Sputtering targets with low mobile ion contamination
Assignee: St Clair Intellectual Property Consultants Inc
•
Filing: 1980-01-31
•
Granted: 1982-05-25
•
Expires: 2000-01-31
Abstract
Abstract Metallic sputtering targets having minimal mobile ion contamination are produced by forming a compacted slab of particles of the constituent metal(s) in an isostatic pressing operation. The slab is then transferred to a heat resistant support faced with a material, such as alumina, that is inert at high temperatures. Next, the supported slab is placed in a vacuum oven and heated to a temperature sufficient to bond the metal particles together and volatilize mobile ion contaminants. The sintered slab is usable as a cathodic sputtering target with minimal additional treatment. The level of mobile ion contaminants in the completed target may be monitored by fabricating an MOS capacitor using the target, plotting its capacitance versus applied voltage over a suitable range, then measuring the extent to which the plot shifts after a high temperature-positive bias stress treatment.
Inventors
- 👤 Earl R. Helderman
- 👤 Robert R. Zimmerman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 23:04
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/34; C23C14/3407; C23C14/3414; B; B22; B22F; B22F3/00; B22F3/10; C22; C22C; C22C1/00; C22C1/04; C22C1/045; B22F2201/00; B22F2201/20
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
149 words
A method of manufacturing a sintered metal alloy sputtering target consisting essentially of titanium and tungsten and having a reduced level of sodium and other alkali metal contamination, comprising the subsequential steps of: (a) providing a die having a cavity of a desired configuration, said cavity having a relatively flexible movable wall section, (b) charging said cavity with a suitable quantity of a titanium and tungsten particle mixture containing an undesirably high level of alkali metal contamination, including sodium, (c) compacting said mixture into a coherent mass by the application of substantially uniform surface pressure to said movable wall section, (d) transferring the compacted particle mass to a temperature-resistant support, and (e) heating the supported particle mass in a low pressure environment to a temperature and for a time sufficient to fuse the particles together and volatilize a substantial portion of the alkali metal contaminants present in said mass.
Claim 2
Independent Claim
149 words
A method of manufacturing a sintered metal alloy sputtering target consisting essentially of titanium and tungsten and having a reduced level of sodium and other alkali metal contamination, comprising the subsequential steps of: (a) providing a die having a cavity of a desired configuration, said cavity having a relatively flexible movable wall section, (b) charging said cavity with a suitable quantity of a titanium and tungsten particle mixture containing an undesirably high level of alkali metal contamination, including sodium, (c) compacting said mixture into a coherent mass by the application of substantially uniform surface pressure to said movable wall section, (d) transferring the compacted particle mass to a temperature-resistant support, and (e) heating the supported particle mass in a low pressure environment to a temperature and for a time sufficient to fuse the particles together and volatilize a substantial portion of the alkali metal contaminants present in said mass.
Claim 3
Dependent Claim
29 words
The method of claim 1, wherein said mixture is compacted during step (c) by a pressure on said movable wall section of at least 13,000 pounds per square inch.
Claim 4
Dependent Claim
30 words
The method of claim 1, wherein said particle mass is heated during step (e) to a temperature of at least 1250° C. for a period of at least four hours.
Claim 5
Dependent Claim
27 words
The method of claim 1, wherein the titanium and tungsten particles forming the mixture are present in a weight ratio of about 10% titanium and 90% tungsten.
Claim 6
Dependent Claim
10 words
A sputtering target manufactured by the method of claim 1.
Claim 7
Independent Claim
141 words
A method of manufacturing a sintered titanium-tungsten alloy sputtering target having a reduced level of sodium contamination, comprising the subsequential steps of: (a) providing a die having a cavity of a desired configuration, said cavity having a relatively flexible movable wall section, (b) charging said cavity with a mixture of finely-divided titanium and tungsten particles, said mixture containing as an impurity an undesirably high concentration of sodium, (c) compacting said particle mixture into a coherent mass by the application of substantially uniform surface pressure to said movable wall section, (d) transferring the compacted particle mass to a temperature-resistant support, and (e) heating the supported particle mass in a low pressure environment to a temperature of at least 1250° C. for a period of at least four hours to fuse the particles together and volatilize at least a portion of said sodium.
Claim 8
Independent Claim
141 words
A method of manufacturing a sintered titanium-tungsten alloy sputtering target having a reduced level of sodium contamination, comprising the subsequential steps of: (a) providing a die having a cavity of a desired configuration, said cavity having a relatively flexible movable wall section, (b) charging said cavity with a mixture of finely-divided titanium and tungsten particles, said mixture containing as an impurity an undesirably high concentration of sodium, (c) compacting said particle mixture into a coherent mass by the application of substantially uniform surface pressure to said movable wall section, (d) transferring the compacted particle mass to a temperature-resistant support, and (e) heating the supported particle mass in a low pressure environment to a temperature of at least 1250° C. for a period of at least four hours to fuse the particles together and volatilize at least a portion of said sodium.
Claim 9
Dependent Claim
60 words
The method of claim 6, wherein said particle mass during step (e) is heated at an atmospheric pressure not greater than 10 -6 torr to a temperature of at least 1250° C. for a period of at least four hours, then to a temperature of at least 1350° C. for a period of approximately one-half hour while maintaining said pressure.
References Cited (Backward Citations)
US1719128A
Cited
US1731244A
Cited
GB450552A
Cited
US3116146A
Cited
US3300285A
Cited
US3700434A
Cited
US3963485A
Cited
US3793014A
Cited
US4135286A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-05-24 | 1985-11-23 | 1986-05-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-05-24 | 1989-11-23 | 1990-05-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-05-24 | 1993-11-23 | 1994-05-25 | $7700.00 | Window Closed / Lapsed |