US4731116A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Sputter target and process for producing sputter target
Assignee: Schwarzkopf Technologies Corp
•
Filing: 1986-12-18
•
Granted: 1988-03-15
•
Expires: 2006-12-18
Abstract
Abstract Sputter targets and a process for producing sputter targets are provided, comprised of carbides and/or nitrides and/or borides of refractory metals. In a first step, a dense composite body is produced comprised of one or more carbides and/or nitrides and/or borides of the metals of Groups IV A-VI A of the periodic table and a metallic binding agent comprised of one or more metals of the iron group of the periodic table. This composite body in the form of a shaped blank is machined, if necessary, and the binding agent is removed by chemical or electrochemical treatment. The sputter target as so produced has excellent mechanical strength and high thermal shock resistance. Levels of contaminating elements and the residual metallic binding agent are extremely low, meeting the requirements typically placed on sputter targets.
Inventors
- 👤 Erich Kny
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:50
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/34; C23C14/3407; C23C14/3414
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
114 words
A process for producing a sputter target the bulk of said sputter target comprised of carbides and/or nitrides and/or borides of a refractory metal, comprising: providing a dense composite body the bulk of which being comprised of (1) one or more carbides and/or nitrides and/or borides of the metals of Group IV A to VI A of the periodic table and (2) a metallic binding agent comprised of one or more metals of the iron group of the periodic table; densifying said composite body by pressing and/or sintering; preferably machining the densified composite body before and/or after sintering to form a shaped sputter target; and removing the binding agent by chemical and/or electrochemical treatment.
Claim 2
Dependent Claim
114 words
A process for producing a sputter target the bulk of said sputter target comprised of carbides and/or nitrides and/or borides of a refractory metal, comprising: providing a dense composite body the bulk of which being comprised of (1) one or more carbides and/or nitrides and/or borides of the metals of Group IV A to VI A of the periodic table and (2) a metallic binding agent comprised of one or more metals of the iron group of the periodic table; densifying said composite body by pressing and/or sintering; preferably machining the densified composite body before and/or after sintering to form a shaped sputter target; and removing the binding agent by chemical and/or electrochemical treatment.
Claim 3
Dependent Claim
64 words
A process for producing a sputter target according to claim 1, wherein the composite body is comprised of one or more of carbides selected from the group consisting of tungsten carbide, titanium carbide, tantalum carbide, niobium carbide, zirconium carbide, chromium carbide, and molybdenum carbide and wherein said binding agent is comprised of one or more metals of the iron group of the periodic table.
Claim 4
Dependent Claim
65 words
A process for producing a sputter target according to claim 1, wherein the composite body is comprised of one or more of the nitrides selected from the group consisting of tungsten nitride, titanium nitride, tantalum nitride, niobium nitride, zirconium nitride, chromium nitride, and molybdenum nitride, and wherein said binding agent is comprised of one or more metals of the iron group of the periodic table.
Claim 5
Dependent Claim
12 words
A sputter target formed in accordance with the process of claim 1.
Claim 6
Dependent Claim
96 words
A process for producing a sputter target consisting essentially of carbides and/or nitrides and/or borides of a refractory metal, comprising: providing a dense composite body consisting essentially of (1) one or more carbides and/or nitrides and/or borides of the metals of Group IV A to VI A of the periodic table of the elements and (2) a metallic binding agent consisting essentially of one or more metals of the iron group of the periodic table of the elements; densifying said composite body by pressing and/or sintering; and removing the binding agent by chemical and/or electrochemical treatment.
Claim 7
Dependent Claim
96 words
A process for producing a sputter target consisting essentially of carbides and/or nitrides and/or borides of a refractory metal, comprising: providing a dense composite body consisting essentially of (1) one or more carbides and/or nitrides and/or borides of the metals of Group IV A to VI A of the periodic table of the elements and (2) a metallic binding agent consisting essentially of one or more metals of the iron group of the periodic table of the elements; densifying said composite body by pressing and/or sintering; and removing the binding agent by chemical and/or electrochemical treatment.
Claim 8
Dependent Claim
34 words
A process for producing a sputter target according to claim 5 wherein the densified composite body is machined before and/or after sintering to form a shaped sputter target prior to removing the binding agent.
Claim 9
Dependent Claim
66 words
A process for producing a sputter target according to claim 5, wherein the composite body consists essentially of one or more of carbides selected from the group consisting of tungsten carbide, titanium carbide, tantalum carbide, niobium carbide, zirconium carbide, chromium carbide, and molybdenum carbide and wherein said binding agent consists essentially of one or more of the iron group of the periodic table of the elements.
Claim 10
Dependent Claim
68 words
A process for producing a sputter target according to claim 5, wherein the composite body consists essentially of one or more of the nitrides selected from the group consisting of tungsten nitride, titanium nitride, tantalum nitride, niobium nitride, zirconium nitride, chromium nitride, and molybdenum nitride, and wherein said binding agent consists essentially of one or more metals of the iron group of the periodic table of the elements.
Claim 11
Dependent Claim
12 words
A sputter target formed in accordance with the process of claim 5.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-03-15 | 1991-09-14 | 1992-03-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-03-15 | 1995-09-14 | 1996-03-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-03-15 | 1999-09-14 | 2000-03-15 | $7700.00 | Window Closed / Lapsed |