Process for fabricating a belt
Assignee: Xerox Corp
•
Filing: 1986-03-24
•
Granted: 1988-05-31
•
Expires: 2006-03-24
Abstract
Abstract A process is disclosed for forming at least one thin substantially uniform fluid coating comprising polymeric film forming material on a cylindrical mandrel, solidifying the fluid coating to form a uniform solid coating and separating the uniform solid coating from the mandrel. The process may comprise forming at least one thin substantially uniform fluid coating comprising polymeric film forming material around a cylindrical mandrel, the mandrel having a larger mass or lower thermal conductivity than the polymeric film forming material and a critical surface tension greater than the surface tension of the fluid coating, solidifying the fluid coating to form at least one thin substantially uniform solid coating comprising the polymeric film forming material around the cylindrical mandrel, heating both the uniform solid coating and the mandrel to a temperature at least above the apparent T g of the solid coating to expand the coating and the mandrel while maintaining contact between the coating and the mandrel, cooling the coating to below the apparent T g of the solid coating prior to substantial cooling of the mandrel, and cooling the mandrel whereby the mandrel contracts at a greater rate than the polymeric coating until separation occurs between the mandrel and the coating, and removing the coating from the mandrel.
Inventors
- 👤 Donald S. Sypula
- 👤 Merlin E. Scharfe
- 👤 Dennis A. Abramsohn
- 👤 Paul J. Brach
- 👤 Clifford H. Griffiths
- 👤 Deborah J. Nichol-Landry
- 👤 Andrew R. Melnyk
- 👤 John W. Spiewak
- 👤 Joseph Mammino
- 👤 Edward C. Williams
- 👤 Lieng-Huang Lee
- 👤 Christine J. Tarnawskyj
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:29
CPC Classifications
B; B29; B29C; B29C37/00; B29C37/0003; B29C41/00; B29C41/02; B29C41/08; B29C41/085; B29C41/34; B29C41/42; B29C41/46; B29D; B29D29/00; B29K; B29K2105/00; B29K2105/0058; B29K2105/0073; B29L; B29L2009/00; B29L2031/00; B29L2031/709; B29L2031/764; Y; Y10; Y10S; Y10S264/00; Y10S264/72
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
195 words
A process for fabricating a thin, flexible, seamless belt comprising forming at least one thin substantially uniform fluid coating comprising film forming polymer material on a cylindrical mandrel having a cylindrical molding surface parallel to the axis of said cylinder, said mandrel having a larger mass, lower thermal conductivity, or larger mass and lower thermal conductivity than said film forming polymer material and a critical surface tension greater than the surface tension of said fluid coating, solidifying said fluid coating to form at least one thin substantially uniform solid coating comprising said film forming polymer material on said cylindrical mandrel, heating both said uniform solid coating and said mandrel to a temperature at least above the apparent T g of said solid coating to expand said coating and said mandrel while maintaining contact between said coating and said mandrel, cooling said coating to a temperature below the apparent T g of said solid coating prior to substantial cooling of said mandrel, and cooling said mandrel whereby said mandrel contracts at a greater rate than said solid coating until separation occurs between said mandrel and said solid coating, and removing said solid coating from said mandrel.
Claim 2
Dependent Claim
195 words
A process for fabricating a thin, flexible, seamless belt comprising forming at least one thin substantially uniform fluid coating comprising film forming polymer material on a cylindrical mandrel having a cylindrical molding surface parallel to the axis of said cylinder, said mandrel having a larger mass, lower thermal conductivity, or larger mass and lower thermal conductivity than said film forming polymer material and a critical surface tension greater than the surface tension of said fluid coating, solidifying said fluid coating to form at least one thin substantially uniform solid coating comprising said film forming polymer material on said cylindrical mandrel, heating both said uniform solid coating and said mandrel to a temperature at least above the apparent T g of said solid coating to expand said coating and said mandrel while maintaining contact between said coating and said mandrel, cooling said coating to a temperature below the apparent T g of said solid coating prior to substantial cooling of said mandrel, and cooling said mandrel whereby said mandrel contracts at a greater rate than said solid coating until separation occurs between said mandrel and said solid coating, and removing said solid coating from said mandrel.
Claim 3
Dependent Claim
82 words
A process for fabricating a thin, flexible, seamless belt according to claim 1 wherein said thin substantially uniform fluid coating comprises a film forming polymeric binder and a liquid carrier for said film forming polymer binder, and said liquid carrier is removed from said fluid coating prior to removing said coating from said mandrel, the combination of said film forming polymer material and said liquid carrier having a lower surface tension than said film forming polymer material free of said liquid carrier.
Claim 4
Dependent Claim
35 words
A process for fabricating a thin, flexible, seamless belt according to claim 1 wherein said thin substantially uniform fluid coating is applied to and solidified on said mandrel at a temperature below about 60° C.
Claim 5
Dependent Claim
26 words
A process for fabricating a thin, flexible, seamless belt according to claim 1 wherein said solid coating is cooled by rapid quenching in a cool fluid.
Claim 6
Dependent Claim
68 words
A process for fabricating a thin, flexible, seamless belt according to claim 1 comprising rotating said cylindrical mandrel around its axis and forming at least one thin substantially uniform fluid coating comprising said film forming polymer material on the outer surface of said cylindrical mandrel by spraying with a spray gun traversing in a direction parallel to said axis of said mandrel while said cylindrical mandrel is rotated.
Claim 7
Dependent Claim
22 words
A process for fabricating a thin, flexible, seamless belt according to claim 1 wherein said mandrel comprises polyethylene, polypropylene, and copolymers thereof.
Claim 8
Dependent Claim
271 words
A process for fabricating a thin, flexible, seamless belt comprising forming a first thin substantially uniform fluid coating comprising film forming polymer material on a cylindrical mandrel having a cylindrical molding surface parallel to the axis of said cylinder, said mandrel having a larger mass or lower thermal conductivity than said film forming polymer material and a critical surface tension greater than the surface tension of said fluid coating, solidifying said first fluid coating at a temperature below the apparent T g of the solidified coating to form a first thin substantially uniform solid coating comprising said film forming polymer material on said cylindrical mandrel, forming at least a second thin substantially uniform fluid coating comprising film forming polymer material on said first thin substantially uniform solid coating, solidifying said second fluid coating to form a second thin substantially uniform solid coating comprising said film forming polymer material on said first coating, heating said first uniform solid coating, said second uniform solid coating and said mandrel to a temperature above the apparent T g of the first uniform solid coating and said second uniform solid coating to expand said first uniform solid coating, said second uniform solid coating and said mandrel while maintaining contact between said mandrel and said first and second uniform solid coatings, cooling said coatings to a temperature below the apparent T g of said solid coatings prior to substantial cooling of said mandrel, and cooling said mandrel whereby said mandrel contracts at a greater rate than said solid coatings until separation occurs between said mandrel and said solid coatings, and removing said solid coatings from said mandrel.
Claim 9
Dependent Claim
271 words
A process for fabricating a thin, flexible, seamless belt comprising forming a first thin substantially uniform fluid coating comprising film forming polymer material on a cylindrical mandrel having a cylindrical molding surface parallel to the axis of said cylinder, said mandrel having a larger mass or lower thermal conductivity than said film forming polymer material and a critical surface tension greater than the surface tension of said fluid coating, solidifying said first fluid coating at a temperature below the apparent T g of the solidified coating to form a first thin substantially uniform solid coating comprising said film forming polymer material on said cylindrical mandrel, forming at least a second thin substantially uniform fluid coating comprising film forming polymer material on said first thin substantially uniform solid coating, solidifying said second fluid coating to form a second thin substantially uniform solid coating comprising said film forming polymer material on said first coating, heating said first uniform solid coating, said second uniform solid coating and said mandrel to a temperature above the apparent T g of the first uniform solid coating and said second uniform solid coating to expand said first uniform solid coating, said second uniform solid coating and said mandrel while maintaining contact between said mandrel and said first and second uniform solid coatings, cooling said coatings to a temperature below the apparent T g of said solid coatings prior to substantial cooling of said mandrel, and cooling said mandrel whereby said mandrel contracts at a greater rate than said solid coatings until separation occurs between said mandrel and said solid coatings, and removing said solid coatings from said mandrel.
Claim 10
Dependent Claim
46 words
A process for fabricating a thin, flexible, seamless belt according to claim 7 including repeating said coating forming and solidifying steps to form at least an electrically conductive coating, a charge generator coating and a charge transport coating prior to removing said coatings from said mandrel.
Claim 11
Dependent Claim
226 words
A process for fabricating a thin, flexible, seamless belt comprising forming at least one thin substantially uniform fluid coating comprising a film forming polymer and at least one solvent for said film forming binder around a cylindrical mandrel at a temperature below about 60° C., said thin substantially uniform fluid coating having a surface tension sufficiently less than the critical surface tension of said mandrel to form said uniform fluid coating on said mandrel, said mandrel having a cylindrical molding surface parallel to the axis of said cylinder, solidifying said fluid coating at a temperature below about 60° C. to form a uniform solid coating around said cylindrical mandrel, heating said mandrel and said uniform solid coating to a temperature above about 130° C. and above the apparent T g of said uniform solid coating, and cooling said uniform solid coating below about 130° C. and below the apparent T g of said uniform said coating prior to substantial cooling of said mandrel, cooling said mandrel whereby said mandrel contracts at a greater rate than said uniform solid coating, and removing said uniform solid coating as a thin, flexible, seamless belt from said mandrel, said uniform solid coating being substantially dry and having a critical surface tension greater than the critical surface tension of said mandrel when said uniform solid coating is removed from said mandrel.
Claim 12
Dependent Claim
226 words
A process for fabricating a thin, flexible, seamless belt comprising forming at least one thin substantially uniform fluid coating comprising a film forming polymer and at least one solvent for said film forming binder around a cylindrical mandrel at a temperature below about 60° C., said thin substantially uniform fluid coating having a surface tension sufficiently less than the critical surface tension of said mandrel to form said uniform fluid coating on said mandrel, said mandrel having a cylindrical molding surface parallel to the axis of said cylinder, solidifying said fluid coating at a temperature below about 60° C. to form a uniform solid coating around said cylindrical mandrel, heating said mandrel and said uniform solid coating to a temperature above about 130° C. and above the apparent T g of said uniform solid coating, and cooling said uniform solid coating below about 130° C. and below the apparent T g of said uniform said coating prior to substantial cooling of said mandrel, cooling said mandrel whereby said mandrel contracts at a greater rate than said uniform solid coating, and removing said uniform solid coating as a thin, flexible, seamless belt from said mandrel, said uniform solid coating being substantially dry and having a critical surface tension greater than the critical surface tension of said mandrel when said uniform solid coating is removed from said mandrel.
Claim 13
Dependent Claim
66 words
A process for fabricating a thin, flexible, seamless belt according to claim 9 wherein said thin substantially uniform fluid coating comprises at a mixture of solvents for said film forming binder, said mixture comprising from about 40 percent to about 80 percent by weight of a low boiling solvent and from about 20 percent to about 60 about percent by weight of a high boiling solvent.
Claim 14
Dependent Claim
64 words
A process for fabricating a thin, flexible, seamless belt according to claim 9 wherein said critical surface tension of said mandrel is at least about 5 percent greater than the surface tension of said thin substantially uniform fluid coating and said uniform solid coating has a critical surface tension of at least about 10 percent greater than said critical surface tension of said mandrel.
Claim 15
Dependent Claim
29 words
A process for fabricating a thin, flexible, seamless belt according to claim 9 wherein said thin substantially uniform fluid coating comprises a film forming polymer and a release agent.
Claim 16
Dependent Claim
34 words
A process for fabricating a thin, flexible, seamless belt according to claim 9 including reducing adhesion between said mandrel and said uniform solid coating prior to removing said uniform solid coating from said mandrel.
Claim 17
Dependent Claim
44 words
A process for fabricating a thin, flexible, seamless belt according to claim 13 comprising introducing a fluid between said coating and said mandrel thereby reducing adhesion between said mandrel and said uniform solid coating prior to removing said uniform solid coating from said mandrel.
Claim 18
Dependent Claim
29 words
A process for fabricating a thin, flexible, seamless belt according to claim 9 wherein said said mandrel comprises a core having an outer surface coated with a release coating.
Claim 19
Dependent Claim
30 words
A process for fabricating a thin, flexible, seamless belt according to claim 9 wherein said thin, flexible, seamless belt has a thickness between about 15 micrometers and about 500 micrometers.
Claim 20
Dependent Claim
35 words
A process for fabricating a thin, flexible, a seamless belt according to claim 9 wherein said cylindrical mandrel is a hollow sleeve and said cylindrical molding surface is the inside surface of said hollow sleeve.
References Cited (Backward Citations)
US1036416A
Cited
US1573386A
Cited
US1535368A
Cited
US1752371A
Cited
US2045123A
Cited
US2272704A
Cited
US2384055A
Cited
US2361026A
Cited
US2604658A
Cited
US2888712A
Cited
GB951881A
Cited
US3290728A
Cited
US3576928A
Cited
US3564661A
Cited
US3849128A
Cited
US3634572A
Cited
US3607998A
Cited
US3617588A
Cited
GB1288717A
Cited
BE771176A
Cited
US3676210A
Cited
US3905400A
Cited
US3698847A
Cited
US4252883A
Cited
US3876510A
Cited
US3844906A
Cited
CA1018932A
Cited
US3927463A
Cited
US3950839A
Cited
US3947348A
Cited
US3994726A
Cited
US3963587A
Cited
US4002476A
Cited
US4095480A
Cited
US4061599A
Cited
US4143024A
Cited
US4111861A
Cited
US4265990A
Cited
US4067782A
Cited
US4169903A
Cited
US4258113A
Cited
JPS54128740A
Cited
US4337220A
Cited
US4210710A
Cited
US4383020A
Cited
US4418132A
Cited
US4394340A
Cited
US4326928A
Cited
US4426435A
Cited
JPS57201640A
Cited
US4438065A
Cited
US4435351A
Cited
US4481273A
Cited
US4481273B1
Cited
US4548779A
Cited
US4472341A
Cited
US4501646A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-31 | 1991-11-30 | 1992-05-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-31 | 1995-11-30 | 1996-05-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-31 | 1999-11-30 | 2000-05-31 | $7700.00 | Window Closed / Lapsed |