/6943; H10P14/69433
Claims Analysis
Total Claims: 39
Claim 1
Independent Claim
112 words
A method of inducing a surface reaction on a silicon substrate to provide a thin film of silicon nitride or other nitrogen-containing composition on the silicon substrate, comprising the steps of: placing the silicon substrate in contact with one of a pair of electrodes; evacuating a chamber in which said electrodes and the substrate are located; introducing a nitrogen-containing reagent gas into the chamber; and applying an a.c. voltage having a frequency of about 10 KHz or greater between said electrodes to thereby ionize and activate the reagent gas and accelerate ions thereof into the substrate and thereby cause said ions to react with silicon of the substrate to form the film.
Claim 2
Independent Claim
112 words
A method of inducing a surface reaction on a silicon substrate to provide a thin film of silicon nitride or other nitrogen-containing composition on the silicon substrate, comprising the steps of: placing the silicon substrate in contact with one of a pair of electrodes; evacuating a chamber in which said electrodes and the substrate are located; introducing a nitrogen-containing reagent gas into the chamber; and applying an a.c. voltage having a frequency of about 10 KHz or greater between said electrodes to thereby ionize and activate the reagent gas and accelerate ions thereof into the substrate and thereby cause said ions to react with silicon of the substrate to form the film.
Claim 3
Dependent Claim
19 words
The method of claim 1 wherein said reagent gas comprises one of pure nitrogen, ammonia and a nitrogen-hydrogen mixture.
Claim 4
Dependent Claim
23 words
The method of claim 1 wherein said a.c. voltage is capacitively coupled to said one electrode to thereby provide a d.c. bias thereto.
Claim 5
Dependent Claim
20 words
The method of claim 1 further including the step of cooling said one electrode to inhibit heating of said substrate.
Claim 6
Dependent Claim
16 words
The method of claim 4 wherein the temperature of said substrate is less than 200° C.
Claim 7
Dependent Claim
20 words
The method of claim 1 further including the step of annealing the thin film of nitride formed on said substrate.
Claim 8
Dependent Claim
19 words
The method of claim 6 wherein said annealing step is carried out in the presence of a non-oxidizing gas.
Claim 9
Dependent Claim
16 words
The method of claim 6 wherein said annealing is carried out in the presence of oxygen.
Claim 10
Dependent Claim
20 words
The method of claim 1 wherein said one electrode comprises a plate which supports said silicon substrate in said chamber.
Claim 11
Dependent Claim
20 words
The method of claim 9 wherein said electrodes are spaced from one another and said substrate is disposed between them.
Claim 12
Dependent Claim
30 words
The method of claim 1 wherein the area of the other electrode of said pair of electrodes is at least twice as great as the area of said one electrode.
Claim 13
Dependent Claim
16 words
The method of claim 1 wherein the temperature of the substrate is maintained below 200° C.
Claim 14
Independent Claim
128 words
A method for isolating active regions from one another in an integrated circuit, comprising the steps of: generating a plasma by introducing a nitrogen-containing gas between a pair of spaced plate electrodes and applying an rf frequency to the electrodes; placing a silicon wafer in contact with one of said electrodes to thereby cause ions of the plasma to react with silicon of the wafer and a nitride film to be formed on a surface of the wafer; removing select portions of said film so that the remaining portions of the film correspond to areas in which active devices are to be formed in the wafer; and oxidizing the areas on said surface of the wafer that are not covered by the remaining portions of the nitride film.
Claim 15
Independent Claim
128 words
A method for isolating active regions from one another in an integrated circuit, comprising the steps of: generating a plasma by introducing a nitrogen-containing gas between a pair of spaced plate electrodes and applying an rf frequency to the electrodes; placing a silicon wafer in contact with one of said electrodes to thereby cause ions of the plasma to react with silicon of the wafer and a nitride film to be formed on a surface of the wafer; removing select portions of said film so that the remaining portions of the film correspond to areas in which active devices are to be formed in the wafer; and oxidizing the areas on said surface of the wafer that are not covered by the remaining portions of the nitride film.
Claim 16
Dependent Claim
28 words
The method of claim 13 wherein said rf frequency signal has a power density in the range of about 1.6 to about 3.2 W/cm 2 of the wafer.
Claim 17
Dependent Claim
17 words
The method of claim 13 wherein said nitride film has a thickness no greater than 200 angstroms.
Claim 18
Dependent Claim
21 words
The method of claim 15 wherein said film has a thickness in the range of about 50 to about 100 angstroms.
Claim 19
Dependent Claim
19 words
The method of claim 13 wherein the ratio of nitrogen to nitrogen-plus-oxygen in said film is at least 90%.
Claim 20
Dependent Claim
17 words
The method of claim 13 further including the step of providing a d.c. bias to said electrodes.
Claim 21
Dependent Claim
16 words
The method of claim 13 wherein the pressure of said plasma is about 10 -2 Torr.
Claim 22
Dependent Claim
29 words
The method of claim 13 wherein said surface of the wafer has a trench in it, and said nitride film remains in the trench after said selective removing step.
Claim 23
Independent Claim
125 words
A method for dielectrically isolating active regions from one another in an integrated circuit, comprising the steps of: forming a trench in the surface of a silicon wafer to define a boundary of at least one area in which an active device is to be located; placing the wafer in contact with one of a pair of spaced plate electrodes; introducing a nitrogen-containing gas between said electrodes; applying an rf frequency signal to said electrodes to thereby create a nitrogen plasma and cause ions of the plasma to react with silicon of the wafer and a nitride film to be formed on said surface of the wafer and along the walls of said trench; and filling the remainder of said trench with an insulating material.
Claim 24
Independent Claim
125 words
A method for dielectrically isolating active regions from one another in an integrated circuit, comprising the steps of: forming a trench in the surface of a silicon wafer to define a boundary of at least one area in which an active device is to be located; placing the wafer in contact with one of a pair of spaced plate electrodes; introducing a nitrogen-containing gas between said electrodes; applying an rf frequency signal to said electrodes to thereby create a nitrogen plasma and cause ions of the plasma to react with silicon of the wafer and a nitride film to be formed on said surface of the wafer and along the walls of said trench; and filling the remainder of said trench with an insulating material.
Claim 25
Dependent Claim
18 words
The method of claim 21 wherein said film has a thickness of about 50 to about 70 angstroms.
Claim 26
Dependent Claim
28 words
The method of claim 21 wherein said rf frequency signal has a power density in the range of about 1.6 to about 3.2 W/cm 2 on the wafer.
Claim 27
Dependent Claim
19 words
The method of claim 21 wherein the ratio of nitrogen to nitrogen-plus-oxygen in said film is at least 90%.
Claim 28
Independent Claim
93 words
A method of providing a dielectric film which forms a component of an electrical device in an integrated circuit, comprising the steps of: generating a plasma by introducing a nitrogen-containing gas between a pair of spaced plate electrodes and applying an rf frequency signal to the electrodes; placing a silicon wafer in contact with one of said electrodes to thereby cause ions in said plasma to react with silicon of the wafer and a nitride film to be formed on said wafer; and annealing said wafer and said film in an oxidizing atmosphere.
Claim 29
Independent Claim
93 words
A method of providing a dielectric film which forms a component of an electrical device in an integrated circuit, comprising the steps of: generating a plasma by introducing a nitrogen-containing gas between a pair of spaced plate electrodes and applying an rf frequency signal to the electrodes; placing a silicon wafer in contact with one of said electrodes to thereby cause ions in said plasma to react with silicon of the wafer and a nitride film to be formed on said wafer; and annealing said wafer and said film in an oxidizing atmosphere.
Claim 30
Dependent Claim
25 words
The method of claim 25 wherein said rf frequency signal has a power density of about 0.4 to about 2.0 W/cm 2 of the wafer.
Claim 31
Dependent Claim
30 words
The method of claim 25 further including the step of depositing an electrode on the surface of said nitride film that is opposite the silicon to thereby form a capacitor.
Claim 32
Dependent Claim
12 words
The method of claim 27 wherein said nitrogen containing gas is ammonia.
Claim 33
Dependent Claim
37 words
The method of claim 25 wherein said nitride film comprises the gate dielectric for a MOSFET, and further including the step of depositing a doped polysilicon on said film to form the gate electrode of the MOSFET.
Claim 34
Dependent Claim
12 words
The method of claim 29 wherein said polysilicon is doped with boron.
Claim 35
Dependent Claim
12 words
The method of claim 29 wherein said gas is N 2 .
Claim 36
Independent Claim
92 words
A method for forming a film of silicon nitride on a surface of a silicon wafer by direct reaction with the silicon of the wafer, comprising the steps of: generating a plasma by introducing a nitrogen containing gas between a pair of spaced, substantially parallel plate electrodes and applying an rf excitation voltage between the electrodes; and disposing the silicon wafer on one of said electrodes to thereby cause ions of the plasma to react with silicon of the wafer and form the silicon nitride film on the surface of the wafer.
Claim 37
Independent Claim
92 words
A method for forming a film of silicon nitride on a surface of a silicon wafer by direct reaction with the silicon of the wafer, comprising the steps of: generating a plasma by introducing a nitrogen containing gas between a pair of spaced, substantially parallel plate electrodes and applying an rf excitation voltage between the electrodes; and disposing the silicon wafer on one of said electrodes to thereby cause ions of the plasma to react with silicon of the wafer and form the silicon nitride film on the surface of the wafer.
Claim 38
Dependent Claim
19 words
The method of claim 32 further including the step of maintaining the temperature of the wafer below 200° C.
Claim 39
Dependent Claim
19 words
The method of claim 32 further including the step of providing a d.c. bias voltage to said one electrode.
References Cited (Backward Citations)
US4113515A
Cited
US4292153A
Cited
US4300989A
Cited
US4384038A
Cited
JPS5893242A
Cited
US4461237A
Cited
US4481229A
Cited
US4522886A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-09 | 1992-02-08 | 1992-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-09 | 1996-02-08 | 1996-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-09 | 2000-02-08 | 2000-08-09 | $7700.00 | Window Closed / Lapsed |