Manufacture of optical fibre preforms
Assignee: Ispra Fibroptics Industries Herzlia Ltd
•
Filing: 1984-11-13
•
Granted: 1986-07-01
•
Expires: 2004-11-13
Abstract
Abstract Manufacture of optical fibre preforms. A material such as Si, Ge and B 2 O 3 is evaporated in vacuo into a silica tube and is made to condense therein as a viscous liquid which is then oxidized. The operation may be repeated several times with different materials. In this way the tube is clad from within in such a way that the optical index of refraction increases from the periphery inwards. Upon completion of the cladding the tube is collapsed into a rod which is then used for drawing optical fibres.
Inventors
- 👤 Amnon Jacobson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 17:05
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/018
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
226 words
In a method of producing a glass preform useful for drawing optical fibres, which comprises forming a system comprising a glass tube having a first end operatively connected to a chamber, charging the chamber with solid silicon, effecting a reduced pressure in the system of 10 -8 to 10 3 microns Hg, heating the silicon to a temperature up to 1500° C. so as to evaporate the same while maintaining the reduced pressure in the system, whereby the glass tube is not deformed during the evaporation, externally cooling said tube from the end opposite the first end towards the first end to a temperature at which said silicon condenses as a liquid, thereby causing deposition of the silicon as a liquid layer on the inner surface of the tube from the other end to the first end, passing oxygen through said tube from the first end to the other end, thereby oxidizing the deposited silicon to silica and forming a uniform silica coating on the inner surface of the glass tube, and forming a coating of a metal oxide on said silica coating by evaporation of a metal and oxidation thereof in the same manner as with the silica, or by evaporation of a metal oxide and deposition thereof by cooling on the silica, whereby the metal oxide diffuses into the silica to dope the same.
Claim 2
Dependent Claim
226 words
In a method of producing a glass preform useful for drawing optical fibres, which comprises forming a system comprising a glass tube having a first end operatively connected to a chamber, charging the chamber with solid silicon, effecting a reduced pressure in the system of 10 -8 to 10 3 microns Hg, heating the silicon to a temperature up to 1500° C. so as to evaporate the same while maintaining the reduced pressure in the system, whereby the glass tube is not deformed during the evaporation, externally cooling said tube from the end opposite the first end towards the first end to a temperature at which said silicon condenses as a liquid, thereby causing deposition of the silicon as a liquid layer on the inner surface of the tube from the other end to the first end, passing oxygen through said tube from the first end to the other end, thereby oxidizing the deposited silicon to silica and forming a uniform silica coating on the inner surface of the glass tube, and forming a coating of a metal oxide on said silica coating by evaporation of a metal and oxidation thereof in the same manner as with the silica, or by evaporation of a metal oxide and deposition thereof by cooling on the silica, whereby the metal oxide diffuses into the silica to dope the same.
Claim 3
Dependent Claim
48 words
Method according to claim 1 wherein the silicon and the metal or metal oxide are deposited in successive pairs of cycles of operation with the relative proportions of silica and the metal in each pair of cycles being gradually changed from one pair of cycles to the other.
Claim 4
Dependent Claim
16 words
Method according to claim 1 wherein evaporation is enhanced by supplying non-thermal energy to the system.
Claim 5
Dependent Claim
56 words
Method according to claim 1 wherein the metal or metal oxide to be evaporated is introduced into the chamber in the form of a filament that is spun inside the tube in axial direction between vacuum tight terminals; and electric current is passed through the filament to supply additional energy thereto and thus to enhance evaporation.
Claim 6
Dependent Claim
16 words
Method according to claim 1 wherein the chamber is charged sequentially with the materials for evaporation.
Claim 7
Dependent Claim
35 words
Method according to claim 1 wherein the glass tube is operatively connected to several chambers containing different materials for evaporation and wherein conditions are effected to evaporate and deposit only one material at a time.
Claim 8
Dependent Claim
10 words
Method according to claim 1 wherein the metal is germanium.
Claim 9
Dependent Claim
15 words
Method according to claim 1 wherein the metal oxide is B 2 O 3 .
Claim 10
Dependent Claim
29 words
Method according to claim 1 wherein at least a portion of the deposited silica layer is doped by passing fluorine through the system after the deposition of silicon therein.
References Cited (Backward Citations)
DE2447353A1
Cited
US3971645A
Cited
US4039607A
Cited
DE2637937A1
Cited
GB1598760A
Cited
FR2490211A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-30 | 1989-12-30 | 1990-07-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-30 | 1993-12-30 | 1994-07-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-30 | 1997-12-30 | 1998-07-01 | $7700.00 | Window Closed / Lapsed |