Process and apparatus for producing optical-fiber preforms for mid-infrared range fibers
Assignee: Telecom Italia SpA
•
Filing: 1987-03-25
•
Granted: 1988-03-01
•
Expires: 2007-03-25
Abstract
Abstract The process employs solid-state halides heated at high temperature, under pressure conditions necessary to their vaporization, and obtains their condensation to a solid state on the internal surface of a glass tube, which, after collapsing, forms the preform.
Inventors
- 👤 Giuseppe Cocito
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 18:24
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/018; C03B37/01807; C03C; C03C13/00; C03C13/04; C03B2201/00; C03B2201/80; C03B2201/82; Y; Y10; Y10S; Y10S65/00; Y10S65/15; Y10S65/16
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
111 words
A method of making an optical preform capable of being drawn into an optical fiber for operation in a mid-infrared spectral range, said method comprising the steps of: heating one or more halides to an elevated temperature at a controlled pressure to transform the halides to vapor and conducting vapors of the halides without condensation into the interior of a cooled tube; directing said vapors against an inner wall of said tube whereby said vapors directly condense on said wall to a solid state deposit; and removing nonhalide-based portions of said tube to yield said preform with at least said deposit being adapted to be drawn to form said optical fiber.
Claim 2
Independent Claim
111 words
A method of making an optical preform capable of being drawn into an optical fiber for operation in a mid-infrared spectral range, said method comprising the steps of: heating one or more halides to an elevated temperature at a controlled pressure to transform the halides to vapor and conducting vapors of the halides without condensation into the interior of a cooled tube; directing said vapors against an inner wall of said tube whereby said vapors directly condense on said wall to a solid state deposit; and removing nonhalide-based portions of said tube to yield said preform with at least said deposit being adapted to be drawn to form said optical fiber.
Claim 3
Dependent Claim
33 words
The method defined in claim 1 wherein said vapors are conducted into said tube through a conduit heated at least to the temperature of the highest temperature to which said halides are heated.
Claim 4
Dependent Claim
53 words
The method defined in claim 2 wherein said tube is composed of an oxide-based glass, further comprising the step of coating said wall with at least one stable halide selected from the group which consists of CeF 3 , EuF 2 , HoF 3 , and MgF 2 before said deposit is formed.
Claim 5
Dependent Claim
22 words
The method defined in claim 3 wherein said oxide-based glass is removed before said preform is drawn to form the optical fiber.
Claim 6
Dependent Claim
22 words
The method defined in claim 1, further comprising the step of rotating said tube while said vapors are trained against said wall.
Claim 7
Dependent Claim
23 words
The method defined in claim 1, further comprising the step of axially reciprocating said tube while said vapors are trained against said wall.
Claim 8
Dependent Claim
15 words
The method defined in claim 1 wherein said tube is composed of a halide-based glass.
Claim 9
Dependent Claim
15 words
The method defined in claim 1 wherein said halides are CsF and BeF 2 .
Claim 10
Independent Claim
132 words
An apparatus for making an optical preform capable of being drawn into an optical fiber for operation in a mid-infrared spectral range, said apparatus comprising: means for heating one or more halides to an elevated temperature at a controlled pressure to transform the halides to vapor; a conduit connected to said means for heating for conducting vapors of the halides without condensation into the interior of a cooled tube; and a nozzle at an end of said conduit in said tube for directing said vapors against an inner wall of said tube whereby said vapors directly condense on said wall to a solid state deposit whereby by removing nonhalide-based portions of said tube said preform is obtained with at least said deposit being adapted to be drawn to form said optical fiber.
Claim 11
Independent Claim
132 words
An apparatus for making an optical preform capable of being drawn into an optical fiber for operation in a mid-infrared spectral range, said apparatus comprising: means for heating one or more halides to an elevated temperature at a controlled pressure to transform the halides to vapor; a conduit connected to said means for heating for conducting vapors of the halides without condensation into the interior of a cooled tube; and a nozzle at an end of said conduit in said tube for directing said vapors against an inner wall of said tube whereby said vapors directly condense on said wall to a solid state deposit whereby by removing nonhalide-based portions of said tube said preform is obtained with at least said deposit being adapted to be drawn to form said optical fiber.
Claim 12
Dependent Claim
29 words
The apparatus defined in claim 9 wherein said means for heating comprises one or more vessels respectively containing said halides, heated to high temperature and connected to said conduit.
Claim 13
Dependent Claim
26 words
The apparatus defined in claim 10, further comprising means for heating said conduit to a temperature at least equal to the higher temperature of said vessels.
Claim 14
Dependent Claim
52 words
The apparatus defined in claim 11, further comprising: means for cooling said tube wall; means for rotating said tube relative to said nozzle; means for axially displacing said tube relative to said nozzle in translation parallel to an axis of said tube; and a pump connected to said tube for evacuating same.
Claim 15
Dependent Claim
47 words
The apparatus defined in claim 12 wherein said tube has a coating on said wall of at least one stable halide selected from the group which consists of CeF 3 , EuF 2 , HoF 3 , and MgF 2 and is composed of an oxide-based glass.
Claim 16
Dependent Claim
15 words
The apparatus defined in claim 12 wherein said tube is composed of a halide-based glass.
Claim 17
Dependent Claim
33 words
The apparatus defined in claim 12 wherein said means for heating said conduit is a double-wall structure of said conduit and means for circulating a heating fluid through a space between walls thereof.
Claim 18
Dependent Claim
22 words
The apparatus defined in claim 12 wherein said means for heating said conduit is an electrical resistance heater extending along said conduit.
Claim 19
Dependent Claim
33 words
The apparatus defined in claim 12 wherein said conduit is composed of a material of high thermal conductivity and is heated by said means for heating only at one end of said conduit.
Claim 20
Dependent Claim
21 words
The apparatus defined in claim 12 wherein said nozzle is constructed and arranged to direct said vapors onto said wall uniformly.
Claim 21
Dependent Claim
26 words
The apparatus defined in claim 12 wherein said nozzle is constructed and arranged to direct said vapors against said wall selectively in a plurality of directions.
Claim 22
Dependent Claim
16 words
The apparatus defined in claim 12 wherein said vessels respectively contain CsF and BF 2 .
References Cited (Backward Citations)
US3971645A
Cited
US4253863A
Cited
US4278459A
Cited
US4597787A
Cited
US4666247A
Cited
US4610708A
Cited
WO1987001110A1
Cited
US4666486A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-03-01 | 1991-08-31 | 1992-03-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-03-01 | 1995-08-31 | 1996-03-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-03-01 | 1999-08-31 | 2000-03-01 | $7700.00 | Window Closed / Lapsed |